Method for preparing filter-coated phosphor particles
Assignee: RCA Licensing Corp
•
Filing: 1976-01-23
•
Granted: 1977-05-03
•
Expires: 1996-01-23
Abstract
Abstract Method comprises dispersing phosphor particles in a liquid medium and then precipitating filter material on the phosphor particles. The filter-covered phosphor particles are removed from the medium, dried and then heated until the filter material sinters to the surfaces of the phosphor particles as discrete filter particles.
Inventors
- 👤 Martin Robert Royce
- 👤 Robert Paul Thompson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:11
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/02; C09K11/025; H; H01; H01J; H01J9/00; H01J9/20; H01J9/22; H01J9/227; H01J9/2278; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
110 words
A method for coating phosphor particles with discrete filter particles comprising (a) suspending said phosphor particles in a liquid medium, (b) precipitating on said phosphor particles only sufficient filter material to cover surfaces of said phosphor particles, said filter material being a chalcogenide selected from the group consisting of sulfides, selenides and/or tellurides of at least one bivalent cation selected from the group consisting of cadmium, zinc, calcium magnesium, strontium and/or barium, (c) removing said covered phosphor particles from said liquid medium (d) and then heating said covered phosphor particles in a nonoxidizing ambient until said filter material sinters to the surfaces of said phosphor particles as discrete filter particles.
Claim 2
Independent Claim
110 words
A method for coating phosphor particles with discrete filter particles comprising (a) suspending said phosphor particles in a liquid medium, (b) precipitating on said phosphor particles only sufficient filter material to cover surfaces of said phosphor particles, said filter material being a chalcogenide selected from the group consisting of sulfides, selenides and/or tellurides of at least one bivalent cation selected from the group consisting of cadmium, zinc, calcium magnesium, strontium and/or barium, (c) removing said covered phosphor particles from said liquid medium (d) and then heating said covered phosphor particles in a nonoxidizing ambient until said filter material sinters to the surfaces of said phosphor particles as discrete filter particles.
Claim 3
Dependent Claim
14 words
The method defined in claim 1 wherein said filter material is a cadmium sulfo-selenide.
Claim 4
Dependent Claim
20 words
The method defined in claim 2 wherein said precipitated filter material only partially covers the surfaces of said phosphor particles.
Claim 5
Dependent Claim
24 words
The method defined in claim 2 wherein the weight ratio of filter particles to phosphor particles is in the range of 0.001 to 0.05.
Claim 6
Dependent Claim
25 words
The method defined in claim 1 wherein said filter material is a chalcogenide of at least one of zinc, cadmium, calcium, strontium, magnesium and barium.
Claim 7
Independent Claim
113 words
A method for coating phosphor particles with discrete filter particles comprising (a) dispersing phosphor particles in an aqueous medium, (b) mixing into said medium cadmium ions in water-soluble form, (c) then mixing into said medium sulfide and selenide ions in water-soluble form in quantities at least sufficient to react with substantially all of cadmium ions present in said medium, whereby cadmium sulfo-selenide precipitates on the surfaces of said phosphor particles, (d) then removing from said medium and drying phosphor particles carrying said precipitated material, (e) and heating said dry phosphor particles in a nonoxidizing atmosphere until said precipitated material forms discrete, crystalline particles which are sintered to the surfaces of said phosphor particles.
Claim 8
Independent Claim
113 words
A method for coating phosphor particles with discrete filter particles comprising (a) dispersing phosphor particles in an aqueous medium, (b) mixing into said medium cadmium ions in water-soluble form, (c) then mixing into said medium sulfide and selenide ions in water-soluble form in quantities at least sufficient to react with substantially all of cadmium ions present in said medium, whereby cadmium sulfo-selenide precipitates on the surfaces of said phosphor particles, (d) then removing from said medium and drying phosphor particles carrying said precipitated material, (e) and heating said dry phosphor particles in a nonoxidizing atmosphere until said precipitated material forms discrete, crystalline particles which are sintered to the surfaces of said phosphor particles.
Claim 9
Dependent Claim
29 words
The method defined in claim 6 wherein in step (c) the mole ratio of sulfide ions to sulfide plus selenide ions is in the range of 0.3 to 0.7.
Claim 10
Dependent Claim
22 words
The method defined in claim 6 wherein in step (c) said sulfide ions and selenide ions are present in substantially equimolar proportions.
Claim 11
Dependent Claim
27 words
The method defined in claim 6 wherein in step (e), said phosphor particles are heated at about 600° to 900° C. for about 30 to 120 minutes.
Claim 12
Dependent Claim
28 words
The method defined in claim 6 wherein in step (e) said phosphor particles are heated in a mildly reducing ambient at about 800° C. for about 90 minutes.
References Cited (Backward Citations)
US2684306A
Cited
US2774682A
Cited
US2971859A
Cited
US3264133A
Cited
GB1168074A
Cited
US3875449A
Cited
US3690929A
Cited
US3927240A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-02 | 1980-11-01 | 1981-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-02 | 1984-11-01 | 1985-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-02 | 1988-11-01 | 1989-05-03 | $7700.00 | Window Closed / Lapsed |