Thermoplastic filament winding process
Assignee: Individual
•
Filing: 1973-10-03
•
Granted: 1977-03-01
•
Expires: 1993-10-03
Abstract
Abstract A precision thermoplastic filament winding process for forming into pipe or similar articles by winding strands comprised of semi-hardened thermoplastic material on a rotating mandrel to form a layer thereon. Single or multiple component, unreinforced and/or continuously reinforced filament wound cylindrical products are continuously produced by winding, at least an inner layer of thermoplastic material upon a rotating cooling mandrel which reciprocates axially in timed relation with moving guiding means and a rotary stripping means. Timing sequence provides a dwell relationship between the cooling mandrel and the hot semi-molten applied material so that at least the inner surface of the freshly applied material is rendered non-sticking and strong enough to enable it to be moved along the surface of the mandrel an incremental distance determined by the planned sequence and pattern required to give the desired specific properties.
Inventors
- 👤 Rexford H. Bradt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:49
CPC Classifications
B; B29; B29C; B29C65/00; B29C65/02; B29C65/18; B29C65/20; B29C53/00; B29C53/56; B29C53/566; B29C53/80; B29C53/8008; B29C53/8016; B29C53/84; B29C53/845; B29C66/00; B29C66/01; B29C66/05; B29C66/10; B29C66/11; B29C66/112; B29C66/1122; B29C66/40; B29C66/41; B29C66/43; B29C66/432; B29C66/4322; B29C66/4329; B29C66/49; B29C66/70; B29C66/73; B29C66/737; B29C66/7371; B29C66/73711; B29C66/80; B29C66/82; B29C66/822; B29C66/8221; B29C66/8227; B29C66/83; B29C66/834; B29C66/8341; B29C66/83411; B29C66/83413; B29C66/836; B29C53/58; B29C66/71
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
144 words
A method for continuously forming cylindrical articles, such as pipe, from a continuous strand of thermoplastic material, which comprises the steps of conveying the strand to a rotating mandrel heating at least the surface of the strand prior to the strand reaching said mandrel and to a temperature high enough to make at least the surface of the thermoplastic material of the strand sticky, wrapping the hot strand on the mandrel at a pre-selected rate using a reciprocatory motion to form a crossed helical wrap thereon, internally chilling said mandrel thereby to chill the inner surface of the formed pipe to a temperature at which the thermoplastic material adjacent the mandrel becomes rigid, and sequentially and incrementally removing the pipe from the mandrel while the pipe is being continuously formed with a rotating gripper means turning at substantially the same speed as the mandrel.
Claim 2
Independent Claim
144 words
A method for continuously forming cylindrical articles, such as pipe, from a continuous strand of thermoplastic material, which comprises the steps of conveying the strand to a rotating mandrel heating at least the surface of the strand prior to the strand reaching said mandrel and to a temperature high enough to make at least the surface of the thermoplastic material of the strand sticky, wrapping the hot strand on the mandrel at a pre-selected rate using a reciprocatory motion to form a crossed helical wrap thereon, internally chilling said mandrel thereby to chill the inner surface of the formed pipe to a temperature at which the thermoplastic material adjacent the mandrel becomes rigid, and sequentially and incrementally removing the pipe from the mandrel while the pipe is being continuously formed with a rotating gripper means turning at substantially the same speed as the mandrel.
Claim 3
Dependent Claim
55 words
A method for forming cylindrical articles as claimed in claim 1 wherein said conveying comprises the steps of guiding said strand toward said mandrel over guiding means which have a volatile release coating, and temporarily hardening the surface region only of the strand immediately prior to the movement of said strand over said guiding means.
Claim 4
Dependent Claim
77 words
A method of forming articles as claimed in claim 1 wherein said mandrel is supported so as to have one end free, and said removing step comprises the steps of axially inserting a radially expandable member rotating at substantially the same speed as the mandrel into the pipe beyond the free end of the mandrel, radially expanding said member into engagement with the inside of said pipe and moving said expandable member axially away from said mandrel.
Claim 5
Dependent Claim
51 words
A method of forming articles as set forth in claim 1 wherein said removing step comprises the steps of externally grasping the outside of the pipe with at least one external chucking device rotating at substantially the same speed as the mandrel and moving said pipe axially away from said mandrel.
Claim 6
Dependent Claim
64 words
A method for forming articles as claimed in claim 1 wherein said conveying comprises the moving of flowable plastic material from a pressure supply source through a flexible conduit to a traversable discharge device capable of shaping and/or metering one or more plastic strands where the moving surface of the rotating mandrel or material previously applied thereon forms part of the material discharge orifice.
Claim 7
Independent Claim
135 words
A method for continuously forming cylindrical articles, such as pipe, from one or more continuous strands of thermoplastic material which comprises the steps of guiding the strand to a rotating mandrel, heating the strand prior to the strand reaching said mandrel to a sufficient temperature to make the thermoplastic material of the strand sticky, wrapping the hot strand on the mandrel at a preselected rate using a reciprocatory motion to form a crossed helical wrap thereon, internally chilling said mandrel thereby to chill the inner surface of the formed pipe to a temperature at which the thermoplastic material adjacent to the mandrel becomes rigid, and sequentially and incrementally removing the pipe from the mandrel while the pipe is being continuously formed with a rotating gripper means turning at subtantially the same speed as the mandrel.
Claim 8
Independent Claim
135 words
A method for continuously forming cylindrical articles, such as pipe, from one or more continuous strands of thermoplastic material which comprises the steps of guiding the strand to a rotating mandrel, heating the strand prior to the strand reaching said mandrel to a sufficient temperature to make the thermoplastic material of the strand sticky, wrapping the hot strand on the mandrel at a preselected rate using a reciprocatory motion to form a crossed helical wrap thereon, internally chilling said mandrel thereby to chill the inner surface of the formed pipe to a temperature at which the thermoplastic material adjacent to the mandrel becomes rigid, and sequentially and incrementally removing the pipe from the mandrel while the pipe is being continuously formed with a rotating gripper means turning at subtantially the same speed as the mandrel.
Claim 9
Independent Claim
123 words
A method for continuously winding a substantially cylindrical article from one or more fiberglass strands saturated with hot sticky thermoplastic material, guiding with devices having means to partially cool the surface of each strand to temporarily case harden the surface of each strand sufficiently to obtain handling capabilities, reciprocating said guiding devices in close proximity to a cooling mandrel to form a cross helical wrap thereon, rotating and reciprocating the cooling mandrel, controlling the rotating and reciprocating speeds of the cooling mandrel in coordination with the reciprocatory speed of the guide devices, and sequentially and incrementally removing the pipe from the mandrel while the article is being continuously formed with a rotating gripper means turning at substantially the same speed as the mandrel.
Claim 10
Independent Claim
123 words
A method for continuously winding a substantially cylindrical article from one or more fiberglass strands saturated with hot sticky thermoplastic material, guiding with devices having means to partially cool the surface of each strand to temporarily case harden the surface of each strand sufficiently to obtain handling capabilities, reciprocating said guiding devices in close proximity to a cooling mandrel to form a cross helical wrap thereon, rotating and reciprocating the cooling mandrel, controlling the rotating and reciprocating speeds of the cooling mandrel in coordination with the reciprocatory speed of the guide devices, and sequentially and incrementally removing the pipe from the mandrel while the article is being continuously formed with a rotating gripper means turning at substantially the same speed as the mandrel.
Claim 11
Independent Claim
124 words
A method for continuously forming a cylindrical article from a thermoplastic article, which comprises the steps of guiding one or more stretch oriented strands of material to a cooling rotating mandrel, reciprocating the guiding of the stretch oriented strands in close proximity to the cooling mandrel to form a cross helical wrap thereon, heating the strand in close proximity to and at its line of intersection with the cooling mandrel to at least the temperature at which the surface of the material becomes semi-molten and winding the strands to form a cylindrical article, and sequentially and incrementally removing the article from the mandrel while the article is being continuously formed with a rotating gripper means turning at substantially the same speed as the mandrel.
Claim 12
Independent Claim
124 words
A method for continuously forming a cylindrical article from a thermoplastic article, which comprises the steps of guiding one or more stretch oriented strands of material to a cooling rotating mandrel, reciprocating the guiding of the stretch oriented strands in close proximity to the cooling mandrel to form a cross helical wrap thereon, heating the strand in close proximity to and at its line of intersection with the cooling mandrel to at least the temperature at which the surface of the material becomes semi-molten and winding the strands to form a cylindrical article, and sequentially and incrementally removing the article from the mandrel while the article is being continuously formed with a rotating gripper means turning at substantially the same speed as the mandrel.
References Cited (Backward Citations)
US3125483A
Cited
US3126306A
Cited
US1719738A
Cited
US2656873A
Cited
US3616063A
Cited
US3301734A
Cited
US3332815A
Cited
US3400029A
Cited
US3492187A
Cited
US3421306A
Cited
US3507412A
Cited
US3563826A
Cited
US3698986A
Cited
US3578532A
Cited
US3932254A
Cited
US3700519A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-29 | 1980-08-30 | 1981-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-29 | 1984-08-30 | 1985-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-29 | 1988-08-30 | 1989-03-01 | $7700.00 | Window Closed / Lapsed |