US3953355A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Preparation of uranium nitride
Assignee: Energy Research and Development Administration ERDA
•
Filing: 1974-05-29
•
Granted: 1976-04-27
•
Expires: 1994-05-29
Abstract
Abstract A process for preparing actinide-nitrides from massive actinide metal which is suitable for sintering into low density fuel shapes by partially hydriding the massive metal and simultaneously dehydriding and nitriding the dehydrided portion. The process is repeated until all of the massive metal is converted to a nitride.
Inventors
- 👤 Ralph A. Potter
- 👤 Victor J. Tennery
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 15:47
CPC Classifications
C; C01; C01B; C01B21/00; C01B21/06; C01B21/0615; C01B21/063; G; G21; G21C; G21C3/00; G21C3/42; G21C3/58; G21C3/62; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
150 words
A process for producing a nitride from an actinide metal selected from the group consisting of thorium, uranium, (uranium, plutonium), plutonium, americium, and neptunium comprising the steps of: heating said metal within a reaction chamber containing a non-reactive atmosphere to a temperature within the range of 450° to 550° C.; admitting hydrogen to said reaction chamber; cooling said metal to a temperature at which partial hydriding of said metal occurs; admitting nitrogen to said reaction chamber so as to flush out said hydrogen; heating said reaction chamber through a temperature range in which dehydriding and nitriding occur; maintaining the temperature within said last-mentioned temperature range until nitrogen is substantially no longer consumed; cooling said reaction chamber to said hydriding temperature; reheating said reaction chamber to said temperature range in which dehydriding and nitriding occur; and repeating the above steps until substantially all of said metal is converted to a nitride.
Claim 2
Dependent Claim
150 words
A process for producing a nitride from an actinide metal selected from the group consisting of thorium, uranium, (uranium, plutonium), plutonium, americium, and neptunium comprising the steps of: heating said metal within a reaction chamber containing a non-reactive atmosphere to a temperature within the range of 450° to 550° C.; admitting hydrogen to said reaction chamber; cooling said metal to a temperature at which partial hydriding of said metal occurs; admitting nitrogen to said reaction chamber so as to flush out said hydrogen; heating said reaction chamber through a temperature range in which dehydriding and nitriding occur; maintaining the temperature within said last-mentioned temperature range until nitrogen is substantially no longer consumed; cooling said reaction chamber to said hydriding temperature; reheating said reaction chamber to said temperature range in which dehydriding and nitriding occur; and repeating the above steps until substantially all of said metal is converted to a nitride.
Claim 3
Dependent Claim
11 words
The process according to claim 1 wherein said metal is uranium.
Claim 4
Dependent Claim
19 words
The process according to claim 2 wherein the resulting uranium nitride has a stoichiometry of about UN 1 .74.
Claim 5
Dependent Claim
37 words
The product of the process of claim 2, wherein the product uranium nitride has a size within the range of 1 to 10 micrometers and a surface area of about 6.5 to 7 square meters per gram.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-27 | 1979-10-27 | 1980-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-27 | 1983-10-27 | 1984-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-27 | 1987-10-27 | 1988-04-27 | $7700.00 | Window Closed / Lapsed |