Surface impregnated catalyst
Assignee: EIDP Inc
•
Filing: 1976-04-12
•
Granted: 1977-09-13
•
Expires: 1996-04-12
Abstract
Abstract A surface impregnated catalyst consisting essentially of a catalyst support, a palladium-gold alloy distributed in a surface layer of the catalyst support extending less than about 0.5 millimeter from the surface, and alkali metal acetate are provided. The catalyst has substantially higher specific activity than prior art catalysts used for the production of vinyl acetate.
Inventors
- 👤 Thomas Charles Bissot
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 02:07
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/48; B01J23/52; B01J23/54; B01J23/56; B01J23/58; B01J35/00; B01J35/60; B01J37/00; B01J37/02; B01J37/0215; B01J37/0221; B01J21/00; B01J21/06; B01J21/08; B01J35/30; B01J35/396; B01J35/397; B01J35/61; B01J35/613; B01J35/615; B01J35/63; B01J35/635
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
345 words
In the process of preparing a catalyst comprising palladium and gold deposited on a catalyst support having a particle diameter of from about 3 to about 7 mm, and a pore volume of from about 0.2 to about 1.5 ml/g, a 10% by weight water suspension of said support having a pH of from about 3.0 to about 9.0, by 1. impregnating the catalyst support with aqueous solution of water-soluble palladium and gold compounds, 2. precipitating water-insoluble palladium and gold compounds on the catalyst support by contacting the impregnated catalyst support with a solution of compounds capable of reacting with the water-soluble palladium and gold compounds to form water-insoluble palladium and gold compounds, 3. converting the water-insoluble palladium and gold compounds into palladium and gold metal by treatment with a reducing agent, 4. washing the catalyst with water, 5. contacting the catalyst with alkali metal acetate, and 6. drying the catalyst, the improvement where the palladium and gold is distributed as an alloy in a surface layer of the catalyst support, said surface layer extending less than about 0.5 mm from the surface of said support, the palladium in said alloy being present in an amount of from about 1.5 to about 5.0 grams per liter of catalyst, the gold being present in an amount of from about 0.5 to about 2.25 grams per liter of catalyst, and the alkali metal acetate being present in an amount of from about 5 to about 60 grams per liter of catalyst, said impregnating step being carried out with an aqueous solution of palladium and gold compounds, the total volume of which is from about 95% to about 100% of the absorptive capacity of the catalyst support and said precipitating step being carried out by soaking the wet catalyst support with a solution of an alkali metal silicate, the amount of alkali silicate being such that after the alkali metal silicate solution has been in contact with the catalyst support for about 12 to 24 hours the pH of said solution is from about 6.5 to about 9.5.
Claim 2
Dependent Claim
345 words
In the process of preparing a catalyst comprising palladium and gold deposited on a catalyst support having a particle diameter of from about 3 to about 7 mm, and a pore volume of from about 0.2 to about 1.5 ml/g, a 10% by weight water suspension of said support having a pH of from about 3.0 to about 9.0, by 1. impregnating the catalyst support with aqueous solution of water-soluble palladium and gold compounds, 2. precipitating water-insoluble palladium and gold compounds on the catalyst support by contacting the impregnated catalyst support with a solution of compounds capable of reacting with the water-soluble palladium and gold compounds to form water-insoluble palladium and gold compounds, 3. converting the water-insoluble palladium and gold compounds into palladium and gold metal by treatment with a reducing agent, 4. washing the catalyst with water, 5. contacting the catalyst with alkali metal acetate, and 6. drying the catalyst, the improvement where the palladium and gold is distributed as an alloy in a surface layer of the catalyst support, said surface layer extending less than about 0.5 mm from the surface of said support, the palladium in said alloy being present in an amount of from about 1.5 to about 5.0 grams per liter of catalyst, the gold being present in an amount of from about 0.5 to about 2.25 grams per liter of catalyst, and the alkali metal acetate being present in an amount of from about 5 to about 60 grams per liter of catalyst, said impregnating step being carried out with an aqueous solution of palladium and gold compounds, the total volume of which is from about 95% to about 100% of the absorptive capacity of the catalyst support and said precipitating step being carried out by soaking the wet catalyst support with a solution of an alkali metal silicate, the amount of alkali silicate being such that after the alkali metal silicate solution has been in contact with the catalyst support for about 12 to 24 hours the pH of said solution is from about 6.5 to about 9.5.
Claim 3
Dependent Claim
25 words
The process of claim 1 wherein the catalyst support has an internal surface area of from about 10 to about 800 square meters per gram.
Claim 4
Dependent Claim
37 words
The process of claim 2 wherein the catalyst support is silica containing at least about 90% by weight SiO 2 and having an internal surface area of from about 40 to about 400 square meters per gram.
Claim 5
Dependent Claim
21 words
The process of claim 3 wherein the catalyst support has a pore volume of from about 0.5 to about 1.1 ml/g.
Claim 6
Dependent Claim
13 words
The process of claim 4 wherein the alkali metal silicate is sodium silicate.
Claim 7
Dependent Claim
24 words
The process of claim 5 wherein the sodium silicate is selected from the group consisting of sodium orthosilicate, sodium metasilicate, sodium disilicate and waterglass.
Claim 8
Dependent Claim
23 words
The process of claim 6 wherein the wet catalyst support is soaked with the sodium silicate solution for at least about 12 hours.
Claim 9
Dependent Claim
13 words
The process of claim 7 wherein the sodium silicate is crystalline hydrated metasilicate.
Claim 10
Dependent Claim
29 words
The process of claim 8 wherein the total volume of palladium and gold solution is from about 98% to about 99% of the absorptive capacity of the catalyst support.
Claim 11
Dependent Claim
45 words
The process of claim 5 wherein the amount of sodium silicate is such that after the sodium silicate solution has been in contact with the catalyst support for about 12 to 24 hours the pH of said solution is from about 7.5 to about 8.5.
Claim 12
Dependent Claim
92 words
The process of claim 3 wherein the palladium compound is present in an amount sufficient to provide about 1.5 to about 5.0 grams of palladium per liter of finished catalyst and is selected from the group consisting of palladium (II) chloride, sodium palladium (II) chloride, palladium (II) nitrate and palladium (II) sulfate and the gold compound is present in an amount sufficient to provide about 0.5 to about 2.25 grams of gold per liter of finished catalyst and is selected from the group consisting of auric (III) chloride and tetrachloroauric (III) acid.
Claim 13
Dependent Claim
66 words
The process of claim 9 wherein the palladium compound is sodium palladium (II) chloride that is present in an amount sufficient to provide about 1.65 to about 3.3 g. of palladium per liter of finished catalyst and the gold compound is tetrachloroauric (III) acid that is present in an amount sufficient to provide about 0.75 to about 1.5 g. of gold per liter of finished catalyst.
Claim 14
Dependent Claim
35 words
The process of claim 12 wherein the palladium and gold are deposited as an alloy in a surface layer of the catalyst support extending less than about 0.2 mm from the surface of said support.
Claim 15
Dependent Claim
145 words
A catalyst having a specific activity of at least about 83 grams of vinyl acetate per gram of precious metal per hour measured at 150° C. consisting essentially of 1. a catalyst support having a particle diameter of from about 3 to about 7 mm, and a pore volume of from about 0.2 to about 1.5 mlg, a 10% by weight water suspension of said support having a pH of from about 3.0 to about 9.0, 2. a palladium-gold alloy distributed in a surface layer of said support, said surface layer extending less than about 0.5 mm from the surface of said support, the palladium in said alloy being present in an amount of from about 1.5 to about 5.0 grams per liter of catalyst, the gold being present in an amount of from about 0.5 to about 2.25 grams per liter of catalyst and
Claim 16
Dependent Claim
145 words
A catalyst having a specific activity of at least about 83 grams of vinyl acetate per gram of precious metal per hour measured at 150° C. consisting essentially of 1. a catalyst support having a particle diameter of from about 3 to about 7 mm, and a pore volume of from about 0.2 to about 1.5 mlg, a 10% by weight water suspension of said support having a pH of from about 3.0 to about 9.0, 2. a palladium-gold alloy distributed in a surface layer of said support, said surface layer extending less than about 0.5 mm from the surface of said support, the palladium in said alloy being present in an amount of from about 1.5 to about 5.0 grams per liter of catalyst, the gold being present in an amount of from about 0.5 to about 2.25 grams per liter of catalyst and
Claim 17
Dependent Claim
15 words
from about 5 to about 60 grams per liter of catalyst of alkali metal acetate.
Claim 18
Dependent Claim
15 words
from about 5 to about 60 grams per liter of catalyst of alkali metal acetate.
Claim 19
Dependent Claim
25 words
The catalyst of claim 14 wherein the catalyst support has an internal surface area of from about 10 to about 800 square meters per gram.
Claim 20
Dependent Claim
28 words
The catalyst of claim 15 wherein said palladium-gold alloy is distributed in a surface layer extending at most about 0.2 mm from the surface of the catalyst support.
Claim 21
Dependent Claim
21 words
The catalyst of claim 15 wherein the catalyst support has a pore volume of from about 0.5 to about 1.1 ml/g.
Claim 22
Dependent Claim
45 words
The catalyst of claim 17 wherein the palladium is present in an amount of from about 1.65 to about 3.3 grams per liter of catalyst and the gold is present in an amount of from about 0.75 to about 1.5 grams per liter of catalyst.
Claim 23
Dependent Claim
38 words
The catalyst of claim 18 wherein the catalyst support is silica containing at least about 90% SiO 2 , said catalyst support having an internal surface area of from about 40 to about 400 square meters per gram.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-12 | 1981-03-14 | 1981-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-12 | 1985-03-14 | 1985-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-12 | 1989-03-14 | 1989-09-13 | $7700.00 | Window Closed / Lapsed |