Ductile cast iron articles
Assignee: Individual
•
Filing: 1976-05-03
•
Granted: 1977-08-09
•
Expires: 1996-05-03
Abstract
Abstract Articles of manufacture in the form of an annular ductile iron piece at least a portion of which has its carbon content in the form of flattened bodies disposed in planes parallel to the central axis of the piece and normal to the outer surface of the piece, the iron grains of the piece being extended significantly both in a direction parallel to the central axis and in directions which are transverse to the central axis and parallel to planes occupied by the flattened carbon bodies, the outer surface of the piece being smooth and uninterrupted without machining and the article being free from structural failure discontinuities.
Inventors
- 👤 Charles H. Noble
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 13:26
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/10; B; B21; B21C; B21C1/00; B21C1/16; B21C1/22; B21C1/24; B21C1/26; B21C23/00; B21C23/02; B21C23/04; B21C23/08; B21C23/085; B21C5/00; B21C5/003; B21D; B21D41/00; B21D41/04; B21K; B21K21/00; B21K21/12; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12292
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
182 words
An article of manufacture comprising an annular ductile iron piece containing 1-4.25% carbon, 1-4.25% silicon, 0-0.20% phosphorous, and at least one nodularizing agent, at least an axial portion of said ductile iron piece being characterized by having the carbon content thereof in the form of significantly flattened bodies which are predominantly disposed in planes parallel to the central axis of the piece and normal to the outer surface of the piece along the line of intersection between the plane and the outer surface, and by having the iron grains thereof significantly extended both in a direction parallel to the central axis of the piece and in directions which are transverse to said axis and parallel to said planes; said piece having a smooth uninterrupted outer surface and being free from structural failure discontinuities, at least said axial portion having been cold extruded through a tapered female die by applying axial pressure to the piece until the compressive yield point of the ductile iron is reached and the metal is caused to traverse the die in plastic flow while maintained under hoop compression.
Claim 2
Dependent Claim
182 words
An article of manufacture comprising an annular ductile iron piece containing 1-4.25% carbon, 1-4.25% silicon, 0-0.20% phosphorous, and at least one nodularizing agent, at least an axial portion of said ductile iron piece being characterized by having the carbon content thereof in the form of significantly flattened bodies which are predominantly disposed in planes parallel to the central axis of the piece and normal to the outer surface of the piece along the line of intersection between the plane and the outer surface, and by having the iron grains thereof significantly extended both in a direction parallel to the central axis of the piece and in directions which are transverse to said axis and parallel to said planes; said piece having a smooth uninterrupted outer surface and being free from structural failure discontinuities, at least said axial portion having been cold extruded through a tapered female die by applying axial pressure to the piece until the compressive yield point of the ductile iron is reached and the metal is caused to traverse the die in plastic flow while maintained under hoop compression.
Claim 3
Dependent Claim
54 words
An article according to claim 1, wherein the ratio of the average dimension of said flattened bodies in a direction from the inner surface toward the outer surface of the article to the average thickness of the bodies at right angles to the plane in which the body is disposed is at least 1.1.
Claim 4
Dependent Claim
41 words
An article according to claim 2, wherein said ratio is not more than 15, and said article exhibits, after being stress relieved, a longitudinal tensile strength of at least 60,000 p.s.i. and a significantly lower tensile strength circumferentially of the piece.
Claim 5
Dependent Claim
16 words
An article according to claim 1, wherein the transverse cross-section of said axial portion is curvilinear.
Claim 6
Dependent Claim
16 words
An article according to claim 1, wherein the transverse cross-section of said axial portion is polygonal.
Claim 7
Dependent Claim
38 words
An article according to claim 1, wherein said axial portion is one end portion of the piece and is of polygonal transverse cross section; and the other end portion of the piece is of curvilinear transverse cross section.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |