Metal bonding glass-ceramic compositions having improved hardness
Assignee: ABB Inc USA
•
Filing: 1975-08-07
•
Granted: 1976-08-31
•
Expires: 1995-08-07
Abstract
Abstract A metal member is coated with or embedded in a high-magnesia glass-ceramic material having the approximate composition of about 60 to 80 weight percent SiO 2 , 12 to 20 weight percent Li 2 O, 2 to 14 weight percent MgO, 1.5 to 6 weight percent P 2 O 5 , 1 to 7 weight percent of an alkali oxide selected from the group consisting of K 2 O and Na 2 O and their mixtures, 0 to 2 weight percent of a transition metal oxide selected from the group consisting of Co 3 O 4 , MnO 2 , Fe 2 O 3 , V 2 O 5 and WO 3 and their mixtures, 0 to 5 weight percent PbO, 0 to 2 weight percent Al 2 O 3 and 0 to 1 weight percent As 2 O 3 .
Inventors
- 👤 Douglas M. Mattox
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:45
CPC Classifications
H; H01; H01B; H01B19/00; C; C03; C03B; C03B19/00; C03B19/02; C03B32/00; C03B32/02; C03C; C03C10/00; C03C10/0009; C03C10/0036; C03C10/0045; C03C27/00; C03C27/02; H01B3/00; H01B3/02; H01B3/08; H01B3/087; H01B3/088
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
252 words
A method of bonding a glass-ceramic material to a metal member comprising the steps of: A. forming a fluid glass composition consisting essentially of about 60 to 80 weight percent SiO 2 12 to 20 weight percent Li 2 O, 2 to 14 weight percent MgO, 1.5 to 6 weight percent P 2 O 5 , 1 to 7 weight percent of an alkali oxide selected from the group consisting of K 2 O and Na 2 O and their mixtures, 0 to 2 weight percent of a transition metal oxide selected from the group consisting of Co 3 O 4 , MnO 2 , Fe 2 O 3 , V 2 O 5 and WO 3 and their mixtures, 0 to 5 weight percent PbO, 0 to 2 weight percent Al 2 O 3 and 0 to 1 weight percent As 2 O 3 ; B. applying the glass composition directly to a metal member; C. cooling the glass to a temperature of below about 600°C; D. heating the glass and metal member up to a temperature of about 900°C at a rate of about 10°-80°C per hour, to form a glass-ceramic from the glass composition which intimately bonds directly to the metal member, said glass-ceramic being a substantially homogeneous microcrystalline mass of ceramic having a Knoop handness value of over about 660 in a glass matrix; E. maintaining the temperature of the glass-ceramic bonded metal member for about 1/2-10 hours; F. cooling the glass-ceramic bonded metal member to room temperature.
Claim 2
Independent Claim
252 words
A method of bonding a glass-ceramic material to a metal member comprising the steps of: A. forming a fluid glass composition consisting essentially of about 60 to 80 weight percent SiO 2 12 to 20 weight percent Li 2 O, 2 to 14 weight percent MgO, 1.5 to 6 weight percent P 2 O 5 , 1 to 7 weight percent of an alkali oxide selected from the group consisting of K 2 O and Na 2 O and their mixtures, 0 to 2 weight percent of a transition metal oxide selected from the group consisting of Co 3 O 4 , MnO 2 , Fe 2 O 3 , V 2 O 5 and WO 3 and their mixtures, 0 to 5 weight percent PbO, 0 to 2 weight percent Al 2 O 3 and 0 to 1 weight percent As 2 O 3 ; B. applying the glass composition directly to a metal member; C. cooling the glass to a temperature of below about 600°C; D. heating the glass and metal member up to a temperature of about 900°C at a rate of about 10°-80°C per hour, to form a glass-ceramic from the glass composition which intimately bonds directly to the metal member, said glass-ceramic being a substantially homogeneous microcrystalline mass of ceramic having a Knoop handness value of over about 660 in a glass matrix; E. maintaining the temperature of the glass-ceramic bonded metal member for about 1/2-10 hours; F. cooling the glass-ceramic bonded metal member to room temperature.
Claim 3
Dependent Claim
57 words
The method of claim 1, wherein the glass is formed in step (A) by heating at a temperature between about 1000° to 1500°C and the glass composition is applied to the metal member in step (B) by pouring the glass composition into a mold containing the metal member, to embed the metal member in the glass composition.
Claim 4
Dependent Claim
48 words
The method of claim 2, wherein the metal member has a coefficient of thermal expansion of between about 8 × 10.sup. -6 in/in/°C and 18 × 10.sup. -6 in/in/°C and the glass-ceramic bonded metal member is cooled in step (F) over about a 6 to 48 hour period.
Claim 5
Dependent Claim
62 words
The method of claim 3, wherein the mold is preheated and the metal member has a coefficient of thermal expansion of between about 8 × 10.sup. -6 in/in/°C and 13 × 10.sup. -6 in/in/°C, a relatively smooth surface and is oxidized before step (C) to form a dense oxide layer thereon having a thickness of between about 0.8 to about 10 microns.
Claim 6
Dependent Claim
54 words
The method of claim 3, wherein, in step (D) the P 2 O 5 nucleates crystals of lithium phosphate which form sites for growth of lithium metasilicate crystals, which lithium metasilicate crystals in turn form sites for growth of lithium disilicate crystals and wherein the ceramic phase constitutes 60-95 volume percent of the glass-ceramic.
Claim 7
Dependent Claim
32 words
The method of claim 3, wherein the composition contains about 4-12 weight percent MgO, 2 to 4 weight percent P 2 O 5 and 0 weight percent Al 2 O 3 .
Claim 8
Dependent Claim
19 words
The method of claim 4, wherein the oxidized metal member has a thin pre-glassed coating on the oxide layer.
References Cited (Backward Citations)
US2089791A
Cited
US3730698A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-31 | 1980-03-01 | 1980-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-31 | 1984-03-01 | 1984-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-31 | 1988-03-01 | 1988-08-31 | $7700.00 | Window Closed / Lapsed |