Steel substrate electroplated with Al powder dispersed in Zn
Assignee: JFE Steel Corp
•
Filing: 1976-05-27
•
Granted: 1977-07-19
•
Expires: 1996-05-27
Abstract
Abstract A composite zinc-aluminum dispersion plated steel sheet and a method of producing same are disclosed. The plated steel sheet comprises an electrolytical zinc plated layer containing 1.5 to 70% by weight of aluminum dispersed therein. The method comprises adding aluminum powder to an electrolytical zinc plating bath composition, dispersing the aluminum powder into the plating bath to provide a composite zinc-aluminum dispersion plating bath, and electrolytical treating a steel sheet in the composite zinc-aluminum dispersion plating bath while agitating it. The plated steel sheet enhances corrosion resistances and does not show any spangles which impair the appearances after subsequent painting of the plated steel sheet.
Inventors
- 👤 Hajime Kimura
- 👤 Takahisa Yoshihara
- 👤 Shunichi Harada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 01:24
CPC Classifications
C; C25; C25D; C25D15/00; C25D15/02; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12069; Y10T428/12076; Y10T428/12097; Y10T428/12493; Y10T428/12736; Y10T428/1275; Y10T428/12757
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
85 words
A composite comprising a steel sheet substrate having electrolytically plated thereon a layer consisting essentially of 1.5-70% by weight of aluminum dispersed in zinc, said layer having been plated electrolytically from an electrolytical zinc plating bath containing dispersed aluminum powder of a particle size of at least 100 meshes (at most 147 μm diameter) while agitating said bath, said composite being characterized by the substantial absence of a detrimental alloy layer of iron and of zinc-aluminum at the interface of said substrate and said layer.
Claim 2
Dependent Claim
85 words
A composite comprising a steel sheet substrate having electrolytically plated thereon a layer consisting essentially of 1.5-70% by weight of aluminum dispersed in zinc, said layer having been plated electrolytically from an electrolytical zinc plating bath containing dispersed aluminum powder of a particle size of at least 100 meshes (at most 147 μm diameter) while agitating said bath, said composite being characterized by the substantial absence of a detrimental alloy layer of iron and of zinc-aluminum at the interface of said substrate and said layer.
Claim 3
Dependent Claim
26 words
The composite of claim 1, wherein said aluminum powder in said bath has a particle size of at least 325 meshes (at most 44 μm diameter).
Claim 4
Dependent Claim
20 words
The composite of claim 1, wherein the amount of said aluminum powder in said bath is 5 to 300 g/l.
Claim 5
Dependent Claim
20 words
The composite of claim 1, wherein the amount of said aluminum powder in said bath is 20 to 100 g/l.
Claim 6
Dependent Claim
13 words
The composite of claim 1, having been subjected to a subsequent rolling step.
Claim 7
Dependent Claim
14 words
The composite of claim 5 having been subjected to a subsequent heat treating step.
Claim 8
Dependent Claim
21 words
The composite of claim 5, wherein said rolling step is effected with a reduction rate of thickness of at most 5%.
Claim 9
Dependent Claim
26 words
The composite of claim 6, wherein said heating step is effected at a temperature for a time defined by the shaded area shown in FIG 4.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-18 | 1981-01-17 | 1981-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-18 | 1985-01-17 | 1985-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-18 | 1989-01-17 | 1989-07-19 | $7700.00 | Window Closed / Lapsed |