US4014815A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Removal of carbon and vanadium or lead from spent catalysts by means of controlled high temperature treatment with sulfur
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1975-06-19
•
Granted: 1977-03-29
•
Expires: 1995-06-19
Abstract
Abstract The regeneration of spent metal catalysts is accomplished by treatment with a sulfurous atmosphere at a pressure of at least 0.10 atmospheres and at a controlled high temperature of between 400-825 DEG C. (preferably between 400 DEG -715 DEG C., and most preferably between 400 DEG -600 DEG C.) for a time sufficient for the selective formation of sulfides of carbon and sulfides of vanadium or lead which sulfides are characterized by having high volatility and solubility in the sulfurous atmosphere and which vanadium and carbon sulfides are selectively removed from the catalyst within the stated temperature range.
Inventors
- 👤 Fred R. Gamble, Jr.
- 👤 Ricardo B. Levy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:25
CPC Classifications
C; C10; C10G; C10G45/00; C10G45/02; C10G45/04; C10G45/06; C10G45/08; B; B01; B01J; B01J23/00; B01J23/90; B01J23/92; B01J23/94; B01J23/96; Y; Y10; Y10S; Y10S502/00; Y10S502/515; Y10S502/516; Y10S502/518
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
106 words
A process for selectively removing vanadium and carbon contamination from supported metal catalyst systems, which supported metal catalyst systems are selected from the group consisting of Group VI metals, Group VIII metals and bi and tri combinations thereof on a refractory oxide support, which process comprises the steps of: a. contacting the contaminated supported metal catalyst system with an elemental sulfur vapor atmosphere at a temperature between 400° to 825° C, and a sulfur pressure of at least 0.10 atmospheres for a time sufficient to selectively form volatile vanadium and carbon sulfides; b. removing the volatile vanadium and carbon sulfides from the supported metal catalyst system.
Claim 2
Dependent Claim
106 words
A process for selectively removing vanadium and carbon contamination from supported metal catalyst systems, which supported metal catalyst systems are selected from the group consisting of Group VI metals, Group VIII metals and bi and tri combinations thereof on a refractory oxide support, which process comprises the steps of: a. contacting the contaminated supported metal catalyst system with an elemental sulfur vapor atmosphere at a temperature between 400° to 825° C, and a sulfur pressure of at least 0.10 atmospheres for a time sufficient to selectively form volatile vanadium and carbon sulfides; b. removing the volatile vanadium and carbon sulfides from the supported metal catalyst system.
Claim 3
Dependent Claim
17 words
A process according to claim 1 wherein vanadium sulfides are selectively removed from contaminated supported metal catalysts.
Claim 4
Dependent Claim
17 words
A process according to claim 1 wherein CS 2 is selectively removed from contaminated supported metal catalysts.
Claim 5
Dependent Claim
68 words
A process according to claim 1 wherein the contacting of the contaminated metal catalyst system with a gaseous sulfurous atmosphere comprises: a. establishing a temperature gradient in the system having a temperature difference across the gradient of at least 50° C.; b. moving the volatile vanadium and carbon sulfide across the temperature gradient; c. condensing the vanadium and carbon sulfide at the low temperature end of the gradient.
Claim 6
Dependent Claim
17 words
A process according to claim 4 wherein vanadium sulfides are selectively removed from contaminated supported metal catalysts.
Claim 7
Dependent Claim
17 words
A process according to claim 4 wherein CS 2 is selectively removed from contaminated supported metal catalysts.
Claim 8
Dependent Claim
51 words
A process according to claim 1 wherein the contacting of the contaminated metal catalyst system with a gaseous sulfurous atmosphere comprises: a. establishing a uniform temperature in the system; b. passing a moving sulfurous atmosphere across the catalyst; c. moving the volatile vanadium and carbon sulfides in the moving sulfurous atmosphere.
Claim 9
Dependent Claim
17 words
A process according to claim 7 wherein vanadium sulfides are selectively removed from contaminated supported metal catalysts.
Claim 10
Dependent Claim
17 words
A process according to claim 7 wherein CS 2 is selectively removed from contaminated supported metal catalysts.
Claim 11
Dependent Claim
59 words
A process according to claim 1 wherein the contacting of the contaminated metal catalyst system with a gaseous sulfurous atmosphere comprises: establishing a static sulfurous atmosphere over the metal catalyst whereby crystallites of vanadium and carbon sulfide form on the surface of the metal catalyst in the gaseous sulfurous atmosphere thus selectively removing the contaminants from the catalyst pores.
Claim 12
Dependent Claim
17 words
A process according to claim 10 wherein vanadium sulfides are selectively removed from contaminated supported metal catalysts.
Claim 13
Dependent Claim
17 words
A process according to claim 10 wherein CS 2 is selectively removed from contaminated supported metal catalysts.
Claim 14
Dependent Claim
13 words
A process according to claim 1 wherein the temperature ranges between 400°-715° C.
Claim 15
Dependent Claim
13 words
A process according to claim 1 wherein the temperature ranges between 400°-600° C.
Claim 16
Dependent Claim
11 words
A process according to claim 1 wherein the support is alumina.
Claim 17
Dependent Claim
15 words
A process according to claim 1 wherein the supported metal catalyst systems are cobalt-molybdenum catalysts.
Claim 18
Dependent Claim
102 words
A process for selectively removing vanadium and carbon contamination from supported metal catalysts, which supported metal catalysts are selected from the group consisting of Group VI metals, Group VIII metals and bi and tri combinations thereof on a refractory oxide support, which comprises the steps of: a. contacting the contaminated supported catalyst system with liquid sulfur at a temperature of between 300°-825° C; b. forming soluble carbon and vanadium sulfides on the supported metal catalyst, c. dissolving the soluble carbon and vanadium sulfides in the liquid sulfur; d. removing the dissolved soluble carbon and vanadium sulfides from the supported metal catalyst system.
Claim 19
Dependent Claim
102 words
A process for selectively removing vanadium and carbon contamination from supported metal catalysts, which supported metal catalysts are selected from the group consisting of Group VI metals, Group VIII metals and bi and tri combinations thereof on a refractory oxide support, which comprises the steps of: a. contacting the contaminated supported catalyst system with liquid sulfur at a temperature of between 300°-825° C; b. forming soluble carbon and vanadium sulfides on the supported metal catalyst, c. dissolving the soluble carbon and vanadium sulfides in the liquid sulfur; d. removing the dissolved soluble carbon and vanadium sulfides from the supported metal catalyst system.
Claim 20
Dependent Claim
17 words
A process according to claim 16 wherein vanadium sulfides are selectively removed from contaminated supported metal catalysts.
Claim 21
Dependent Claim
17 words
A process according to claim 16 wherein CS 2 is selectively removed from contaminated supported metal catalysts.
Claim 22
Dependent Claim
11 words
A process according to claim 16 wherein the support is alumina.
Claim 23
Dependent Claim
15 words
A process according to claim 2 wherein the supported metal catalyst systems are cobalt-molybdenum catalysts.
Claim 24
Dependent Claim
67 words
A process for selectively removing lead from supported platinum catalysts which process comprises the steps of: a. contacting the contaminated platinum catalyst system with an elemental sulfur vapor atmosphere at a temperature between 400° to 600° C and a sulfur pressure of at least 0.10 atm for a time sufficient to selectively form volatile lead sulfides; b. removing the volatile lead sulfides from the platinum catalyst system.
Claim 25
Dependent Claim
67 words
A process for selectively removing lead from supported platinum catalysts which process comprises the steps of: a. contacting the contaminated platinum catalyst system with an elemental sulfur vapor atmosphere at a temperature between 400° to 600° C and a sulfur pressure of at least 0.10 atm for a time sufficient to selectively form volatile lead sulfides; b. removing the volatile lead sulfides from the platinum catalyst system.
Claim 26
Dependent Claim
66 words
A process according to claim 22 wherein the contacting of the lead contaminated platinum catalyst with a gaseous sulfurous atmosphere comprises: a. establishing a temperature gradient having a difference across the gradient of at least 50° C., b. moving the volatile lead sulfides across the temperature gradient from high temperature to low temperature, c. collecting the lead sulfides at the low temperature end of the gradient.
Claim 27
Dependent Claim
50 words
A process according to claim 22 wherein the contacting of the lead contaminated platinum catalyst with a gaseous sulfurous atmosphere comprises: a. establishing a uniform temperature in the system; b. passing a moving sulfurous atmosphere across the platinum catalyst; c. moving the volatile lead sulfides in the moving sulfurous atmosphere.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-28 | 1980-09-27 | 1981-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-28 | 1984-09-27 | 1985-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-28 | 1988-09-27 | 1989-03-29 | $7700.00 | Window Closed / Lapsed |