Low temperature active aliphatic/aromatic polycarbodiimides
Assignee: Union Carbide Chemicals and Plastics Technology LLC
•
Filing: 1991-03-22
•
Granted: —
•
Expires: 2011-03-22
Abstract
Abstract A mixed aliphatic/aromatic polycarbodiimide prepared by first polymerizing an aliphatic isocyanate or mixture thereof, optionally in the presence of a polyfunctional isocyanate; arresting polymer chain growth by reaction with a stoichiometrically deficient amount of a monofunctional isocyanate-reactive compound, followed by further polymerization with an aromatic diisocyanate.
Inventors
- 👤 Charles B. Mallon
- 👤 Howard Chu
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-02 02:25
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/2805; C08G18/2815; C08G18/283; C08G18/02; C08G18/025; C08G18/83; C08G18/833; C08G2115/00; C08G2115/06
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
102 words
A method for preparing a mixed aliphatic/aromatic polycarbodiimide comprising: (a) polymerizing a saturated aliphatic diisocyanate or a saturated cycloaliphatic diisocyanate or a mixture thereof, optionally containing a polyfunctional isocyanate, in the presence of a polycarbodiimide polymerization catalyst to form a polycarbodiimide intermediate having free isocyanate groups; (b) reacting said polycarbodiimide intermediate with a monofunctional isocyanate-reactive compound or a mixture thereof in an amount insufficient to react with all of said free isocyanate groups, and (c) further polymerizing said polycarbodiimide intermediate in the presence of an aromatic diisocyanate and said catalyst under polycarbodiimide-forming conditions until essentially all of the isocyanate groups are depleted.
Claim 2
Dependent Claim
38 words
The method of claim 1 wherein said saturated aliphatic diisocyanate is selected from the group consisting of isophorone diisocyanate, 1,6-hexane diisocyanate, dicyclohexylmethane diisocyanate, trimethylene diisocyanate 1,4-tetramethylene diisocyanate, decamethylene diisocyanate, 1,12-dodecane diisocyanate, cyclohexane diisocyanates, cyclobutane-1,3-diisocyanate, and hexahydrotolylene-2,4 and 2,6-diisocyanates.
Claim 3
Dependent Claim
24 words
The method of claim 2 wherein the aromatic diisocyanate is selected from the group consisting of 4,4'-diisocyanotodiphenylmethane, toluene diisocyanates; naphthalene diisocyanates, and m-phenylene diisocyanate.
Claim 4
Dependent Claim
37 words
The method of claim 1 wherein the monofunctional isocyanate-reactive compound is selected from the group consisting of alkanols having 1 to 10 carbon atoms, benzyl alcohol; glycol ethers; glycol esters; aliphatic amines; dialiphatic amines, and mixtures thereof.
Claim 5
Dependent Claim
28 words
The method of claim 4 wherein said alkanol is selected from methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, isoamyl alcohol, n-hexanol, cyclohexanol, 2-chloro-1-propanol, and 2-octanol.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein said monofunctional isocyanate-reactive compound is a methoxy polyethylene glycol or diethylene glycol mono-n-butyl ether.
Claim 7
Dependent Claim
29 words
The method of claim 1 wherein said catalyst is a phosphorous compound selected from the group consisting of phospholines, phospholine oxides and sulfies, phospholidines and phospholidine oxides and sulfides.
Claim 8
Dependent Claim
29 words
The method of claim 7 wherein said catalyst is used in an amount between about 0.001 and 0.03 mol per mol of aliphatic diisocyanate, cycloaliphatic diisocyanate or mixture thereof.
Claim 9
Dependent Claim
19 words
The method of claim 1 wherein said polymerization step (a) is continued for between about 1 and 3 hours.
Claim 10
Dependent Claim
29 words
The method of claim 1 wherein between about 0.2 to 0.5 mol of said aromatic diisocyanate is used per mol of said aliphatic diisocyanate, cycloaliphatic diisocyanate or mixture thereof.
Claim 11
Dependent Claim
30 words
The method of claim 10 wherein between about 0.2 and 0.9 mol of monofunctional isocyanate-reactive compound is used per mol of isocyanate groups in said diisocyanates and optional polyfunctional isocyanate.
Claim 12
Dependent Claim
24 words
The method of claim 11 wherein said reaction between the polycarbodiimide intermediate and said monofunctional isocyanate-reactive compound is conducted at a temperature below 120°C.
Claim 13
Dependent Claim
14 words
The method of claim 4 wherein said glycol ether is an alkoxy-capped polyethylene glycol.
Claim 14
Dependent Claim
83 words
The method of claim 1 wherein said saturated aliphatic diisocyanate is isophorone diisocyanate and said aromatic diisocyanate is a toluene diisocyanate, in an amount of between about 0.2 to 0.5 mol of toluene diisocyanate per mol of isophorone diisocyanate, wherein said monofunctional isocyanate-reactive compound includes an alkanol having 1 to 10 carbon atoms and a methoxy polyethylene glycol in an amount of between 0.2 and 0.9 mol of monofunctional isocyanate-reactive compound per mol of isocyanate groups in said isophorone diisocyanate and toluene diisocyanate.
Claim 15
Dependent Claim
100 words
A storage stable mixed aliphatic/aromatic polycarbodiimide prepared by (a) polymerizing a saturated aliphatic diisocyanate, or a saturated cycloaliphatic diisocyanate or a mixture thereof, optionally containing a polyfunctional isocyanate, in the presence of a polycarbodiimide polymerization catalyst to form a polycarbodiimide intermediate having free isocyanate groups, (b) reacting said polycarbodiimide intermediate with a monofunctional isocyanate-reactive compound or mixture thereof in an amount insufficient to react with all of said free isocyanate groups, and (c) further reacting said polycarbodiimide intermediate in the presence of an aromatic diisocyanate and said catalyst under carbodiimide-forming conditions until essentially all of the isocyanate groups are depleted.
Claim 16
Dependent Claim
34 words
The polycarbodiimide of claim 15 wherein said saturated aliphatic diisocyanate comprises isophorone diisocyanate, said monofunctional isocyanate-reactive compound comprises a mixture of n-butyl alcohol and methoxy polyethylene glycol and said aromatic diisocyanate comprises toluene diisocyanate.
Claim 17
Dependent Claim
56 words
The polycarbodiimide of claim 16 wherein said toluene diisocyanate, is provided in an amount of between about 0.2 to 0.5 mol per mol of isophorone diisocyanate and, wherein said monofunctional isocyanate-reactive compound is provided in an amount of between about 0.2 and 0.9 mol per mol of isocyanate groups in said isophorone diisocyanate and toluene diisocyanate.
Claim 18
Dependent Claim
17 words
A cross-linkable composition comprising a mixture of an aqueous carboxyl-containing resin and a polycarbodiimide of claim 15.
Claim 19
Dependent Claim
17 words
A cross-linkable composition comprising a mixture of an aqueous carboxyl-containing resin and a polycarbodiimide of claim 16.
Claim 20
Dependent Claim
17 words
A cross-linkable composition comprising a mixture of an aqueous carboxyl-containing resin and a polycarbodiimide of claim 17.