Synthetic resin composition
Assignee: Toyo Cloth Co Ltd
•
Filing: 1974-05-01
•
Granted: 1976-02-03
•
Expires: 1994-05-01
Abstract
Abstract A synthetic resin composition which comprises 20 to 50 parts by weight of olefinic resins, 10 to 40 parts by weight of vinyl chloride resins, and 70 to 10 parts by weight of alumina trihydrate having a gibbsite crystal structure whose average particle size is 30 microns at most.
Inventors
- 👤 Fumio Sakaguchi
- 👤 Kenji Takemura
- 👤 Tadao Suzuki
- 👤 Isamu Yamazaki
- 👤 Yoshifumi Nishibayashi
- 👤 Kazunobu Shiozawa
- 👤 Toshimitsu Sasaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:50
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/10; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08L2207/00; C08L2207/06; C08L2207/062
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
255 words
A synthetic resin composition capable of forming moldings with good surface hardness and flame resistance consisting essentially of 20 to 50 parts by weight of olefinic resin, 10 to 40 parts by weight of vinyl chloride resin and 70 to 10 parts by weight of alumina trihydrate of the formula α-Al(OH) 3 with a gibbsite crystal structure in which the lattice constant is measured as a = 8.62A, b = 5.06A and c = 9.70A, the β (B) angle is determined to be 85°26' and the refractive index is expressed as α = 1.568, β = 1.568 and γ = 1.567 and which has an average particle size under 30 microns, said olefinic resin being selected from the group consisting of ethylene homopolymer, copolymers formed of at least 80 mol% ethylene and not over 20 mol% of other α-olefin, propylene homopolymers and copolymers formed of at least 80 mol% propylene and not over 20 mol% of other α-olefin or diolefin, and said vinyl choride resin being selected from the group consisting of vinyl chloride polymer and mixtures thereof with up to 120 parts by weight of plasticizer, up to 10 parts by weight of lubricant and up to 10 parts by weight of stabilizer per 100 parts of vinyl chloride polymer, said vinyl chloride polymer having a degree of polymerization between about 850 to 1,800 and being selected from the group consisting of vinyl chloride homopolymer and copolymers formed of at least 85 mol% vinyl chloride with ethylene, vinylidene chloride, vinyl acetate or acrylic ester.
Claim 2
Dependent Claim
255 words
A synthetic resin composition capable of forming moldings with good surface hardness and flame resistance consisting essentially of 20 to 50 parts by weight of olefinic resin, 10 to 40 parts by weight of vinyl chloride resin and 70 to 10 parts by weight of alumina trihydrate of the formula α-Al(OH) 3 with a gibbsite crystal structure in which the lattice constant is measured as a = 8.62A, b = 5.06A and c = 9.70A, the β (B) angle is determined to be 85°26' and the refractive index is expressed as α = 1.568, β = 1.568 and γ = 1.567 and which has an average particle size under 30 microns, said olefinic resin being selected from the group consisting of ethylene homopolymer, copolymers formed of at least 80 mol% ethylene and not over 20 mol% of other α-olefin, propylene homopolymers and copolymers formed of at least 80 mol% propylene and not over 20 mol% of other α-olefin or diolefin, and said vinyl choride resin being selected from the group consisting of vinyl chloride polymer and mixtures thereof with up to 120 parts by weight of plasticizer, up to 10 parts by weight of lubricant and up to 10 parts by weight of stabilizer per 100 parts of vinyl chloride polymer, said vinyl chloride polymer having a degree of polymerization between about 850 to 1,800 and being selected from the group consisting of vinyl chloride homopolymer and copolymers formed of at least 85 mol% vinyl chloride with ethylene, vinylidene chloride, vinyl acetate or acrylic ester.
Claim 3
Dependent Claim
28 words
A synthetic resin composition according to claim 1 wherein said alumina trihydrate contains at least 0.20 percent by weight of fixed sodium compounds expressed as Na 2 O.
Claim 4
Dependent Claim
32 words
The composition of claim 1 wherein said olefinic resin is high density polyethylene having a melt index of 0.001 to 5 g/10 min. measured at 190°C under a load of 2.16 kg.
Claim 5
Dependent Claim
29 words
The composition of claim 1 wherein said olefinic resin is polypropylene having a melt index of about 20 g/10 min. measured at 230°C under a load of 2.16 kg.
Claim 6
Dependent Claim
27 words
The composition of claim 1 which contains 0.1 to 4.0 parts by weight of unsaturated carboxylic acid based on 100 parts by weight of said resin composition.
Claim 7
Dependent Claim
26 words
The composition of claim 1 which contains 0.01 to 0.2 parts by weight of organic peroxide based on 100 parts by weight of said resin composition.
Claim 8
Dependent Claim
42 words
A synthetic resin composition according to claim 5 wherein the unsaturated carboxylic acid is one selected from the group consisting of acrylic acid, methacrylic acid, monomethyl 2-methylene glutarate, crotonic acid, maleic acid, fumaric acid, itaconic acid, 2-methylene glutaric acid and citraconic acid.
Claim 9
Dependent Claim
29 words
A synthetic resin composition according to claim 6 wherein the organic peroxide is one selected from the group consisting of ketone peroxide, hydroperoxide, dialkyl peroxide, diacyl peroxide and peroxyester.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-02 | 1979-08-04 | 1980-02-03 | $2000.00 | Window Closed / Lapsed |