Assignee: Centre de Recherches Metallurgiques CRM ASBL
•
Filing: 1976-01-29
•
Granted: 1977-04-05
•
Expires: 1996-01-29
Abstract
Abstract In the rolling mill the temperature of the product is reduced to between Ac3 and Ac3 + 150 DEG C before it enters the finishing stands. The product emerging from the finishing stands is quenched to provide a surface layer of martensite and/or bainite. Subsequently the heat of the core of the product is allowed to raise the temperature of the surface layer to between 450 DEG and 750 DEG C, so that the quenched layer is tempered.
Inventors
- 👤 Mario Economopoulos
- 👤 Yves Jean Respen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:31
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/02; C21D8/04; C21D8/0447; C21D8/0463; C21D1/00; C21D1/62; C21D1/02; C21D1/18; C21D8/0421; C21D8/0426; C21D8/06; C21D9/00; C21D9/52; C21D9/525; C21D2211/00; C21D2211/002; C21D2211/008; C21D2221/00; C21D2221/10
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
97 words
A method of producing a rolled steel product in a rolling mill including finishing stands, the method comprising the steps of reducing the temperature of the product, before it enters the finishing stands, to a value between Ac 3 and Ac 3 + 150° C; quenching the product emerging from the finishing stands, thereby forming a quenched surface comprising martensite and/or bainite, the product still having an unquenched core; and allowing heat from the core to raise the temperature of the quenched surface to a value between 450° and 750° C, whereby the quenched surface is tempered.
Claim 2
Independent Claim
97 words
A method of producing a rolled steel product in a rolling mill including finishing stands, the method comprising the steps of reducing the temperature of the product, before it enters the finishing stands, to a value between Ac 3 and Ac 3 + 150° C; quenching the product emerging from the finishing stands, thereby forming a quenched surface comprising martensite and/or bainite, the product still having an unquenched core; and allowing heat from the core to raise the temperature of the quenched surface to a value between 450° and 750° C, whereby the quenched surface is tempered.
Claim 3
Dependent Claim
23 words
A method as claimed in claim 1, in which the product enters the finishing stands at a temperature just above Ac 3 .
Claim 4
Dependent Claim
29 words
A method as claimed in claim 1, in which the heat from the core raises the temperature of the quenched surface to a value between 550° and 700° C.
Claim 5
Dependent Claim
34 words
A method as claimed in claim 1, in which the step of reducing the temperature of the product before it enters the finishing stands comprises a cooling step followed by a temperature homogenisation step.
Claim 6
Independent Claim
32 words
A method as claimed in any of claims 1 to 4, in which the cross-sectional area of the quenched surface occupies 10 to 50% of the total cross-sectional area of the product.
Claim 7
Dependent Claim
28 words
A method as claimed in claim 5, in which the cross-sectional area of the quenched surface occupies 15 to 35% of the total cross-sectional area of the product.
Claim 8
Dependent Claim
28 words
A method as claimed in claim 1, in which the step of reducing the temperature of the product before it enters the finishing stands comprises cooling with water.
Claim 9
Dependent Claim
17 words
A method as claimed in claim 1, in which the step of quenching comprises cooling with water.
Claim 10
Dependent Claim
30 words
A method as claimed in claim 1, in which the step of reducing the temperature of the product before it enters the finishing stands is carried out in several stages.
Claim 11
Dependent Claim
18 words
A method as claimed in claim 1, in which the quenching step is carried out in several stages.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-04 | 1980-10-04 | 1981-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-04 | 1984-10-04 | 1985-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-04 | 1988-10-04 | 1989-04-05 | $7700.00 | Window Closed / Lapsed |