Austenitic aging of metallic compositions
Assignee: Raychem Corp
•
Filing: 1975-02-18
•
Granted: 1978-01-10
•
Expires: 1995-02-18
Abstract
Abstract Some metallic compositions that undergo a reversible transformation between austenitic and martensitic states as a result of being heated or cooled through critical temperature ranges may lose a portion or all of the ability to revert from martensite to austenite. That loss can be inhibited by "aging" the composition prior to its conversion to the martensitic state by holding it at a temperature at which it exists in the austenitic state. The time required to significantly inhibit loss of reversibility may vary as the nature of the composition changes. For a specific composition, the time required typically is shortened as the holding temperature is raised. The ability of a composition to respond to preconditioning methods by which its A s temperature can be elevated may also be improved by aging in the austenitic state prior to attempting preconditioning.
Inventors
- 👤 Greville B. Brook
- 👤 Peter L. Brooks
- 👤 Roger F. Iles
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:40
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/08
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
30 words
A metallic composition having a substantially reduced tendency to lose reversibility between its martensitic and austenitic state as compared with its normal tendency to do so at a given temperature.
Claim 2
Dependent Claim
30 words
A metallic composition having a substantially reduced tendency to lose reversibility between its martensitic and austenitic state as compared with its normal tendency to do so at a given temperature.
Claim 3
Dependent Claim
45 words
An alloy comprising copper and a metal selected from a group consisting of zinc and aluminum, said alloy having a substantially reduced tendency to lose reversibility between its martensitic and austenitic state as compared with its normal tendency to do so at a given temperature.
Claim 4
Dependent Claim
45 words
An alloy comprising copper and a metal selected from a group consisting of zinc and aluminum, said alloy having a substantially reduced tendency to lose reversibility between its martensitic and austenitic state as compared with its normal tendency to do so at a given temperature.
Claim 5
Dependent Claim
10 words
The alloy of claim 2 wherein said metal is zinc.
Claim 6
Dependent Claim
24 words
The alloy of claim 3 and wherein said alloy contains a third metal selected from the group consisting of aluminum, manganese, silicon and tin.
Claim 7
Dependent Claim
11 words
The alloy of claim 4 wherein said third metal is silicon.
Claim 8
Dependent Claim
11 words
The alloy of claim 4 wherein said third metal is aluminum.
Claim 9
Dependent Claim
11 words
The alloy of claim 4 wherein the third metal is manganese.
Claim 10
Dependent Claim
10 words
The alloy of claim 2 wherein said metal is aluminum.
Claim 11
Dependent Claim
23 words
The alloy of claim 7 wherein said alloy contains a third metal selected from a group consisting of manganese, silicon, tin and zinc.
Claim 12
Dependent Claim
39 words
The alloy of claim 2 comprising 60-85 wt. % copper, 0 to about 40 wt. % zinc, 0 to about 5 wt. % silicon, 0 to about 14 wt. % aluminum and 0 to about 15 wt. % manganese.
Claim 13
Independent Claim
67 words
A method of inhibiting loss of reversibility between the martensitic and austenitic states in a metallic composition comprising holding said composition at a temperature above the M s temperature while in the austenitic state for a time sufficient to reduce said loss, said holding temperature being one at which there is no significant transformation of the metallic composition to a phase that undergoes no reversible austenite-martensite transformation.
Claim 14
Independent Claim
67 words
A method of inhibiting loss of reversibility between the martensitic and austenitic states in a metallic composition comprising holding said composition at a temperature above the M s temperature while in the austenitic state for a time sufficient to reduce said loss, said holding temperature being one at which there is no significant transformation of the metallic composition to a phase that undergoes no reversible austenite-martensite transformation.
Claim 15
Dependent Claim
26 words
The process of claim 10 wherein, prior to said holding step, said composition is heated to a temperature substantially above room temperature and is then quenched.
Claim 16
Dependent Claim
26 words
The process of claim 11 wherein said quenching elevated temperature is a temperature at which the composition is at least substantially wholly in the austenitic state.
Claim 17
Dependent Claim
29 words
A method according to claim 11 wherein the M s temperature of the composition is below room temperature and the holding temperature is from about 50° to 125° C.
Claim 18
Dependent Claim
19 words
A method according to claim 14 wherein the holding time is from about 5 minutes to about 4 hours.
Claim 19
Dependent Claim
90 words
An alloy comprising copper and a metal selected from the group consisting of zinc and aluminum having a substantially reduced tendency to lose reversibility between its martensitic and austenitic state, said alloy being the product of the process comprising holding said composition at a temperature above the M s temperature while in the austenitic state for a time sufficient to reduce said tendency to lose reversibility, said holding temperature being one at which there is no significant transformation of the alloy to a phase that undergoes no reversible austenite-martensite transformation.
Claim 20
Dependent Claim
90 words
An alloy comprising copper and a metal selected from the group consisting of zinc and aluminum having a substantially reduced tendency to lose reversibility between its martensitic and austenitic state, said alloy being the product of the process comprising holding said composition at a temperature above the M s temperature while in the austenitic state for a time sufficient to reduce said tendency to lose reversibility, said holding temperature being one at which there is no significant transformation of the alloy to a phase that undergoes no reversible austenite-martensite transformation.
Claim 21
Dependent Claim
19 words
An alloy according to claim 16 wherein during said holding, the alloy is substantially free of externally applied stress.
Claim 22
Dependent Claim
10 words
The alloy of claim 17 wherein said metal is zinc.
Claim 23
Dependent Claim
23 words
The alloy of claim 18 wherein said alloy contains a third metal selected from the group consisting of aluminum, manganese, silicon and tin.
Claim 24
Dependent Claim
10 words
The alloy of claim 17 wherein said metal is aluminum.
Claim 25
Dependent Claim
23 words
The alloy of claim 20 wherein said alloy contains a third metal selected from the group consisting of manganese, silicon, tin and zinc.
Claim 26
Dependent Claim
39 words
The alloy of claim 17 comprising 60-85 wt. percent copper, 0 to about 40 wt. percent zinc, 0 to about 5 wt. percent silicon, 0 to about 14 wt. percent aluminum and 0 to about 15 wt. percent manganese.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |