Continuous optical fiber preform fabrication method
Assignee: NTT Inc
•
Filing: 1977-04-05
•
Granted: 1977-12-13
•
Expires: 1997-04-05
Abstract
Abstract A refractory starting member is rotated and, at the same time, moved along the axis of rotation. A glass raw material for the formation of the core of a porous preform and consequently an optical fiber preform is introduced into a high temperature portion near the tip of a high temperature burner from a nozzle for the core disposed in alignment with the center of rotation of one end face of the starting member. The glass raw material blown out from the nozzle for the core are caused by the flames of the high temperature burner to react to produce glass fine particles, which are deposited on abovesaid end face of the starting member at the central portion thereof in its axial direction to form a porous core. At least one nozzle for spraying a glass raw material for the formation of the cladding of the optical fiber preform is disposed opposite to the end face of the starting member but a little deviated from the axis of rotation thereof, or disposed opposite to the peripheral surface of the porous core. The glass raw material for the cladding is sprayed from the nozzle for the cladding to the high temperature portion of the high temperature burner, and caused to react to form glass fine particles, which are deposited on the end face of the starting member on the outside of the porous core or on the peripheral surface thereof at the same time as the formation of the latter, forming a porous cladding. The porous preform thus obtained is moved into a high temperature furnace provided on the path of movement of the preform for the vitrification thereof into an optical fiber preform.
Inventors
- 👤 Tatsuo Izawa
- 👤 Tadashi Miyashita
- 👤 Fumiaki Hanawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:31
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01413; C03B37/0142; C03B37/01426; C03B37/01406; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2201/30; C03B2201/40; C03B2201/42; C03B2203/00; C03B2203/10; C03B2203/22; C03B2207/00; C03B2207/04; C03B2207/12; C03B2207/16; C03B2207/20; C03B2207/22; C03B2207/42; C03B2207/60; C03B2207/62; C03B2207/70; C03B2207/80; C03B2207/81; C03B2207/85; C03B2207/86
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
233 words
A continuous optical fiber preform fabrication method, comprising the steps of: preparing a refractory starting member; moving said starting member along its axis of rotation while rotating it by rotating and moving means; blowing a glass raw material for the formation of the core from a nozzle for the core into a high temperature portion near the tip of a high temperature burner for the reaction of said glass raw material to deposit glass fine particles consisting principally of silicon dioxide, resulting from the reaction, on one end face of said starting member to form thereon a columnar porous glass core about said axis of rotation of the starting member; blowing a glass raw material for the formation of the cladding from at least one nozzle for the cladding into a high temperature portion near the tip of a high temperature burner for the reaction of said glass raw material to deposit glass fine particles consisting principally of silicon dioxide, resulting from the reaction, on the peripheral surface of said porous glass core to form thereon a porous glass layer for the cladding to provide a porous preform, said porous glass layer having a refractive index lower than said porous glass core; and continuously feeding said porous preform into a high temperature furnace provided on said axis of rotation of the starting member for vitrifying said porous preform into an optical fiber preform.
Claim 2
Dependent Claim
233 words
A continuous optical fiber preform fabrication method, comprising the steps of: preparing a refractory starting member; moving said starting member along its axis of rotation while rotating it by rotating and moving means; blowing a glass raw material for the formation of the core from a nozzle for the core into a high temperature portion near the tip of a high temperature burner for the reaction of said glass raw material to deposit glass fine particles consisting principally of silicon dioxide, resulting from the reaction, on one end face of said starting member to form thereon a columnar porous glass core about said axis of rotation of the starting member; blowing a glass raw material for the formation of the cladding from at least one nozzle for the cladding into a high temperature portion near the tip of a high temperature burner for the reaction of said glass raw material to deposit glass fine particles consisting principally of silicon dioxide, resulting from the reaction, on the peripheral surface of said porous glass core to form thereon a porous glass layer for the cladding to provide a porous preform, said porous glass layer having a refractive index lower than said porous glass core; and continuously feeding said porous preform into a high temperature furnace provided on said axis of rotation of the starting member for vitrifying said porous preform into an optical fiber preform.
Claim 3
Dependent Claim
80 words
The method according to claim 1, wherein said at least one nozzle for the cladding is disposed opposite to said one end face of the starting member but a little deviated from said axis of rotation to deposit the glass fine particles on said one end face of the starting member at the same time as the glass fine particles from said nozzle for the core, forming a porous glass layer on the peripheral surface of said porous glass core.
Claim 4
Dependent Claim
57 words
The method according to claim 2, wherein said nozzle for the core and said at least one nozzle for the cladding are disposed to partially intermix the glass fine particles from both of said nozzles to obtain a graded index type optical fiber preform that the refractive index profile in its cross-section is substantially a square curve.
Claim 5
Dependent Claim
54 words
The method according to claim 2, wherein at least one pair of nozzles for the formation of the cladding are disposed symmetrically with respect to said axis of rotation of the starting member, each pair of nozzles symmetrical with respect to said axis of rotation blowing off glass raw materials of the same components.
Claim 6
Dependent Claim
25 words
The method according to claim 2, said nozzle for the core and said nozzle for the cladding are respectively incorporated in different high temperature burners.
Claim 7
Dependent Claim
20 words
The method according to claim 2, wherein said nozzle for the cladding are all incorporated in one high temperature burner.
Claim 8
Dependent Claim
70 words
The method according to claim 1, wherein at least one nozzle for the cladding is provided further to the side of the high temperature furnace than said nozzle for the core, and wherein glass fine particles from said at least one nozzle for the cladding are deposited on the peripheral surface of said porous glass core from a lateral direction, to form thereon a porous glass layer for the cladding.
Claim 9
Dependent Claim
46 words
The method according to claim 7, wherein a plurality of nozzles for the cladding are arranged along said axis of rotation for blowing off glass raw materials selected so that the refractive indexes of the resulting glass decrease gradually as said high temperature furnace is approached.
Claim 10
Dependent Claim
48 words
The method according to claim 7, wherein a cutting blade is contacted with the peripheral surface of said porous glass core before said porous glass core reaches the position of deposition of said porous glass layer, thereby maintaining the diameter of said porous preform at a constant value.
Claim 11
Dependent Claim
166 words
The method according to claim 1, wherein at least one nozzle for the cladding is disposed opposite to said starting material but a little deviated from said axis of rotation to deposit glass fine particles from said at least one nozzle on said one end face of the starting member in its axial direction to form a porous glass layer on the peripheral surface of said porous glass core at the same time as the formation thereof, and wherein at least one more nozzle for the cladding is provided further to the side of said high temperature furnace than said nozzle to blow a glass raw material for the formation of glass of smaller refractive index than that of the glass raw material supplied to said nozzle for the cladding, glass fine particles obtained from said at least one more nozzle for the cladding being deposited on the peripheral surface of said porous glass layer for the cladding to form thereon an outer porous glass layer.
Claim 12
Dependent Claim
36 words
The method according to claim 1, wherein an inert gas is emitted in layers along said axis of rotation from the marginal edge of said high temperature burner to prevent diffusion of the glass fine particles.
Claim 13
Dependent Claim
46 words
The method according to claim 1, wherein the position of the growing end face of said porous preform in the axial direction of said starting material is detected to control the moving speed of said starting member to hold the diameter of said porous preform constant.
Claim 14
Dependent Claim
37 words
The method according to claim 1, wherein said high temperature burner is a burner for use with oxygen and hydrogen or other combustible gas, and hydrolyzes the glass raw materials by flames to produce glass fine particles.
Claim 15
Dependent Claim
44 words
The method according to claim 1, said high temperature burner is a plasma torch, and wherein a high temperature oxygen gas produced by said burner and glass raw materials containing no hydrogen are caused to react with each other to produce glass fine particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |