Hollow, multi-layered, cross-linked plastic structures and process for producing same
Assignee: Microporous Products LP
•
Filing: 1975-02-07
•
Granted: 1976-06-29
•
Expires: 1995-02-07
Abstract
Abstract Hollow, multi-layered plastic structures are provided comprising a layer of thermoplastic polyester material and a layer of polyethylene, the polyethylene and polyester layers being cross-linked together at their interface. A process for producing such structures which comprises charging a mold with thermoplastic polyester material, rotating and heating the mold so as to fuse and form a layer of the polyester material on the inner surface of the mold, cooling the mold to a point below the melting point of the polyester but above the melting point of a subsequently added cross-linkable polyethylene material, stopping the rotation and charging the mold with the cross-linkable polyethylene material, resuming the rotation of the mold and heating it to a temperature sufficient to fuse and cross-link the polyethylene with the polyester layer, cooling the mold to a point below the melting point of the polyethylene and removing the finished structure from the mold.
Inventors
- 👤 Camillo M. Vecchiotti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:57
CPC Classifications
B; B29; B29C; B29C41/00; B29C41/02; B29C41/04; B29C41/06; B29C41/22; H; H01; H01M; H01M50/00; H01M50/10; H01M50/116; H01M50/117; H01M50/121; H01M50/122; H01M50/124; H01M50/14; H01M50/143; B29C67/00; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
255 words
A process for producing a hollow, multi-layered cross-linked, plastic structure from a linear thermoplastic polyester and a cross-linkable polyethylene having a melting point lower than the melting point of the polyester, said process comprising the steps of: charging a mold with a sufficient amount of the thermoplastic polyester material to form a substantially uniform layer on the inner surface of said mold; heating said mold to a temperature above the melting point of the polyester; rotating said mold so as to fuse the polyester contained within the mold and to uniformly distribute the fused polyester on the inner surface of the mold; cooling said mold to a temperature below the melting point of the polyester but above that of the cross-linkable polyethylene thus crystallizing the polyester to a solid layer; stopping the rotation of the mold; charging said mold with a sufficient amount of the cross-linkable polyethylene to form a substantially uniform layer on said polyester layer; heating said mold to a temperature above the melting point of the polyethylene and sufficiently below the melting point of the polyester so as not to cause dimensional distortion of the polyester; rotating the polyethylene charged mold for a sufficient period of time to fuse said polyethylene, uniformly distribute the polyethylene on the inner surface of the polyester layer and effect cross-linking of said polyethylene so as to set the polyethylene layer and effect cross-linking of said polyethylene to said linear polyester; and stopping the rotation of said mold to remove the resulting hollow, cross-linked multi-layered polymeric structure.
Claim 2
Dependent Claim
255 words
A process for producing a hollow, multi-layered cross-linked, plastic structure from a linear thermoplastic polyester and a cross-linkable polyethylene having a melting point lower than the melting point of the polyester, said process comprising the steps of: charging a mold with a sufficient amount of the thermoplastic polyester material to form a substantially uniform layer on the inner surface of said mold; heating said mold to a temperature above the melting point of the polyester; rotating said mold so as to fuse the polyester contained within the mold and to uniformly distribute the fused polyester on the inner surface of the mold; cooling said mold to a temperature below the melting point of the polyester but above that of the cross-linkable polyethylene thus crystallizing the polyester to a solid layer; stopping the rotation of the mold; charging said mold with a sufficient amount of the cross-linkable polyethylene to form a substantially uniform layer on said polyester layer; heating said mold to a temperature above the melting point of the polyethylene and sufficiently below the melting point of the polyester so as not to cause dimensional distortion of the polyester; rotating the polyethylene charged mold for a sufficient period of time to fuse said polyethylene, uniformly distribute the polyethylene on the inner surface of the polyester layer and effect cross-linking of said polyethylene so as to set the polyethylene layer and effect cross-linking of said polyethylene to said linear polyester; and stopping the rotation of said mold to remove the resulting hollow, cross-linked multi-layered polymeric structure.
Claim 3
Dependent Claim
42 words
A process as defined in claim 1 wherein said thermoplastic polyester is a glass-fiber filled polyester of terephthalic acid and a glycol of the series HO(CH 2 )n OH wherein n is a whole number within the range of 2 to 10.
Claim 4
Dependent Claim
16 words
A process as defined in claim 2 wherein said cross-linkable polyethylene includes a fire retardant agent.
Claim 5
Dependent Claim
39 words
A process as defined in claim 3 wherein said cross-linkable polyethylene includes a cross-linking agent selected from the group consisting of dicumyl peroxide, 2-5 dimethyl 2,5-di(t-butyl peroxy) hexane and 2,5-dimethyl-2,5-di(t-butyl peroxy) hexyne -3 and a halogenated fire retardant agent.
Claim 6
Dependent Claim
250 words
A process for producing a fire retardant, hollow, multi-layered, cross-linked, plastic structure comprising the following steps: charging a mold with a sufficient amount of a linear, thermoplastic polyester material having a melting point between about 400°F and about 500°F to form a substantially uniform layer on the inner surface of said mold biaxially rotating and heating said mold to a temperature between about 500°F and about 650°F for a period of time between about 20 and about 30 minutes so as to fuse the polyester contained within the mold and uniformly distribute said fused polyester on the inner surface of said mold; cooling said mold while maintaining its biaxial rotation to a temperature between about 280°F and about 350°F to set the polyester to a substantially set layer; stopping the rotation of the mold and charging said mold with a sufficient amount of cross-linkable polyethylene including a cross-linking agent and a fire retardant agent; biaxially rotating and heating the polyethylene charged mold to a temperature between about 425°F and about 450°F for a period of time between about 20 and about 25 minutes so as to uniformly distribute the polyethylene on the inner surface of the polyester layer and effect cross-linking of said polyethylene and said linear polyester at their interface; cooling said mold to a temperature below the melting point of said polyethylene so as to substantially set the polyethylene layer; and stopping the rotation of said mold to remove the resulting fire retardant, hollow, cross-linked, multi-layered polymeric structure.
Claim 7
Dependent Claim
250 words
A process for producing a fire retardant, hollow, multi-layered, cross-linked, plastic structure comprising the following steps: charging a mold with a sufficient amount of a linear, thermoplastic polyester material having a melting point between about 400°F and about 500°F to form a substantially uniform layer on the inner surface of said mold biaxially rotating and heating said mold to a temperature between about 500°F and about 650°F for a period of time between about 20 and about 30 minutes so as to fuse the polyester contained within the mold and uniformly distribute said fused polyester on the inner surface of said mold; cooling said mold while maintaining its biaxial rotation to a temperature between about 280°F and about 350°F to set the polyester to a substantially set layer; stopping the rotation of the mold and charging said mold with a sufficient amount of cross-linkable polyethylene including a cross-linking agent and a fire retardant agent; biaxially rotating and heating the polyethylene charged mold to a temperature between about 425°F and about 450°F for a period of time between about 20 and about 25 minutes so as to uniformly distribute the polyethylene on the inner surface of the polyester layer and effect cross-linking of said polyethylene and said linear polyester at their interface; cooling said mold to a temperature below the melting point of said polyethylene so as to substantially set the polyethylene layer; and stopping the rotation of said mold to remove the resulting fire retardant, hollow, cross-linked, multi-layered polymeric structure.
Claim 8
Dependent Claim
77 words
A process as defined in claim 5 wherein said cooling of the mold containing said fused polyester is effected by exposing the mold to a fan and the cooling of the mold containing both the set polyester layer and the fused polyethylene layer is achieved in a three-step procedure including exposing the mold to a fan for about 8 minutes followed by a water spray for about 10 minutes and a fan again for about 2 minutes.
References Cited (Backward Citations)
US2649622A
Cited
US2919474A
Cited
US3214422A
Cited
US3449191A
Cited
US3455483A
Cited
US3350745A
Cited
US3816582A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |