Silicone compositions containing platinum-containing material and manganese carbonate
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1975-01-08
•
Granted: 1976-02-03
•
Expires: 1995-01-08
Abstract
Abstract Silicone compositions consisting essentially of 100 parts by weight organopolysiloxane, 20-200 parts by weight finely divided silica filler, 5-100 parts by weight finely divided manganese carbonate, and 5-1,000 ppm platinum alone or in a platinum containing material, based on the weight of the organopolysiloxane. Finished products prepared by molding the compositions exhibit particularly excellent flame-proofing and improved degrees of permanent strain caused by stress. Particularly preferred are silicone compositions with 5-100 parts by weight of finely divided manganese carbonate having a particle size from about 1 mu to about 50 mu .
Inventors
- 👤 Kunio Itoh
- 👤 Takeo Yoshida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:36
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/18; C08K3/24; C08K3/26
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
128 words
Silicone compositions which comprise a. 100 parts by weight of an organopolysiloxane having the formula: R.sub.a SiO.sub.4-a/2 wherein R is a member selected from the group consisting of substituted and unsubstituted monovalent hydrocarbon radicals; and a is a number from about 1.90 to about 2.05; b. from about 20 to about 200 parts by weight of finely divided silica filler, c. from about 5 to about 100 parts by weight of manganese carbonate having a particle size of from about 1μ to about 50μ and d. from about 5 to about 1,000 parts per million parts by weight of a platinum-containing composition, at least a part of which is platinum, the parts of platinum in said composition being based on the weight of the said organopolysiloxane component (a).
Claim 2
Dependent Claim
128 words
Silicone compositions which comprise a. 100 parts by weight of an organopolysiloxane having the formula: R.sub.a SiO.sub.4-a/2 wherein R is a member selected from the group consisting of substituted and unsubstituted monovalent hydrocarbon radicals; and a is a number from about 1.90 to about 2.05; b. from about 20 to about 200 parts by weight of finely divided silica filler, c. from about 5 to about 100 parts by weight of manganese carbonate having a particle size of from about 1μ to about 50μ and d. from about 5 to about 1,000 parts per million parts by weight of a platinum-containing composition, at least a part of which is platinum, the parts of platinum in said composition being based on the weight of the said organopolysiloxane component (a).
Claim 3
Dependent Claim
126 words
Silicone composition consisting essentially of a. 100 parts by weight of an organopolysiloxane having the formula: R.sub.a SiO.sub.4-a/2 wherein R is a member selected from the group consisting of substituted and unsubstituted monovalent hydrocarbon radicals; and a is a number from about 1.90 to about 2.05; b. from about 20 to about 200 parts by weight of finely divided silica filler; c. from about 5 to about 100 parts by weight of manganese carbonate having a particle size of from about 1μ to about 50μ; d. from about 5 to about 1,000 parts per million by weight of platinum, said weight of platinum being based on the weight of organopolysiloxane component (a); and e. from about 0.3 to about 6 parts by weight of organic peroxide.
Claim 4
Dependent Claim
126 words
Silicone composition consisting essentially of a. 100 parts by weight of an organopolysiloxane having the formula: R.sub.a SiO.sub.4-a/2 wherein R is a member selected from the group consisting of substituted and unsubstituted monovalent hydrocarbon radicals; and a is a number from about 1.90 to about 2.05; b. from about 20 to about 200 parts by weight of finely divided silica filler; c. from about 5 to about 100 parts by weight of manganese carbonate having a particle size of from about 1μ to about 50μ; d. from about 5 to about 1,000 parts per million by weight of platinum, said weight of platinum being based on the weight of organopolysiloxane component (a); and e. from about 0.3 to about 6 parts by weight of organic peroxide.
Claim 5
Dependent Claim
157 words
Silicone composition consisting essentially of a. 100 parts by weight of an organopolysiloxane having the formula R.sub.a Sio.sub.4-a/2 wherein R is a member selected from the group consisting of substituted and unsubstituted monovalent hydrocarbon radicals; and a is a number from about 1.90 to about 2.05, and wherein a contains at least 2 .tbd. Si-CH=CH 2 moieties in an average radical; b. from about 20 to about 200 parts by weight of finely divided silica filler; c. from about 5 to about 100 parts by weight of manganese carbonate having a particle size of from about 1μ to about 50μ; d. from about 5 to about 1,000 parts per million parts by weight of platinum, said weight of platinum being based on the weight of organopolysiloxane component (a); and e. organohydrogenpolysiloxane in such an amount that the number of .tbd. Si--H moieties is from about 0.8 to about 1.5 per .tbd.SiCH=CH 2 moiety in organpolysiloxane component (a).
Claim 6
Dependent Claim
157 words
Silicone composition consisting essentially of a. 100 parts by weight of an organopolysiloxane having the formula R.sub.a Sio.sub.4-a/2 wherein R is a member selected from the group consisting of substituted and unsubstituted monovalent hydrocarbon radicals; and a is a number from about 1.90 to about 2.05, and wherein a contains at least 2 .tbd. Si-CH=CH 2 moieties in an average radical; b. from about 20 to about 200 parts by weight of finely divided silica filler; c. from about 5 to about 100 parts by weight of manganese carbonate having a particle size of from about 1μ to about 50μ; d. from about 5 to about 1,000 parts per million parts by weight of platinum, said weight of platinum being based on the weight of organopolysiloxane component (a); and e. organohydrogenpolysiloxane in such an amount that the number of .tbd. Si--H moieties is from about 0.8 to about 1.5 per .tbd.SiCH=CH 2 moiety in organpolysiloxane component (a).
Claim 7
Dependent Claim
25 words
The silicone composition according to claim 1, wherein said component (d) is present in an amount of from about 10 to 100 parts per million.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-02 | 1979-08-04 | 1980-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-02 | 1983-08-04 | 1984-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-02 | 1987-08-04 | 1988-02-03 | $7700.00 | Window Closed / Lapsed |