Process for hardening microcapsules containing hydrophobic oil droplets
Assignee: Fujifilm Holdings Corp
•
Filing: 1973-07-18
•
Granted: 1976-05-11
•
Expires: 1993-07-18
Abstract
Abstract In a process for hardening microcapsules produced by microencapsulating hydrophobic oil droplets using a complex coacervation process with gelatin as one of the hydrophilic colloids: including the steps of 1. emulsifying a water-immiscible oil in an aqueous solution of at least one first hydrophilic colloid ionizable in water and admixing an aqueous solution of at least one second hydrophilic colloid having an electric charge opposite to that of said first colloid, 2. causing coacervation of said colloids to occur by adding water thereto or adjusting the pH thereof to form coacervates, 3. cooling said coacervates to cause gelling thereof, 4. adjusting the pH to alkalinity and adding a hardening agent sequentially or simultaneously, 5. increasing the temperature so as to cause hardening, the improvement wherein glyoxal or glutaraldehyde in combination with formaldehyde is present during step (4).
Inventors
- 👤 Keiso Saeki
- 👤 Hiroharu Matsukawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 16:08
CPC Classifications
B; B01; B01J; B01J13/00; B01J13/02; B01J13/20; B01J13/206; B01J13/06; B01J13/10; B41; B41M; B41M5/00; B41M5/124; B41M5/165; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2984; Y10T428/2985; Y10T428/2987
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
116 words
In a process for hardening microcapsules produced by microencapsulating hydrophobic oil droplets using a complex coacervation process with gelatin as one of the hydrophilic colloids wherein the process includes the steps of 1. emulsifying a water-immiscible oil in an aqueous solution of at least one first hydrophilic colloid ionizable in water and admixing an aqueous solution of at least one second hydrophilic colloid having an electric charge opposite to that of said first colloid, 2. causing coacervation of said colloids to occur by adding water thereto or adjusting the pH thereof to form coacervates, 3. cooling said coacervates to cause gelling thereof, 4. adjusting the pH to alkalinity and adding a hardening agent sequentially or simultaneously,
Claim 2
Dependent Claim
116 words
In a process for hardening microcapsules produced by microencapsulating hydrophobic oil droplets using a complex coacervation process with gelatin as one of the hydrophilic colloids wherein the process includes the steps of 1. emulsifying a water-immiscible oil in an aqueous solution of at least one first hydrophilic colloid ionizable in water and admixing an aqueous solution of at least one second hydrophilic colloid having an electric charge opposite to that of said first colloid, 2. causing coacervation of said colloids to occur by adding water thereto or adjusting the pH thereof to form coacervates, 3. cooling said coacervates to cause gelling thereof, 4. adjusting the pH to alkalinity and adding a hardening agent sequentially or simultaneously,
Claim 3
Dependent Claim
138 words
increasing the temperature so as to cause hardening, the improvement wherein glyoxal or glutaraldehyde together with formaldehyde is present during step (4), the amounts employed being (a) with glyoxal, as the amount of glyoxal increases the minimum amount of formaldehyde decreases, such that when the amount of glyoxal per 100 parts of gelatin is 0.6 parts the minimum amount of formaldehyde per 100 parts of gelatin is 0.6 parts, the minimum amount of formaldehyde per 100 parts of gelatin being at least 0.05 parts, and (b) with glutaraldehyde, when the amount of glutaraldehyde per 100 parts of gelatin is less than 5 parts the minimum amount of formaldehyde is at least 0.7 parts, and when 5 or more parts of glutaraldehyde are employed the amount of formaldehyde is not less than 0.05 parts, said parts being by weight.
Claim 4
Dependent Claim
138 words
increasing the temperature so as to cause hardening, the improvement wherein glyoxal or glutaraldehyde together with formaldehyde is present during step (4), the amounts employed being (a) with glyoxal, as the amount of glyoxal increases the minimum amount of formaldehyde decreases, such that when the amount of glyoxal per 100 parts of gelatin is 0.6 parts the minimum amount of formaldehyde per 100 parts of gelatin is 0.6 parts, the minimum amount of formaldehyde per 100 parts of gelatin being at least 0.05 parts, and (b) with glutaraldehyde, when the amount of glutaraldehyde per 100 parts of gelatin is less than 5 parts the minimum amount of formaldehyde is at least 0.7 parts, and when 5 or more parts of glutaraldehyde are employed the amount of formaldehyde is not less than 0.05 parts, said parts being by weight.
Claim 5
Dependent Claim
85 words
The process of claim 1, wherein a surface active agent is additionally present during said emulsifying step; and wherein a shock-preventing agent in the form of a polyelectrolyte having an anionic functional group is present during said pH adjustment to alkalinity step, said shock-preventing agent being selected from the group consisting of modified cellulose, an anionic starch derivative, an anionic acid polysaccharide, a condensate of naphthalene sulfonic acid and Formalin, a hydroxyethyl cellulose derivative, a copolymer of vinylbenzene sulfonate, and a copolymer of sodium acrylate.
Claim 6
Dependent Claim
23 words
The process of claim 1, wherein said hydrophobic oil is a mineral oil, an animal oil, a vegetable oil or a synthetic oil.
Claim 7
Dependent Claim
22 words
The process of claim 1, wherein said hydrophilic colloids are amino acid-containing compounds, saccharide compounds, synthetic copolymers, cellulose compounds, or soluble starches.
Claim 8
Dependent Claim
31 words
The process of claim 4, wherein said colloids are gelatin, casein, alginate, gum arabic, carrageenan, styrene-maleic anhydride copolymer, methyl vinyl ether-maleic anhydride copolymer, carboxy methyl cellulose, cellulose sulfate or sulfated starch.
Claim 9
Dependent Claim
27 words
The process of claim 1, wherein one of said hydrophilic colloids is gelatin and the second of said hydrophilic collids is gum arabic or carboxy methyl cellulose.
References Cited (Backward Citations)
US3043782A
Cited
US3687865A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-11 | 1979-11-10 | 1980-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-11 | 1983-11-10 | 1984-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-11 | 1987-11-10 | 1988-05-11 | $7700.00 | Window Closed / Lapsed |