Cemented carbides containing hexagonal molybdenum
Assignee: TDY Industries LLC
•
Filing: 1975-05-29
•
Granted: 1977-09-20
•
Expires: 1995-05-29
Abstract
Abstract A composition of material is disclosed which comprises sintered carbide-binder metal alloys. The carbide is a solid solution of hexagonal tungsten monocarbide and molybdenum monocarbide of stoichiometric composition containing between 10 and 100 mole percent molybdenum monocarbide. The binder is selected from the metals of the iron group, and comprises between 3 and 50 weight percent of the composition. A method for making the hexagonal carbide is also disclosed.
Inventors
- 👤 Stephen Wei Hong Yih
- 👤 Samuel Austin Worcester, Jr.
- 👤 Erwin Rudy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:21
CPC Classifications
C; C22; C22C; C22C29/00; C22C29/02; C22C29/06
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
97 words
A composition of material comprising sintered carbide-binder metal alloys in which the carbide comprises a hexagonal monocarbide phase which is a solid solution of tungsten monocarbide and molybdenum monocarbide of stoichiometric composition containing between 10 and 100 mole percent molybdenum monocarbide, and in which the binder is selected from the metals of the iron group and from the additional group consisting of molybdenum, tungsten, chromium, copper, silver and aluminum, with the iron group consisting between 3 and 50 weight percent of the composition and the additional group comprising between 0 and 10 weight percent of the composition.
Claim 2
Dependent Claim
97 words
A composition of material comprising sintered carbide-binder metal alloys in which the carbide comprises a hexagonal monocarbide phase which is a solid solution of tungsten monocarbide and molybdenum monocarbide of stoichiometric composition containing between 10 and 100 mole percent molybdenum monocarbide, and in which the binder is selected from the metals of the iron group and from the additional group consisting of molybdenum, tungsten, chromium, copper, silver and aluminum, with the iron group consisting between 3 and 50 weight percent of the composition and the additional group comprising between 0 and 10 weight percent of the composition.
Claim 3
Dependent Claim
131 words
A composition of material comprising sintered carbide-binder metal alloys, in which the carbide comprises a hexagonal monocarbide phase which is a solid solution of tungsten monocarbide and molybdenum monocarbide of stoichiometric composition containing between 10 and 100 mole percent molybdenum carbide and a cubic carbide phase selected from the group consisting of titanium carbide, tantalum carbide, vanadium carbide, niobium carbide and hafnium carbide, with the cubic carbide comprising up to 85 weight percent of the total carbide phase, and in which the binder is selected from the iron group and from the additional group consisting of molybdenum, tungsten, chromium, copper, silver and aluminum, with the iron group comprising between 3 and 50 weight percent of the composition and the additional group comprising between 0 and 10 weight percent of the composition.
Claim 4
Dependent Claim
131 words
A composition of material comprising sintered carbide-binder metal alloys, in which the carbide comprises a hexagonal monocarbide phase which is a solid solution of tungsten monocarbide and molybdenum monocarbide of stoichiometric composition containing between 10 and 100 mole percent molybdenum carbide and a cubic carbide phase selected from the group consisting of titanium carbide, tantalum carbide, vanadium carbide, niobium carbide and hafnium carbide, with the cubic carbide comprising up to 85 weight percent of the total carbide phase, and in which the binder is selected from the iron group and from the additional group consisting of molybdenum, tungsten, chromium, copper, silver and aluminum, with the iron group comprising between 3 and 50 weight percent of the composition and the additional group comprising between 0 and 10 weight percent of the composition.
References Cited (Backward Citations)
GB890757A
Cited
US3479155A
Cited
US3677722A
Cited
GB1326769A
Cited
US3842581A
Cited
US3840367A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |