Method of forming a hydrophilic coating on an aluminum surface
Assignee: Henkel Corp
•
Filing: 1975-04-21
•
Granted: 1976-11-02
•
Expires: 1995-04-21
Abstract
Abstract A method of forming a hydrophilic coating on an aluminum surface comprises the steps of:
Inventors
- 👤 Nelson J. Newhard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:27
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/82; C23C22/83
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
126 words
A method of forming a hydrophilic coating on an aluminum surface comprising the steps of: a. etching the aluminum surface with an aqueous etching solution to provide a rough surface; b. treating the etched surface with an acidic first aqueous solution consisting essentially of active fluoride, chromate ion and phosphate ion to form a coating having a coating weight of at least 150 mg/sq.ft.; c. treating the coated surface with an alkaline second aqueous solution consisting essentially of an alkali metal silicate, the molar ratio of alkali metal oxide to silicon dioxide in said alkaline solution in the range of from about 1:4 to about 2:1, the solution containing at least about .05 percent by weight of silicon dioxide; and immediately thereafter d. baking the surface.
Claim 2
Independent Claim
126 words
A method of forming a hydrophilic coating on an aluminum surface comprising the steps of: a. etching the aluminum surface with an aqueous etching solution to provide a rough surface; b. treating the etched surface with an acidic first aqueous solution consisting essentially of active fluoride, chromate ion and phosphate ion to form a coating having a coating weight of at least 150 mg/sq.ft.; c. treating the coated surface with an alkaline second aqueous solution consisting essentially of an alkali metal silicate, the molar ratio of alkali metal oxide to silicon dioxide in said alkaline solution in the range of from about 1:4 to about 2:1, the solution containing at least about .05 percent by weight of silicon dioxide; and immediately thereafter d. baking the surface.
Claim 3
Dependent Claim
55 words
The method of claim 1 wherein the acidic first solution consists essentially of from about 0.5 to about 3 grams per liter of active fluoride, from about 2.5 to about 60 grams per liter of chromate ion (calculated as CO 3 ) and from about 2 to about 300 grams per liter of phosphate ion.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein said etching solution comprises an alkali metal hydroxide.
Claim 5
Dependent Claim
26 words
The method of claim 3 wherein the alkali metal hydroxide is sodium hydroxide present in an amount from about 2 to about 20 grams per liter.
Claim 6
Dependent Claim
33 words
The method of claim 4 wherein there is added to the etching solution an alkali metal salt selected from the group consisting of alkali metal nitrate, alkali metal sulfide, and alkali metal halide.
Claim 7
Dependent Claim
25 words
The method of claim 5 wherein the alkali metal salt is present in an amount of from about 0.01 to about 5 grams per liter.
Claim 8
Dependent Claim
27 words
The method of claim 6 wherein the alkali metal salt is sodium fluoride present in an amount of from about 0.1 to about 2 grams per liter.
Claim 9
Dependent Claim
27 words
The method of claim 1 wherein the molar ratio of alkali metal oxide to silicon dioxide in the alkaline solution is from about 1:2 to about 1:1.
Claim 10
Dependent Claim
22 words
The method of claim 8 wherein the alkaline solution contains from about 0.05 to about 2 percent by weight of silicon dioxide.
Claim 11
Dependent Claim
46 words
The method of claim 1 wherein the alkaline solution is maintained at a temperature of from about 100° F to about 200° F and wherein the aluminum surface is immersed in said alkaline solution for a period of from about 1 minute to about 5 minutes.
References Cited (Backward Citations)
DE678119C
Cited
US2438877A
Cited
US2654701A
Cited
US3391032A
Cited
US3592747A
Cited
US3493441A
Cited
US3687740A
Cited
US3846182A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |