Catalyst for production of α,β-unsaturated aldehydes
Assignee: Daicel Corp
•
Filing: 1974-12-10
•
Granted: 1976-10-05
•
Expires: 1994-12-10
Abstract
Abstract A catalyst for preparing α,β-unsaturated aldehydes by the gas phase catalytic oxidation of α,β-unsaturated hydrocarbons, which catalyst contains as indispensable metal components molybdenum, bismuth and at least one transition metal selected from iron, nickel and cobalt. A chelating agent, or a chelate compound of any of the metals comprising the catalyst, is added to all or some of the starting liquid mixtures during the catalyst preparation stage, whereby to increase the catalytic activity of the catalyst so that the desired α,β-unsaturated aldehyde products such as acrolein and methacrolein can be obtained in high yields. In catalysts of this type, the catalytic activity can be maintained at a high level even if the catalyst does not contain an arsenic component.
Inventors
- 👤 Masayochi Kubo
- 👤 Kazuyuki Matsuoka
- 👤 Takushi Yokoyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:28
CPC Classifications
C; C07; C07C; C07C45/00; C07C45/27; C07C45/32; C07C45/33; C07C45/34; B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; B01J23/88; B01J23/887; B01J23/8876; B01J37/00; B01J37/0009; B01J37/0018; C07C45/35; B01J2523/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
156 words
In a catalyst composition consisting essentially of oxides of elements as active catalyst constituents, wherein said elements comprise molybdenum, bismuth, at least one transition metal selected from the group consisting of iron, nickel and cobalt, an alkali metal selected from the group consisting of potassium, rubidium and cesium, and, optionally, an element selected from the group consisting of boron, phosphorus, arsenic and tungsten, said catalyst composition being prepared by mixing aqueous solutions of water-soluble salts of said elements, and then drying the mixture to obtain the solids and calcining the solids to obtain the catalyst composition, the improvement which comprises: said catalyst composition is prepared by incorporating into at least one of said aqueous solutions a chelating substance selected from the group consisting of organic chelating agents and chelate compounds obtained by reaction between an organic chelating agent and at least one of said elements, said chelating agent being volatilized or combusted during said calcination step.
Claim 2
Dependent Claim
156 words
In a catalyst composition consisting essentially of oxides of elements as active catalyst constituents, wherein said elements comprise molybdenum, bismuth, at least one transition metal selected from the group consisting of iron, nickel and cobalt, an alkali metal selected from the group consisting of potassium, rubidium and cesium, and, optionally, an element selected from the group consisting of boron, phosphorus, arsenic and tungsten, said catalyst composition being prepared by mixing aqueous solutions of water-soluble salts of said elements, and then drying the mixture to obtain the solids and calcining the solids to obtain the catalyst composition, the improvement which comprises: said catalyst composition is prepared by incorporating into at least one of said aqueous solutions a chelating substance selected from the group consisting of organic chelating agents and chelate compounds obtained by reaction between an organic chelating agent and at least one of said elements, said chelating agent being volatilized or combusted during said calcination step.
Claim 3
Dependent Claim
22 words
A catalyst composition as claimed in claim 1, in which said catalyst composition is deposited on particles of an inert catalyst carrier.
Claim 4
Dependent Claim
124 words
In a process for preparing a catalyst composition consisting essentially of metal oxides as active catalyst constituents, wherein said metals comprise molybdenum, bismuth and at least one transition metal selected from the group consisting of iron, nickel and cobalt, which comprises mixing aqueous solutions of water-soluble salts of said metals, and then drying the mixture to obtain the solids and calcining the solids to obtain the metal oxide catalyst composition, the improvement which comprises: incorporating in at least one of said aqueous solutions a chelating substance selected from the group consisting of organic chelating agents and chelate compounds obtained by reaction between an organic chelating agent and at least one of said metals, said chelating agent being volatilized or combusted during said calcination step.
Claim 5
Dependent Claim
124 words
In a process for preparing a catalyst composition consisting essentially of metal oxides as active catalyst constituents, wherein said metals comprise molybdenum, bismuth and at least one transition metal selected from the group consisting of iron, nickel and cobalt, which comprises mixing aqueous solutions of water-soluble salts of said metals, and then drying the mixture to obtain the solids and calcining the solids to obtain the metal oxide catalyst composition, the improvement which comprises: incorporating in at least one of said aqueous solutions a chelating substance selected from the group consisting of organic chelating agents and chelate compounds obtained by reaction between an organic chelating agent and at least one of said metals, said chelating agent being volatilized or combusted during said calcination step.
Claim 6
Dependent Claim
27 words
A process as claimed in claim 3, in which an aqueous solution of ammonium molybdate is mixed with an aqueous solution of ferric nitrate and bismuth nitrate.
Claim 7
Dependent Claim
22 words
A process as claimed in claim 3, in which an inert catalyst carrier is incorporated into the mixture of said aqueous solutions.
Claim 8
Dependent Claim
52 words
In a process for the preparation of acrolein or methacrolein by catalytically oxidizing propylene or isobutylene, respectively, in the gas phase, with a molecular oxygen-containing gas, at a temperature of 250° to 400°C, the improvement which comprises: conducting the reaction in the presence of a catalyst composition as claimed in claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-05 | 1980-04-05 | 1980-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-05 | 1984-04-05 | 1984-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-05 | 1988-04-05 | 1988-10-05 | $7700.00 | Window Closed / Lapsed |