Production of fine grained ferrite bodies
Assignee: Lignes Telegraphiques et Telephoniques LTT SA
•
Filing: 1973-01-23
•
Granted: 1976-05-11
•
Expires: 1993-01-23
Abstract
Abstract The small dimension (inferior to one micrometer) of the grains of oxydes obtained by chemical precipitation is retained during the processing of the ferrimagnetic part through precise stoichiometry, cold isostatic pressing and sintering under vacuum at a temperature below 1400°C and for a duration shorter than 4 hours.
Inventors
- 👤 Andre Deschamps
- 👤 Georges Faye
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:43
CPC Classifications
B; B01; B01D; B01D47/00; C; C04; C04B; C04B35/00; C04B35/01; C04B35/26; C04B35/2675; Y; Y10; Y10S; Y10S264/00; Y10S264/58
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
126 words
A process for the production of shaped bodies of fine grained ferrimagnetic material which comprises in combination the steps: preparing a stoichiometeric suspension of salts selected from the group consisting of nitrates and chlorides corresponding to the ferrimagnetic material chemical formulation in alcohol, coprecipitating said salts in alcoholic suspension as metal hydroxides by addition thereto of a base, recovering and drying the resulting coprecipitate, baking the dried coprecipitate in air at about 700°C for about 2 hours, isostatically pressing the baked coprecipitate into a solid desired shaped body under a pressure between 10 8 and 10 9 Pascal, sintering said shaped body under a vacuum of about 10 - 5 mm/Hg for about 3 to less than 4 hours at a temperature about 1200°C to 1400°C.
Claim 2
Dependent Claim
126 words
A process for the production of shaped bodies of fine grained ferrimagnetic material which comprises in combination the steps: preparing a stoichiometeric suspension of salts selected from the group consisting of nitrates and chlorides corresponding to the ferrimagnetic material chemical formulation in alcohol, coprecipitating said salts in alcoholic suspension as metal hydroxides by addition thereto of a base, recovering and drying the resulting coprecipitate, baking the dried coprecipitate in air at about 700°C for about 2 hours, isostatically pressing the baked coprecipitate into a solid desired shaped body under a pressure between 10 8 and 10 9 Pascal, sintering said shaped body under a vacuum of about 10 - 5 mm/Hg for about 3 to less than 4 hours at a temperature about 1200°C to 1400°C.
Claim 3
Dependent Claim
14 words
The process of claim 1 wherein said sintering temperature is attained in two levels.
Claim 4
Dependent Claim
50 words
The process of claim 2 wherein the first temperature level is about 1000°C which is attained in about 10 minutes and lasts for about 1 hour and the second temperature level is about 1200°C which is followed by cooling at a cooling gradient between about 300°C to 600°C per hour.
Claim 5
Dependent Claim
18 words
The process of claim 1 in which said alcoholic suspension is continuously stirred during precipitation and subsequent washing.
Claim 6
Dependent Claim
26 words
The process of claim 1 wherein said shaped body after said sintering step is cooled at a cooling gradient between about 300°C to 600°C per hour.
References Cited (Backward Citations)
US3039963A
Cited
US3751366A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-11 | 1979-11-10 | 1980-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-11 | 1983-11-10 | 1984-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-11 | 1987-11-10 | 1988-05-11 | $7700.00 | Window Closed / Lapsed |