Method for producing impact resistant thermoplastic resin by continuous bulk polymerization
Assignee: Toray Industries Inc
•
Filing: 1974-06-12
•
Granted: 1976-09-21
•
Expires: 1994-06-12
Abstract
Abstract A method is provided for continuously manufacturing high impact strength thermoplastic resins comprised of the sequential steps of (a) bulk-polymerizing a monomer solution, which contains a diene type rubber polymer or a graft polymer obtained by extracting the rubber polymer particle or vinyl monomer grafted polymer particle in latex with vinyl monomers which contain 5-20 percent by weight of water at a temperature of 85°-135°C, while continuously stirring the solution, vaporizing the volatile components, condensing the volatile component and recycling them back to reaction mixture, until the solid content in the reaction mixture reaches 40-75 percent by weight, and thereafter (b) bulk polymerizing the resulting prepolymer solution under the condition that plug-flowing can be attained with a temperature gradient 100°-170°C at the top of the reaction vessel and 170°-270°C at the bottom thereof, while the volatile component of the mixture are evaporated off, condensed and recycled to the reaction mixture, until the solid content is at least 90 percent by weight.
Inventors
- 👤 Takehiko Okamoto
- 👤 Akihiko Kishimoto
- 👤 Ikuo Nagai
- 👤 Hiroshi Sato
- 👤 Hotsuma Okasaka
- 👤 Masakazu Inoue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:31
CPC Classifications
C; C08; C08F; C08F285/00; C08F279/00; C08F279/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
292 words
The method for the manufacture of high impact resistant thermoplastic resin by continuous bulk polymerization which comprises the steps of: A. continuously charging a prepolymerization reactor with (1) a vinyl monomer solution of a vinyl composition which contains about 1-40 percent by weight of a diene type rubber polymer or a graft polymer obtained by extracting rubber polymer particles or vinyl monomer grafter rubber polymer particles in latex with vinyl monomers wherein said vinyl monomers consist of a. 60-90 percent by weight of styrene and 40-10 percent by weight of acrylonitrile or b. 0-70 percent by weight of styrene, 50-98 percent by weight of methylmethacrylate and 0-35 percent by weight of acrylonitrile and (2) 5-20 percent by weight of water; B. mixing said monomer solution so as to maintain a substantially uniform mixture; C. prepolymerizing said monomer solution at about 95°-130°C until the concentration of the solid contents of the resulting reaction product is about 40-75 percent by weight, with generation of vapor of water and monomer during said prepolymerization reaction; D. while simultaneously condensing the vapor volatilized during the prepolymerization reaction, separating the monomer solution from the resulting condensate and recycling the monomer solution at a rate of 20-60 percent by weight of feed monomer solution back to the prepolymerization reaction whereby a prepolymer solution is obtained; E. charging said prepolymer solution in a polymerization reactor; F. plug-flow advancing said prepolymer solution through said second reactor while gradually heating said prepolymer solution in a plurality of stages, starting at a temperature of about 100°-170°C up to about a temperature of 170°-270°C, polymerizing said prepolymer solution while vaporizing and recycling 5-20 percent by weight of the volatiles until the concentration of the solid components is at least about 90 percent by weight.
Claim 2
Independent Claim
292 words
The method for the manufacture of high impact resistant thermoplastic resin by continuous bulk polymerization which comprises the steps of: A. continuously charging a prepolymerization reactor with (1) a vinyl monomer solution of a vinyl composition which contains about 1-40 percent by weight of a diene type rubber polymer or a graft polymer obtained by extracting rubber polymer particles or vinyl monomer grafter rubber polymer particles in latex with vinyl monomers wherein said vinyl monomers consist of a. 60-90 percent by weight of styrene and 40-10 percent by weight of acrylonitrile or b. 0-70 percent by weight of styrene, 50-98 percent by weight of methylmethacrylate and 0-35 percent by weight of acrylonitrile and (2) 5-20 percent by weight of water; B. mixing said monomer solution so as to maintain a substantially uniform mixture; C. prepolymerizing said monomer solution at about 95°-130°C until the concentration of the solid contents of the resulting reaction product is about 40-75 percent by weight, with generation of vapor of water and monomer during said prepolymerization reaction; D. while simultaneously condensing the vapor volatilized during the prepolymerization reaction, separating the monomer solution from the resulting condensate and recycling the monomer solution at a rate of 20-60 percent by weight of feed monomer solution back to the prepolymerization reaction whereby a prepolymer solution is obtained; E. charging said prepolymer solution in a polymerization reactor; F. plug-flow advancing said prepolymer solution through said second reactor while gradually heating said prepolymer solution in a plurality of stages, starting at a temperature of about 100°-170°C up to about a temperature of 170°-270°C, polymerizing said prepolymer solution while vaporizing and recycling 5-20 percent by weight of the volatiles until the concentration of the solid components is at least about 90 percent by weight.
Claim 3
Dependent Claim
34 words
The method according to claim 1 wherein said graft polymer is obtained by graft polymerizing 2-45 parts of said vinyl compound onto 55-98 parts of said diene type rubber polymer in the emulsion rate.
Claim 4
Dependent Claim
25 words
The method according to claim 1 wherein the diene type rubber polymer is selected from the group consisting of polybutadiene, styrene-butadiene copolymer, and acrylonitrile-butadiene copolymer.
Claim 5
Dependent Claim
46 words
The method according to claim 1 wherein the amount of the vapor volatilized from the monomer solution during prepolymerization is maintained at 20-60 percent by weight of the charged amount of monomer solution by controlling the pressure within said first reactor at 0.5-2 kg/cm 2 gauge.
Claim 6
Dependent Claim
43 words
The method according to claim 1 wherein the vapor volatilized off is thereafter separated in a first portion comprised of the monomer solution which is condensed and recycled to said first reactor and a second portion comprised essentially of water which is discarded.
Claim 7
Dependent Claim
77 words
The method according to claim 1 wherein an amount 20-60 percent by weight of the monomer solution charged into the said first reactor is vaporized from the reaction mixture and separated in a first portion comprised of said monomer solution which is condensed and recycled to said first reactor and a second portion comprised of water which is discarded, said amount of vaporized composition being maintained by controlling the rate of condensate recovery from said first reactor.
Claim 8
Dependent Claim
21 words
The method according to claim 1 wherein said prepolymer solution is polymerized to a solids content of 55-65 percent by weight.
Claim 9
Dependent Claim
23 words
The process according to claim 1 wherein 5-10 percent by weight of the volatilized compound is condensed and refluxed in said second reactor.
Claim 10
Dependent Claim
16 words
The method defined in claim 1 wherein said percent by weight of water is 5-15 percent.
References Cited (Backward Citations)
US3439065A
Cited
US3660534A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-21 | 1980-03-22 | 1980-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-21 | 1984-03-22 | 1984-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-21 | 1988-03-22 | 1988-09-21 | $7700.00 | Window Closed / Lapsed |