Process for the determination of the boron contents of pure halogensilanes

Assignee: Siltronic AG
•
Filing: 1976-11-01
•
Granted: 1977-08-16
•
Expires: 1996-11-01
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract Process for the determination of the boron content of pure halogensilanes pecially silicon tetrachloride and trichlorosilane, which contain up to 0.1% of atoms of acceptors and donors, which comprises the steps of converting the halogen silanes into the gaseous state in a testing apparatus by contacting said halogensilanes with an evaporator surface heated to a temperature ranging from 80° C to 350° C, passing the generated gases to a support heated to the decomposition temperature of the gases whereby the released silicon is deposited on the support, removing the support and the deposit thereon from the testing apparatus and determining the boron content by calculation from the measured value of the specific resistance of the support plus the deposited silicon. It should be understood that all parts of the testing apparatus which come into contact with the generated gas, with the exception of the support heated to the required deposition temperature, should be at the temperature above 80° C, but below the decomposition temperature of the halogensilane.

Inventors

  • 👤 Dietrich Schmidt
  • 👤 Johann Hofer
  • 👤 Winfried Lang
  • 👤 Erich Bildl

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-01 23:28
CPC Classifications
G; G01; G01N; G01N31/00; G01N27/00; G01N27/02; G01N27/04; G01N27/041

Claims Analysis

Total Claims: 9
Claim 1
Independent Claim 159 words
A process for the determination of the boron content of pure halogen-silanes which contain up to 0.1% of atoms of acceptors and donors, which comprises the steps of converting the halogen silanes into the gaseous state in a testing apparatus by contacting said halogensilanes with an evaporator surface heated to a temperature ranging from 80°C to 350°C, passing the generated gases to a silicon support heated to the decomposition temperature of the gases whereby the released silicon is deposited on the support, removing the support and the deposit thereon from the testing apparatus and determining the boron content by calculation from the measured value of the specific resistance of the support plus the deposited silicon, with the proviso that all parts of the testing apparatus which come into contact with the gas should be at a temperature above 80°C, but below the decomposition temperature of the halogensilane, with the exception of the support heated to the required deposition temperature.
Claim 2
Dependent Claim 159 words
A process for the determination of the boron content of pure halogen-silanes which contain up to 0.1% of atoms of acceptors and donors, which comprises the steps of converting the halogen silanes into the gaseous state in a testing apparatus by contacting said halogensilanes with an evaporator surface heated to a temperature ranging from 80°C to 350°C, passing the generated gases to a silicon support heated to the decomposition temperature of the gases whereby the released silicon is deposited on the support, removing the support and the deposit thereon from the testing apparatus and determining the boron content by calculation from the measured value of the specific resistance of the support plus the deposited silicon, with the proviso that all parts of the testing apparatus which come into contact with the gas should be at a temperature above 80°C, but below the decomposition temperature of the halogensilane, with the exception of the support heated to the required deposition temperature.
Claim 3
Dependent Claim 13 words
The process claimed in claim 1, wherein the halogensilanes are silicontetrachloride or trichlorosilane.
Claim 4
Dependent Claim 29 words
The process claimed in claim 1, wherein the deposited silicon and its support are freed from impurities with the exception of boron by at least one step of zone-refining.
Claim 5
Dependent Claim 21 words
The process as claimed in claim 1, wherein the evaporator surface is heated to a temperature between 220° and 280° C.
Claim 6
Dependent Claim 27 words
The process according to claim 1, wherein the support consists of a substantially monocrystalline thin silicon rod having a specific resistance of 5,000 ohm . cm, P.
Claim 7
Dependent Claim 13 words
The process as claimed in claim 1, wherein the support is heated inductively.
Claim 8
Dependent Claim 17 words
The process as claimed in claim 1, wherein the support and the deposited silicon are not separated.
Claim 9
Dependent Claim 33 words
The process as claimed in claim 3, wherein the silicon body is freed from impurities with the exception of boron by 5 to 10 zone drawing operations before the specific resistance is determined.

References Cited (Backward Citations)

US3403003A Cited
US3540861A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1980-08-15 1981-02-14 1981-08-16 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1984-08-15 1985-02-14 1985-08-16 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1988-08-15 1989-02-14 1989-08-16 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag