Assignee: Panasonic Holdings Corp
•
Filing: 1974-09-18
•
Granted: 1976-06-08
•
Expires: 1994-09-18
Abstract
Abstract A PTC thermistor composition containing barium oxide and titanium oxide as a base material, a semiconducting element to make the base material semiconductive and hafnium dioxide, and if necessary, an additive element. Due to the use of hafnium dioxide, the thermistor composition contributes to a large positive temperature coefficient of resistance. This invention also provides a novel method of making the thermistor composition, in which the addition of hafnium is carried out at the step of milling which comes after the step of calcining. By this method, hafnium can be very effectively used.
Inventors
- 👤 Tomizo Matsuoka
- 👤 Masanori Fujimura
- 👤 Yoshihiro Matsuo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:55
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/62605; C04B35/62645; C04B35/62675; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; C04B35/4684; H; H01; H01C; H01C7/00; H01C7/02; H01C7/022; H01C7/023; H01C7/025; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3205; C04B2235/3213; C04B2235/3224; C04B2235/3227; C04B2235/3231; C04B2235/3244; C04B2235/3251; C04B2235/3262; C04B2235/3268; C04B2235/3293; C04B2235/3294; C04B2235/3296; C04B2235/3298; C04B2235/34; C04B2235/3418; C04B2235/65; C04B2235/656; C04B2235/6565; C04B2235/6567; C04B2235/70; C04B2235/74; C04B2235/78; C04B2235/786; C04B2235/79
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
101 words
A PTC thermistor composition consisting essentially of a first oxide selected from the group consisting of barium oxide, barium strontium oxide, and barium lead oxide, and, on the basis of 1.00 mole of said first oxide, (A) 0.90 to 1.05 mole of an oxide selected from the group consisting of titanium dioxide and titanium stannic dioxide, (B) 0.0005 to 0.002 mole of an oxide selected from the group consisting of rare earth oxides, Nb 2 O 5 , Ta 2 O 5 , Bi 2 O 3 and Sb 2 O 3 and (C) 0.0005 to 0.10 mole of hafnium dioxide.
Claim 2
Dependent Claim
101 words
A PTC thermistor composition consisting essentially of a first oxide selected from the group consisting of barium oxide, barium strontium oxide, and barium lead oxide, and, on the basis of 1.00 mole of said first oxide, (A) 0.90 to 1.05 mole of an oxide selected from the group consisting of titanium dioxide and titanium stannic dioxide, (B) 0.0005 to 0.002 mole of an oxide selected from the group consisting of rare earth oxides, Nb 2 O 5 , Ta 2 O 5 , Bi 2 O 3 and Sb 2 O 3 and (C) 0.0005 to 0.10 mole of hafnium dioxide.
Claim 3
Dependent Claim
122 words
A PTC thermistor composition according to claim 1, wherein the PTC thermistor composition consists essentially of a first oxide selected from the group consisting barium oxide, barium strontium oxide, and barium lead oxide, and, on the basis of 1.00 mole of said first oxide, (A) 0.90 to 1.05 mole of an oxide selected from the group consisting of titanium dioxide and titanium stannic dioxide, (B) 0.0005 to 0.002 mole of an oxide selected from the group consisting of rare earth oxides, Nb 2 O 5 , Ta 2 O 5 , Bi 2 O 3 and Sb 2 O 3 , (C) 0.0005 to 0.10 mole of hafnium dioxide, and (D) 1×10 - 4 to 1.5×10 - 3 mole of manganese oxide.
Claim 4
Dependent Claim
21 words
A PTC thermistor composition according to claim 1, wherein said barium strontium oxide is (1-x)BaO.xSrO wherein x is smaller than 0.70.
Claim 5
Dependent Claim
21 words
A PTC thermistor composition according to claim 1, wherein said barium lead oxide is (1-x)BaO.xPbO wherein x is smaller than 0.80.
Claim 6
Dependent Claim
23 words
A PTC thermistor composition according to claim 1, wherein said titanium stannic dioxide is (1-x)TiO.sub..2 .xSnO 2 wherein x is smaller than 0.25.
Claim 7
Dependent Claim
28 words
A PTC thermistor composition according to claim 2, which further comprises 0.006 to 0.050 mole of SiO 2 on the basis of 1.00 mole of said first oxide.
Claim 8
Independent Claim
209 words
A method of making a PTC thermistor comprising: preparing a mixture consisting of a first oxide selected from the group consisting of barium oxide, barium strontium oxide, and barium lead oxide, and, on the basis of 1.00 mole of said first oxide, (A) 0.90 to 1.05 mole of an oxide selected from the group consisting of titanium dioxide and titanium stannic dioxide, and (B) 0.0005 to 0.002 mole of an oxide selected from the group consisting of rare earth oxides, Nb 2 O 5 , Ta 2 O 5 , Bi 2 O 3 and Sb 2 O 3 and (D) 1×10 - 4 to 1.5×10 - 3 mole of manganese oxide; calcining the thus prepared mixture at a temperature of 900° to 1250°C; milling the thus calcined material with an addition of (C) 0.0005 to 0.10 mole of hafnium dioxide on the basis of 1.00 mole of said first oxide; pressing the thus milled material mixed with the hafnium dioxide into a pressed body; firing the thus obtained pressed body at a temperature of 1240°C to 1400°C for 0.5 to 5 hours; cooling the thus fired body to 400°C at a cooling rate lower than 300°C per hour; and thereafter furnace-cooling the thus cooled body to room temperature.
Claim 9
Independent Claim
209 words
A method of making a PTC thermistor comprising: preparing a mixture consisting of a first oxide selected from the group consisting of barium oxide, barium strontium oxide, and barium lead oxide, and, on the basis of 1.00 mole of said first oxide, (A) 0.90 to 1.05 mole of an oxide selected from the group consisting of titanium dioxide and titanium stannic dioxide, and (B) 0.0005 to 0.002 mole of an oxide selected from the group consisting of rare earth oxides, Nb 2 O 5 , Ta 2 O 5 , Bi 2 O 3 and Sb 2 O 3 and (D) 1×10 - 4 to 1.5×10 - 3 mole of manganese oxide; calcining the thus prepared mixture at a temperature of 900° to 1250°C; milling the thus calcined material with an addition of (C) 0.0005 to 0.10 mole of hafnium dioxide on the basis of 1.00 mole of said first oxide; pressing the thus milled material mixed with the hafnium dioxide into a pressed body; firing the thus obtained pressed body at a temperature of 1240°C to 1400°C for 0.5 to 5 hours; cooling the thus fired body to 400°C at a cooling rate lower than 300°C per hour; and thereafter furnace-cooling the thus cooled body to room temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-08 | 1979-12-08 | 1980-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-08 | 1983-12-08 | 1984-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-08 | 1987-12-08 | 1988-06-08 | $7700.00 | Window Closed / Lapsed |