Sulfur containing silicone elastomer and method of preparation
Assignee: Dow Silicones Corp
•
Filing: 1976-03-03
•
Granted: 1978-01-03
•
Expires: 1996-03-03
Abstract
Abstract Mixing a polydimethylsiloxane having terminal vinyl groups or silacyclopentenyl groups, a mercaptoorganopolysiloxane and an organic peroxide provides a composition which cures to an elastomer at room temperature or by heating. The elastomers are useful as sealants and rubber articles.
Inventors
- 👤 Gary R. Homan
- 👤 Chi-Long Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:53
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08K; C08K5/00; C08K5/04; C08K5/14; C08L83/08; C08G; C08G77/00; C08G77/04; C08G77/20; C08G77/22; C08G77/28; C08G77/70
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
271 words
A composition curable to an elastomer comprising a material prepared by mixing A. 5 to 95 weight percent based on the combined weight of (A) and (B) of a polydimethylsiloxane having a viscosity of at least 0.3 Pa.sup.. s at 25° C. and being endblocked with a siloxy unit selected from the group consisting of methylphenylvinylsiloxy units, dimethylvinylsiloxy units and units of the formula ##STR26## wherein R is a monovalent radical selected from the group consisting of alkyl radicals of from 1 to 3 carbon atoms inclusive and phenyl radicals, B. 5 to 95 weight percent based on the combined weight of (A) and (B) of a mercaptoorganopolysiloxane consisting essentially of a combination of units selected from dimethylsiloxane units, trimethylsiloxane units, units of the formula ##STR27## units of the formula ##STR28## units of the formula ##STR29## units of the formula ##STR30## units of the formula ##STR31## and units of the formula ##STR32## wherein R is defined above, R' is methyl or ethyl and n has a value of from 1 to 4 inclusive, there being in said mercaptoorganopolysiloxane an average of at least two sulfur containing siloxane units per molecule and no more than 16 weight percent --SH groups based on the weight of the mercaptoorganopolysiloxane, the molecular weight of the mercaptoorganopolysiloxane being at least 1,000, the amount of (A) and (B) being combined in weight ratios sufficient to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of 0.1:1 to 15:1, C. 1.4 to 5.5 parts by weight organic peroxide based on 100 parts by weight of (A) and (B) combined.
Claim 2
Dependent Claim
271 words
A composition curable to an elastomer comprising a material prepared by mixing A. 5 to 95 weight percent based on the combined weight of (A) and (B) of a polydimethylsiloxane having a viscosity of at least 0.3 Pa.sup.. s at 25° C. and being endblocked with a siloxy unit selected from the group consisting of methylphenylvinylsiloxy units, dimethylvinylsiloxy units and units of the formula ##STR26## wherein R is a monovalent radical selected from the group consisting of alkyl radicals of from 1 to 3 carbon atoms inclusive and phenyl radicals, B. 5 to 95 weight percent based on the combined weight of (A) and (B) of a mercaptoorganopolysiloxane consisting essentially of a combination of units selected from dimethylsiloxane units, trimethylsiloxane units, units of the formula ##STR27## units of the formula ##STR28## units of the formula ##STR29## units of the formula ##STR30## units of the formula ##STR31## and units of the formula ##STR32## wherein R is defined above, R' is methyl or ethyl and n has a value of from 1 to 4 inclusive, there being in said mercaptoorganopolysiloxane an average of at least two sulfur containing siloxane units per molecule and no more than 16 weight percent --SH groups based on the weight of the mercaptoorganopolysiloxane, the molecular weight of the mercaptoorganopolysiloxane being at least 1,000, the amount of (A) and (B) being combined in weight ratios sufficient to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of 0.1:1 to 15:1, C. 1.4 to 5.5 parts by weight organic peroxide based on 100 parts by weight of (A) and (B) combined.
Claim 3
Dependent Claim
30 words
The composition according to claim 1 in which there is up to 100 parts by weight of a filler based on 100 parts by weight of (A) and (B) combined.
Claim 4
Dependent Claim
39 words
The composition according to claim 1 in which (A) and (B) are combined in sufficient amounts to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of 1:1 to 15:1.
Claim 5
Dependent Claim
30 words
The composition according to claim 3 in which there is up to 100 parts by weight of a filler based on 100 parts by weight of (A) and (B) combined.
Claim 6
Dependent Claim
44 words
The composition according to claim 1 in which (A) and (B) are combined in sufficient amounts to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of from 0.1:1 up to but not including 1:1.
Claim 7
Dependent Claim
30 words
The composition according to claim 5 in which there is up to 100 parts by weight of a filler based on 100 parts by weight of (A) and (B) combined.
Claim 8
Dependent Claim
26 words
The composition according to claim 1 in which the amount of --SH group does not exceed 3.5 weight percent based on the weight of the mercaptoorganopolysiloxane.
Claim 9
Dependent Claim
30 words
The composition according to claim 7 in which there is up to 100 parts by weight of a filler based on 100 parts by weight of (A) and (B) combined.
Claim 10
Dependent Claim
26 words
The composition according to claim 1 in which the amount of --SH group does not exceed 2.2 weight percent based on the weight of the mercaptoorganopolysiloxane.
Claim 11
Dependent Claim
53 words
The composition according to claim 3 in which (A) is present in an amount of from 40 to 90 weight percent based on the combined weight of (A) and (B), and (B) is present in an amount of from 10 to 60 weight percent based on the combined weight of (A) and (B).
Claim 12
Dependent Claim
23 words
The composition according to claim 10 in which the polydimethylsiloxane has a viscosity of from 0.3 to 35 Pa.sup.. s at 25° C.
Claim 13
Dependent Claim
21 words
The composition according to claim 11 in which the mercaptoorganopolysiloxane consists essentially of dimethylsiloxane units and units of the formula ##STR33##
Claim 14
Dependent Claim
15 words
The composition according to claim 12 in which R' is methyl and n is 3.
Claim 15
Dependent Claim
21 words
The composition according to claim 11 in which the mercaptoorganopolysiloxane consists essentially of dimethylsiloxane units and units of the formula ##STR34##
Claim 16
Dependent Claim
15 words
The composition according to claim 14 in which R is methyl and n is 3.
Claim 17
Independent Claim
285 words
A method of preparing an elastomer comprising I. mixing at a temperature below 50° C. A. 5 to 95 weight percent based on the combined weight of (A) and (B) of a polydimethylsiloxane having a viscosity of at least 0.3 Pa.sup.. s at 25° C. and being endblocked with a siloxy unit selected from the group consisting of methylphenylvinylsiloxy units, dimethylvinylsiloxy units and units of the formula ##STR35## wherein R is a monovalent radical selected from the group consisting of alkyl radicals of from 1 to 3 carbon atoms inclusive and phenyl radicals, B. 5 to 95 weight percent based on the combined weight of (A) and (B) of a mercaptoorganopolysiloxane consisting essentially of a combination of units selected from dimethylsiloxane units, trimethylsiloxane units, units of the formula ##STR36## units of the formula ##STR37## units of the formula ##STR38## units of the formula ##STR39## units of the formula ##STR40## and units of the formula ##STR41## where R is defined above, R' is methyl or ethyl and n has a value of from 1 to 4 inclusive, there being in said mercaptoorganopolysiloxane an average of at least two sulfur containing siloxane units per molecule and no more than 16 weight percent --SH groups based on the weight of the mercaptoorganopolysiloxane, the molecular weight of the mercaptoorganopolysiloxane being at least 1,000, the amount of (A) and (B) being combined in weight ratios sufficient to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of 0.1:1 to 15:1, C. 1.4 to 5.5 parts by weight organic peroxide based on 100 parts by weight of (A) and (B) combined thereafter Ii. curing the resulting mixture of (I) above 20° C.
Claim 18
Independent Claim
285 words
A method of preparing an elastomer comprising I. mixing at a temperature below 50° C. A. 5 to 95 weight percent based on the combined weight of (A) and (B) of a polydimethylsiloxane having a viscosity of at least 0.3 Pa.sup.. s at 25° C. and being endblocked with a siloxy unit selected from the group consisting of methylphenylvinylsiloxy units, dimethylvinylsiloxy units and units of the formula ##STR35## wherein R is a monovalent radical selected from the group consisting of alkyl radicals of from 1 to 3 carbon atoms inclusive and phenyl radicals, B. 5 to 95 weight percent based on the combined weight of (A) and (B) of a mercaptoorganopolysiloxane consisting essentially of a combination of units selected from dimethylsiloxane units, trimethylsiloxane units, units of the formula ##STR36## units of the formula ##STR37## units of the formula ##STR38## units of the formula ##STR39## units of the formula ##STR40## and units of the formula ##STR41## where R is defined above, R' is methyl or ethyl and n has a value of from 1 to 4 inclusive, there being in said mercaptoorganopolysiloxane an average of at least two sulfur containing siloxane units per molecule and no more than 16 weight percent --SH groups based on the weight of the mercaptoorganopolysiloxane, the molecular weight of the mercaptoorganopolysiloxane being at least 1,000, the amount of (A) and (B) being combined in weight ratios sufficient to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of 0.1:1 to 15:1, C. 1.4 to 5.5 parts by weight organic peroxide based on 100 parts by weight of (A) and (B) combined thereafter Ii. curing the resulting mixture of (I) above 20° C.
Claim 19
Dependent Claim
56 words
The method in accordance with claim 16 in which (A) and (B) are combined in sufficient amounts to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of 1:1 to 15:1 and in (II) the resulting mixture of (I) is cured in the presence of oxygen gas.
Claim 20
Dependent Claim
19 words
The method in accordance with claim 17 in which the resulting mixture of (I) is heated above 50° C.
Claim 21
Dependent Claim
71 words
The method in accordance with claim 16 in which (A) and (B) are combined in sufficient amounts to provide a molar ratio of moles of --SH group in (B) per mole of C═C bond in (A) of from 0.1 up to but not including 1:1 and in (II) the resulting mixture of (I) is cured in the absence of oxygen gas by heating the resulting mixture of (I) above 50° C.
References Cited (Backward Citations)
US3816282A
Cited
US3873499A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-02 | 1981-07-04 | 1982-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-02 | 1985-07-04 | 1986-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-02 | 1989-07-04 | 1990-01-03 | $7700.00 | Window Closed / Lapsed |