Embossed decorative sheet-type material and process for making same
Assignee: Tarkett AB
•
Filing: 1974-12-30
•
Granted: 1976-08-31
•
Expires: 1994-12-30
Abstract
Abstract Embossed decorative sheet-type covering material such as sheet vinyl flooring is prepared by forming a foamed plastic layer over a pigmented layer on a substrate and then selectively crushing the foamed layer by mechanical embossing to produce selectively crushed transparent portions through which the pigmented layer is visible. Printing is normally included on the upper surface of the plastic layer before the latter is foamed and a conventional wear layer is also preferably used. In a preferred embodiment, a foamed undercoat layer is also used to reduce embossing requirements. Conventional materials are preferred, such as latex coated felt for the substrate, cured, foamed polyvinyl chloride organosol or plastisol for the foamed layers and cured, clear polyvinyl chloride organosol for the wear layer.
Inventors
- 👤 Kenneth J. Faust
- 👤 Richard L. Maass
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:43
CPC Classifications
B; B44; B44C; B44C1/00; B44C1/20; B44C1/205; B32; B32B; B32B5/00; B32B5/18; B32B1/00; B32B5/22; B32B5/24; B32B5/245; B32B7/00; B32B7/04; B32B7/12; B44C3/00; B44C3/04; B44C3/044; B44F; B44F1/00; B44F1/06; D; D06; D06N; D06N7/00; D06N7/0005; D06N7/0028; D06N7/0034; B32B2255/00; B32B2255/02; B32B2307/00; B32B2307/40; B32B2307/412; B32B2451/00; B32B2471/00; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1023; Y10T156/1039; Y10T156/1041; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24496; Y10T428/24504; Y10T428/24512; Y10T428/24521
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
72 words
Decorative sheet-type covering material having an embossed surface and comprising: a. a substrate; b. a pigmented layer; c. a foamed plastic layer adhered to said pigmented layer and having selectively crushed transparent portions through which said pigmented layer is visible; and d. a selectively partially crushed foamed plastic undercoat under said pigmented layer with the selectively partially crushed portions thereof in register with the selectively crushed portions of said foamed plastic layer.
Claim 2
Dependent Claim
72 words
Decorative sheet-type covering material having an embossed surface and comprising: a. a substrate; b. a pigmented layer; c. a foamed plastic layer adhered to said pigmented layer and having selectively crushed transparent portions through which said pigmented layer is visible; and d. a selectively partially crushed foamed plastic undercoat under said pigmented layer with the selectively partially crushed portions thereof in register with the selectively crushed portions of said foamed plastic layer.
Claim 3
Dependent Claim
12 words
Material of claim 1 in which the foamed plastic layer comprises PVC.
Claim 4
Dependent Claim
24 words
Material of claim 2 which also includes a clear, cured wear layer over the foamed plastic layer, said wear layer being polyurethane or PVC.
Claim 5
Dependent Claim
16 words
Material of claim 3 including printing applied to the foamed plastic layer under the wear layer.
Claim 6
Dependent Claim
13 words
Material of claim 4 in which the substrate comprises felt coated with latex.
Claim 7
Dependent Claim
19 words
Material of claim 4 in which the pigmented layer comprises printing between the undercoat and the foamed plastic layer.
Claim 8
Dependent Claim
30 words
Material of claim 4 in which the substrate comprises felt coated with latex and the foamed plastic undercoat is adhered to the substrate and comprises cured PVC plastisol or organosol.
Claim 9
Dependent Claim
31 words
Material of claim 4 in which the selectively crushed transparent portions of the foamed plastic layer have a thickness less than the thickness of said layer prior to the foaming thereof.
Claim 10
Dependent Claim
13 words
Material of claim 4 in which the selectively crushed foamed layer is nonpigmented.
Claim 11
Dependent Claim
72 words
Decorative sheet-type covering material having an embossed surface and comprising: a. a substrate; b. a pigmented, selectively partially crushed, foamed, plastic undercoat adhered to said substrate; and c. a foamed, plastic layer adhered to said undercoat and having selectively crushed transparent portions through which said pigmented undercoat is visible, the selectively crushed transparent portions of said foamed plastic layer being in register with the selectively partially crushed portions of said pigmented undercoat.
Claim 12
Dependent Claim
72 words
Decorative sheet-type covering material having an embossed surface and comprising: a. a substrate; b. a pigmented, selectively partially crushed, foamed, plastic undercoat adhered to said substrate; and c. a foamed, plastic layer adhered to said undercoat and having selectively crushed transparent portions through which said pigmented undercoat is visible, the selectively crushed transparent portions of said foamed plastic layer being in register with the selectively partially crushed portions of said pigmented undercoat.
Claim 13
Dependent Claim
88 words
A process for making decorative sheet-type covering material having an embossed surface which comprises: a. forming a sheet-type material having a substrate, a foamed plastic undercoat adhered to said substrate, a foamed plastic layer and a pigmented layer between the foamed plastic layer and the foamed undercoat; and b. selectively crushing said foamed plastic layer to form crushed transparent portions thereof through which the pigmented layer is visible while selectively partially crushing portions of said foamed undercoat in register with the crushed transparent portions of said plastic layer.
Claim 14
Dependent Claim
88 words
A process for making decorative sheet-type covering material having an embossed surface which comprises: a. forming a sheet-type material having a substrate, a foamed plastic undercoat adhered to said substrate, a foamed plastic layer and a pigmented layer between the foamed plastic layer and the foamed undercoat; and b. selectively crushing said foamed plastic layer to form crushed transparent portions thereof through which the pigmented layer is visible while selectively partially crushing portions of said foamed undercoat in register with the crushed transparent portions of said plastic layer.
Claim 15
Dependent Claim
27 words
The process of claim 11 in which a clear plastic wear layer is formed over the foamed plastic layer prior to selective crushing of the foamed layer.
Claim 16
Dependent Claim
19 words
The process of claim 12 in which the foamed plastic layer is formed with a layer of printing thereon.
Claim 17
Dependent Claim
31 words
The process of claim 11 in which the substrate comprises latex coated felt and the foamed plastic layer and foamed undercoat and wear layer each comprise cured PVC organosol or plastisol.
Claim 18
Dependent Claim
236 words
A process for making decorative sheet-type covering material having an embossed surface which comprises: a. forming a foamable undercoat of wet PVC plastisol or organosol containing blowing agent on a latex coated felt substrate, said foamable undercoat being pigmented and being between about 2 and about 20 mils thick; b. heating the undercoat formed in step (a) under temperature conditions sufficient to gel said undercoat without foaming same; c. applying a wet, nonpigmented layer of foamable PVC plastisol or organosol over the pigmented undercoat, said nonpigmented foamable plastisol or organosol being between about 4 and about 20 mils thick; d. heating the layer of step (c) sufficient to gel same without foaming either the layer of step (c) or the undercoat of step (a); e. applying printing to the gelled, nonpigmented, foamable layer; f. applying a wet wear layer of PVC plastisol or organosol to the printed and gelled, nonpigmented, foamable layer, said wear layer having a thickness between about 4 and about 20 mils; g. heating the sheet sufficiently to cure the wear layer and cure and foam the undercoat and nonpigmented, foamable layers; and h. selectively crushing portions of the sheet by mechanical embossing to form transparent portions of the nonpigmented, foamed layer, at least some of such transparent portions having a thickness less than the thickness of the layer of step (c) and to simultaneously partially crush portions of the nonpigmented, foamed layer.
Claim 19
Dependent Claim
236 words
A process for making decorative sheet-type covering material having an embossed surface which comprises: a. forming a foamable undercoat of wet PVC plastisol or organosol containing blowing agent on a latex coated felt substrate, said foamable undercoat being pigmented and being between about 2 and about 20 mils thick; b. heating the undercoat formed in step (a) under temperature conditions sufficient to gel said undercoat without foaming same; c. applying a wet, nonpigmented layer of foamable PVC plastisol or organosol over the pigmented undercoat, said nonpigmented foamable plastisol or organosol being between about 4 and about 20 mils thick; d. heating the layer of step (c) sufficient to gel same without foaming either the layer of step (c) or the undercoat of step (a); e. applying printing to the gelled, nonpigmented, foamable layer; f. applying a wet wear layer of PVC plastisol or organosol to the printed and gelled, nonpigmented, foamable layer, said wear layer having a thickness between about 4 and about 20 mils; g. heating the sheet sufficiently to cure the wear layer and cure and foam the undercoat and nonpigmented, foamable layers; and h. selectively crushing portions of the sheet by mechanical embossing to form transparent portions of the nonpigmented, foamed layer, at least some of such transparent portions having a thickness less than the thickness of the layer of step (c) and to simultaneously partially crush portions of the nonpigmented, foamed layer.
Claim 20
Dependent Claim
8 words
The product of the process of claim 15.
Claim 21
Dependent Claim
80 words
A process for making decorative sheet-type covering material having an embossed surface which comprises: a. forming a sheet-type material having a substrate, a pigmented foamed undercoat adhered to said substrate and a foamed plastic layer adhered to said pigmented undercoat; and b. selectively crushing said foamed plastic layer to form crushed transparent portions thereof through which said pigmented undercoat is visible while selectively partially crushing portions of said undercoat in register with the crushed transparent portions of the plastic layer.
Claim 22
Dependent Claim
80 words
A process for making decorative sheet-type covering material having an embossed surface which comprises: a. forming a sheet-type material having a substrate, a pigmented foamed undercoat adhered to said substrate and a foamed plastic layer adhered to said pigmented undercoat; and b. selectively crushing said foamed plastic layer to form crushed transparent portions thereof through which said pigmented undercoat is visible while selectively partially crushing portions of said undercoat in register with the crushed transparent portions of the plastic layer.
References Cited (Backward Citations)
US3104192A
Cited
US3196062A
Cited
US3196030A
Cited
US3408248A
Cited
US3399106A
Cited
US3666604A
Cited
US3655312A
Cited
US3808024A
Cited
US3804700A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-31 | 1980-03-01 | 1980-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-31 | 1984-03-01 | 1984-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-31 | 1988-03-01 | 1988-08-31 | $7700.00 | Window Closed / Lapsed |