Process for the polymerization of olefins and catalytic products
Assignee: Solvay SA
•
Filing: 1971-10-18
•
Granted: 1976-10-05
•
Expires: 1991-10-18
Abstract
Abstract This invention relates to the polymerization of α-olefins and to catalysts and to cocatalysts for that purpose wherein the polymerization is carried out in the presence of a catalyst comprising an organometallic compound of a metal of Groups IA, IIA, IIB, IIIA, and IVA of the Periodic Table and a cocatalyst comprising a reaction product of a halogenated derivative of a transition metal of Groups IVB, VB, and VIB of the Periodic Table and a hydrous divalent metal salt of a carboxylic acid, the cocatalyst having a gram equivalent ratio of halogen/divalent metal plus transition metal greater than 0.5. The invention also comprises the method of making the cocatalysts.
Inventors
- 👤 Andre Delbouille
- 👤 Jean-Louis Derroitte
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:04
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
117 words
A catalyst for the polymerization and the copolymerization of α-olefins comprising an organometallic compound of a metal of Groups IA, IIA, IIB, IIIA, and IVA of the Periodic Table and a solid cocatalyst comprising the reaction product of a halogenated compound of a transition metal of Groups IVB, VB and VIB of the Periodic Table selected from the group consisting of halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides and a solid divalent metal salt of a carboxylic acid containing at least one molecule of water of hydration per atom of divalent metal and the metal selected from magnesium, calcium and zinc, the cocatalyst having a gram equivalent ratio of halogen/divalent metal plus transition metal of at least about 0.7.
Claim 2
Dependent Claim
117 words
A catalyst for the polymerization and the copolymerization of α-olefins comprising an organometallic compound of a metal of Groups IA, IIA, IIB, IIIA, and IVA of the Periodic Table and a solid cocatalyst comprising the reaction product of a halogenated compound of a transition metal of Groups IVB, VB and VIB of the Periodic Table selected from the group consisting of halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides and a solid divalent metal salt of a carboxylic acid containing at least one molecule of water of hydration per atom of divalent metal and the metal selected from magnesium, calcium and zinc, the cocatalyst having a gram equivalent ratio of halogen/divalent metal plus transition metal of at least about 0.7.
Claim 3
Dependent Claim
78 words
The catalyst of claim 1 wherein the halogenated compound a transition metal is selected from the group consisting of the halies, oxyhalides, alkoxyhalides and oxyalkoxyhalides of a metal selected from the group consisting of titanium, zirconium, vanadium and chromium; the solid divalent metal salt of a carboxylic acid contains at least 1 molecule of water of hydration per atom of divalent metal and is selected from the group consisting of aliphatic and aromatic monocarboxylates and polycarboxylates of magnesium.
Claim 4
Dependent Claim
27 words
The catalyst of claim 2 wherein the halogenated compound is titanium tetrachloride and the organometallic compound is an organoaluminum compound and the ratio is greater than 0.9.
Claim 5
Dependent Claim
115 words
A cocatalyst for use with an organometallic compound of a metal of Groups IA, IIA, IIB, IIIA, and IVA of the Periodic Table to catalyze the polymerization and copolymerization of α-olefins comprising the reaction product of a halogenated compound of a transition metal of Groups IVB, VB, and VIB of the Periodic Table selected from the group consisting of halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides and a solid divalent metal salt of a carboxylic acid containing at least one molecule of water of hydration per atom of divalent metal and the metal selected from magnesium, calcium and zinc, the cocatalyst having a gram equivalent ratio of halogen/divalent metal plus transistion metal of at least about 0.7.
Claim 6
Dependent Claim
115 words
A cocatalyst for use with an organometallic compound of a metal of Groups IA, IIA, IIB, IIIA, and IVA of the Periodic Table to catalyze the polymerization and copolymerization of α-olefins comprising the reaction product of a halogenated compound of a transition metal of Groups IVB, VB, and VIB of the Periodic Table selected from the group consisting of halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides and a solid divalent metal salt of a carboxylic acid containing at least one molecule of water of hydration per atom of divalent metal and the metal selected from magnesium, calcium and zinc, the cocatalyst having a gram equivalent ratio of halogen/divalent metal plus transistion metal of at least about 0.7.
Claim 7
Dependent Claim
79 words
The cocatalyst of claim 4 wherein the halogenated compound of a transition metal is selected from the group consisting of the halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides of a metal selected from the group consisting of titanium, zirconium, vanadium, and chromium; the solid divalent metal salt of a carboxylic acid contains at least 1 molecule of water of hydration per atom of divalent metal and is selected from the group consisting of aliphatic and aromatic monocarboxylates and polycarboxylates of magnesium.
Claim 8
Dependent Claim
33 words
The cocatalyst of claim 4 wherein the solid salt is a hydrated magnesium benzoate having more than 1 molecule of water per atom of divalent metal and the halogenated compound is titanium tetrachloride.
Claim 9
Dependent Claim
19 words
The cocatalyst of claim 4 wherein the halogenated compound is titanium tetrachloride and the solid salt is magnesium butyrate.
Claim 10
Dependent Claim
36 words
A process for the polymerization and copolymerization of α-olefins which comprises contacting the olefins, at a temperature and at a pressure sufficient to initiate the reaction, with a catalytic amount of the catalyst of claim 2.
Claim 11
Dependent Claim
36 words
A process for the polymerization and copolymerization of α-olefins which comprises contacting the olefins, at a temperature and at a pressure sufficient to initiate the reaction, with a catalytic amount of the catalyst of claim 3.
Claim 12
Dependent Claim
138 words
A process for the polymerization of α-olefins which comprises contacting the α-olefins, at a temperature and at a pressure sufficient to initiate the reaction, with a catalytic amount of a catalyst comprising an organometallic compound of a metal of Groups IA, IIA, IIB, IIIA, and IVA of the Periodic Table and a solid cocatalyst comprising the reaction product of a halogenated compound of a transition metal of Groups IVB, VB and VIB of the Periodic Table selected from the group consisting of halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides and a solid divalent metal salt of a carboxylic acid containing at least one molecule of water of hydration per atom of divalent metal and the metal selected from magnesium, calcium and zinc, the cocatalyst having a gram equivalent ratio of halogen/divalent metal plus transition metal of at least about 0.7.
Claim 13
Dependent Claim
138 words
A process for the polymerization of α-olefins which comprises contacting the α-olefins, at a temperature and at a pressure sufficient to initiate the reaction, with a catalytic amount of a catalyst comprising an organometallic compound of a metal of Groups IA, IIA, IIB, IIIA, and IVA of the Periodic Table and a solid cocatalyst comprising the reaction product of a halogenated compound of a transition metal of Groups IVB, VB and VIB of the Periodic Table selected from the group consisting of halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides and a solid divalent metal salt of a carboxylic acid containing at least one molecule of water of hydration per atom of divalent metal and the metal selected from magnesium, calcium and zinc, the cocatalyst having a gram equivalent ratio of halogen/divalent metal plus transition metal of at least about 0.7.
Claim 14
Dependent Claim
83 words
The process of claim 10 wherein the olefin is ethylene, the halogenated compound of a transition metal is selected from the group consisting of the halides, oxyhalides alkoxyhalides and oxyalkoxyhalides of a metal selected from the group consisting of titanium, zirconium, vanadium and chronium; the solid divalent metal salt of a carboxylic acid contains at least 1 molecule of water of hydration per atom of divalent metal and is selected from the group consisting of aliphatic and aromatic monocarboxylates and polycarboxylates of magnesium.
Claim 15
Dependent Claim
27 words
The method of claim 11 wherein the halogenated compound is titanium tetrachloride and the organometallic compound is an organoaluminum compound, and the ratio is greater than 0.9.
Claim 16
Dependent Claim
60 words
A method of making the cocatalyst of claim 4 comprising the steps of reacting the halogenated compound with the solid divalent metal salt at a temperature and for a time sufficient to form a solid reaction product and in proportions sufficient that the product has a gram equivalent ratio of halogen/divalent metal plus transition metal of at least about 0.7.
Claim 17
Dependent Claim
44 words
The method of claim 13 wherein the reaction between the halogenated compound and solid divalent meetal salt is carried out at a temperature between 0° and 300°C, and the proportions used are sufficient to give a final product having a ratio greater than 0.8.
Claim 18
Dependent Claim
77 words
The method of claim 14 wherein the halogenated compound of a transition metal is selected from the group consisting of the halides, oxyhalides, alkoxyhalides and oxyalkoxyhalides of a metal selected from the group consisting of titanium, zirconium, vanadium and chromium the solid divalent metal salt of a carboxylic acid has at least 1 molecule of water per atom of divalent metal and is selected from the group consisting of aliphatic and aromatic monocarboxylates and polycarboxylates of magnesium.
Claim 19
Dependent Claim
36 words
A process for the polymerization and copolymerization of α-olefins which comprises contacting the olefins, at a temperature and at a pressure sufficient to initiate the reaction, with a catalytic amount of the catalyst of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-05 | 1980-04-05 | 1980-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-05 | 1984-04-05 | 1984-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-05 | 1988-04-05 | 1988-10-05 | $7700.00 | Window Closed / Lapsed |