Fire-retardant 1-butene resin composition
Assignee: Mitsui Chemicals Inc
•
Filing: 1984-05-16
•
Granted: —
•
Expires: 2004-05-16
Abstract
Abstract A fire-retardant 1-butene resin composition composed of (A) 100 parts by weight of a 1-butene polymer or copolymer containing 0 to 20 mole % of an olefin with 2 to 20 carbon atoms other than 1-butene as a comonomer, (B) 110 to 1,000 parts by weight of an inorganic hydroxide selected from the group consisting of magnesium hydroxide and aluminum hydroxide, and (C) 10 to 150 parts by weight of a graft-modified olefin resin resulting from grafting of an unsaturated carboxylic acid or its functional derivative to a polymer or a copolymer of an olefin having 3 to 8 carbon atoms or a copolymer of said olefin with up to 30 mole % of ethylene.
Inventors
- 👤 Motoyasu Yusawa
- 👤 Chikara Igarashi
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-08 10:04
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/18; C08L23/20; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08L51/00; C08L51/06
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
91 words
A fire-retardant 1-butene resin composition composed of (A) 100 parts by weight of a 1-butene polymer or copolymer containing 0 to 20 mole% of an olefin with 2 to 20 carbon atoms other than 1-butene as a comonomer, (B) 110 to 1,000 parts by weight of magnesium hydroxide or aluminum hydroxide, and (C) 10 to 150 parts by weight of a graft-modified olefin resin resulting from grafting of an unsaturated carboxylic acid or a functional derivative thereof onto a polymer or copolymer of an olefin having 2 to 8 carbon atoms.
Claim 2
Dependent Claim
91 words
A fire-retardant 1-butene resin composition composed of (A) 100 parts by weight of a 1-butene polymer or copolymer containing 0 to 20 mole% of an olefin with 2 to 20 carbon atoms other than 1-butene as a comonomer, (B) 110 to 1,000 parts by weight of magnesium hydroxide or aluminum hydroxide, and (C) 10 to 150 parts by weight of a graft-modified olefin resin resulting from grafting of an unsaturated carboxylic acid or a functional derivative thereof onto a polymer or copolymer of an olefin having 2 to 8 carbon atoms.
Claim 3
Dependent Claim
30 words
A composition according to claim 1 wherein the 1-butene polymer or copolymer (A) has a melt flow rate, determined by ASTM D 1238N, of from 0.1 to 50 g/10 min.
Claim 4
Dependent Claim
25 words
A composition according to claim 1 or 2 wherein the 1-butene polymer or copolymer (A) has a degree of crystallinity of from 20 to 65%.
Claim 5
Dependent Claim
26 words
A composition according to claim 1, 2 or 3 wherein the inorganic hydroxide (B) has an average particle size of from 50 nm to 5 pm.
Claim 6
Dependent Claim
47 words
A composition according to any one of the preceding claims wherein the graft-modified olefin resin (C) results from grafting of 0.01 to 10 parts by weight of the unsaturated carboxylic acid or a functional derivative thereof onto 100 parts by weight of the olefin polymer or copolymer.
Claim 7
Dependent Claim
37 words
A composition according to any one of the preceding claims wherein the amount of the graft-modified olefin resin (C) is 3 to 25% by weight based on the total weight of the components (A), (B) and (C).
Claim 8
Dependent Claim
30 words
A composition according to any one of the preceding claims wherein the unsaturated carboxylic acid in the component (C) is an unsaturated carboxylic acid having 3 to 10 carbon atoms.
Claim 9
Dependent Claim
41 words
A composition according to any one of the preceding claims which further comprises up to 1,000 parts by weight of an olefin resin other than the 1-butene polymer or copolymer per 100 parts by weight of the 1-butene polymer or copolymer.
Claim 10
Dependent Claim
31 words
A composition according to any one of the preceding claims which further comprises at least one additive selected from weatherability stabilizers, heat stabilizers, slip agents, nucleating agents, coloring agents and lubricants.
Claim 11
Dependent Claim
15 words
A melt-shaped article of a composition as claimed in any one of the preceding claims.
Claim 12
Dependent Claim
96 words
A process for preparing a fire-retardant 1-butene resin composition which comprises blending (A) 100 parts by weight of a 1-butene polymer or copolymer containing 0 to 20 mole% of an olefin with 2 to 20 carbon atoms other than 1-butene as a comonomer, (B) 110 to 1,000 parts by weight of magnesium hydroxide or aluminum hydroxide, and (C) 10 to 150 parts by weight of a graft-modified olefin resin resulting from grafting of an unsaturated carboxylic acid or a functional derivative thereof onto a polymer or copolymer of an olefin having 2 to 8 carbon atoms.
Claim 13
Dependent Claim
96 words
A process for preparing a fire-retardant 1-butene resin composition which comprises blending (A) 100 parts by weight of a 1-butene polymer or copolymer containing 0 to 20 mole% of an olefin with 2 to 20 carbon atoms other than 1-butene as a comonomer, (B) 110 to 1,000 parts by weight of magnesium hydroxide or aluminum hydroxide, and (C) 10 to 150 parts by weight of a graft-modified olefin resin resulting from grafting of an unsaturated carboxylic acid or a functional derivative thereof onto a polymer or copolymer of an olefin having 2 to 8 carbon atoms.