Porous carbon fuel cell substrates and method of manufacture
Assignee: RTX Corp
•
Filing: 1975-12-15
•
Granted: 1978-03-21
•
Expires: 1995-12-15
Abstract
Abstract Porous carbon sheets suitable for use as fuel cell electrode support plates are produced by stabilizing acrylic filament precursors through the controlled addition of oxygen thereto. The stabilized filaments are thereafter chopped into short lengths, felted and pressed into sheets with the pressing step being performed at a temperature determined by the oxygen content of the stabilized filaments. The sheets are thereafter pyrolyzed to produce the desired porous substrate material.
Inventors
- 👤 George K. Layden
- 👤 Roscoe A. Pike
- 👤 Michael A. DeCrescente
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:38
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/20; D01F9/21; D01F9/22; D21; D21H; D21H13/00; D21H13/10; D21H13/12; D21H13/18; D21H5/00; D21H5/12; D21H5/20; D21H5/205; H; H01; H01M; H01M4/00; H01M4/86; H01M4/96; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y10; Y10T; Y10T442/00; Y10T442/50; Y10T442/56
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
143 words
A process for the manufacture of substrate material having a porosity in the range of 50% to 70% comprising the steps of: stabilizing a plurality of acrylic polymer filaments, said filaments containing at least 50% acrylonitrile, by heating in an oxidizing atmosphere until 3 to 10% by weight oxygen is introduced into the polymer; reducing the length of the stabilized filaments to form fibers having an average length commensurate with the desired substrate porosity; felting the fibers of reduced length to provide a layer of uniform thickness with random fiber orientation; subjecting the layer of fibers to heat and pressure in the range of 50-1000 psi to cause self-bonding of contiguous fibers whereby a sheet is formed without the aid of a binder for the felted fibers; and carbonizing the sheet by heating in a non-oxidizing atmosphere to produce a porous substrate material.
Claim 2
Dependent Claim
143 words
A process for the manufacture of substrate material having a porosity in the range of 50% to 70% comprising the steps of: stabilizing a plurality of acrylic polymer filaments, said filaments containing at least 50% acrylonitrile, by heating in an oxidizing atmosphere until 3 to 10% by weight oxygen is introduced into the polymer; reducing the length of the stabilized filaments to form fibers having an average length commensurate with the desired substrate porosity; felting the fibers of reduced length to provide a layer of uniform thickness with random fiber orientation; subjecting the layer of fibers to heat and pressure in the range of 50-1000 psi to cause self-bonding of contiguous fibers whereby a sheet is formed without the aid of a binder for the felted fibers; and carbonizing the sheet by heating in a non-oxidizing atmosphere to produce a porous substrate material.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein the step of reducing the length of the stabilized filaments comprises: mechanically chopping the filaments into lengths commensurate with the desired substrate porosity.
Claim 4
Dependent Claim
59 words
The method of claim 1 wherein the substrate material has a thickness in the range of 15-20 mils and a lateral resistivity in the range of 0.01 to 0.05 ohm-cm. and wherein the step of felting comprises: distributing the fibers in a water slurry; collecting the distributed fibers from the slurry on a surface; and drying the collected fibers.
Claim 5
Dependent Claim
58 words
The method of claim 1 wherein the step of subjecting the layer of fibers to heat and pressure to form a sheet comprises: placing the layer of fibers in a mold; heating the mold to a temperature commensurate with the oxygen content of the stabilized filaments; and applying a pressure in the range of 50 to 1000 psi.
Claim 6
Dependent Claim
18 words
The method of claim 4 wherein the applied temperature is in the range of 160° to 350° C.
Claim 7
Dependent Claim
29 words
The method of claim 5 wherein the step of reducing the length of the stabilized filaments comprises: mechanically chopping the filaments into lengths commensurate with the desired substrate porosity.
Claim 8
Dependent Claim
59 words
The method of claim 6 wherein the substrate material has a thickness in the range of 15-20 mils and a lateral resistivity in the range of 0.01 to 0.05 ohm-cm. and wherein the step of felting comprises: distributing the fibers in a water slurry; collecting the distributed fibers from the slurry on a surface; and drying the collected fibers.
Claim 9
Dependent Claim
62 words
The method of claim 4 wherein the substrate has a porosity of 55 to 65%, a thickness in the range of 15-20 mils and a lateral resistivity in the range of 0.01 to 0.05 ohm-cm. and wherein the step of stabilizing comprises: heating the filaments in an oxidizing atmosphere until 4 to 8% by weight of oxygen is introduced into the polymer.
Claim 10
Dependent Claim
24 words
The method of claim 8 wherein the temperature applied during the formation of the sheet is in the range of 180° to 270° C.
Claim 11
Dependent Claim
37 words
The method of claim 4 wherein the step of carbonizing the sheet comprises: heating in an argon atmosphere to a temperature in the range of 1000° to 1260° C at a rate of 100° C per hour.
Claim 12
Dependent Claim
37 words
The method of claim 9 wherein the step of carbonizing the sheet comprises: heating in an argon atmosphere to a temperature in the range of 1000° to 1260° C at a rate of 100° C per hour.
Claim 13
Dependent Claim
29 words
The method of claim 11 wherein the step of reducing the length of the stabilized filaments comprises: mechanically chopping the filaments into lengths commensurate with the desired substrate porosity.
Claim 14
Dependent Claim
33 words
The method of claim 12 wherein the step of felting comprises: distributing the fibers in a water slurry; collecting the distributed fibers from the slurry on a surface; and drying the collected fibers.
References Cited (Backward Citations)
US3367812A
Cited
US3265557A
Cited
US3619139A
Cited
US3639266A
Cited
US3671192A
Cited
US3700511A
Cited
US4002426A
Cited
US3818082A
Cited
US3728423A
Cited
US3829327A
Cited
US3971669A
Cited
US3998689A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-20 | 1981-09-19 | 1982-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-20 | 1985-09-19 | 1986-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-20 | 1989-09-19 | 1990-03-21 | $7700.00 | Window Closed / Lapsed |