Method of producing a composite coated steel sheet
Assignee: Toyo Kohan Co Ltd
•
Filing: 1976-10-28
•
Granted: 1978-04-25
•
Expires: 1996-10-28
Abstract
Abstract A method of providing a composite coated steel sheet is provided herein by dipping a steel sheet into a suspension solution consisting of a water-soluble and/or water-dispersible organic polymer resin, a water-dispersible sol of a metal compound and an infusible powder of a water-insoluble polymer resin, removing the coated steel sheet from the suspension and curing the coated composite by heat treatment. In certain cases, a metal powder, an alloy powder of said metal and a powder of a difficultly water-soluble or water-insoluble compound of said metal may be used in the suspension solution.
Inventors
- 👤 Keiji Ariga
- 👤 Nobuyuki Tsutsui
- 👤 Katsumi Kanda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:25
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/448
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
63 words
A method of producing a composite coated steel sheet which comprises electrolytically treating a steel sheet in a suspension solution consisting essentially of a water-soluble resin or a water-dispersible resin; a water-dispersible sol of a metal compound and an infusible organic polymer resin powder, removing the coated steel sheet from the suspension solution and then curing the coated steel sheet by heat treatment.
Claim 2
Independent Claim
63 words
A method of producing a composite coated steel sheet which comprises electrolytically treating a steel sheet in a suspension solution consisting essentially of a water-soluble resin or a water-dispersible resin; a water-dispersible sol of a metal compound and an infusible organic polymer resin powder, removing the coated steel sheet from the suspension solution and then curing the coated steel sheet by heat treatment.
Claim 3
Dependent Claim
49 words
The method of claim 1, wherein the water-soluble resin and water-dispersible resin are selected from the group consisting of epoxy resins, phenol resins, alkyl resins, acryl resins and butadiene resins which are added to the suspension solution as a solid in an amount from about 2 to 50 g/l.
Claim 4
Dependent Claim
58 words
The method of claim 1, wherein the sol is an inorganic compound selected from the group consisting of an oxide or hydroxide of nickel, titanium, chromium, zinc, aluminum and tin having an average particle size of about 1 to 500 mμ, which sol is added to said suspension solution in an amount from about 1 to 100 g/l.
Claim 5
Dependent Claim
49 words
The method of claim 1, wherein the infusible organic polymer resin powder is selected from nylon, polyethylene, polypropylene, polyamides, diacrylphthalate, ethylene-vinyl acetate copolymer resins, cellulose acetate butylate, polyurethanes, polystyrol, polycarbonates, chlorovinyl resins, polyfluorovinyl resins, epoxy resins or acrylic resins, which resins have an average particle diameter of under 200μ.
Claim 6
Dependent Claim
146 words
The method of claim 1, wherein the water-soluble or water-dispersible resins are selected from the group consisting of epoxy resins, phenol resins, alkyl resins, acryl resins and butadiene resins present in the suspension solution in an amount of 2 to 50 g/l; the sol is an inorganic compound selected from the group consisting of an oxide or hydroxide of nickel, titanium, chromium, zinc, aluminum and tin having an average particle size of about 1 to 500 mμ, said sol being present in the suspension solution in an amount from 1 to 100 g/l; the infusible organic polymer resin powder is selected from nylon, polyethylene, polypropylene, polyamides, diacrylphthalate, ethylene-vinyl acetate copolymer resins, cellulose acetate butylate, polyurethanes, polystyrol, polycarbonates, chlorovinyl resins, polyfluorovinyl resins, epoxy resins or acrylic resins, which resins have an average particle diameter of under 200μ in a concentration ranging from 3 g/l to 100 g/l.
Claim 7
Independent Claim
97 words
A method of producing a composite coated steel sheet which comprises electrolytically treating a steel sheet in a suspension solution consisting essentially of at least one water-soluble resin or a water-dispersible resin; a water-dispersible sol of a metal compound and an infusible organic polymer resin powder, and at least one member selected from the group consisting of a metal powder, an alloy powder of said metal or a powder of a difficultly water-soluble or water-insoluble compound of said metal, removing the coated metal sheet from the suspension and then curing the coated metal sheet by heat treatment.
Claim 8
Independent Claim
97 words
A method of producing a composite coated steel sheet which comprises electrolytically treating a steel sheet in a suspension solution consisting essentially of at least one water-soluble resin or a water-dispersible resin; a water-dispersible sol of a metal compound and an infusible organic polymer resin powder, and at least one member selected from the group consisting of a metal powder, an alloy powder of said metal or a powder of a difficultly water-soluble or water-insoluble compound of said metal, removing the coated metal sheet from the suspension and then curing the coated metal sheet by heat treatment.
Claim 9
Dependent Claim
49 words
The method of claim 6, wherein the infusible organic polymer resin powder is selected from nylon, polyethylene, polypropylene, polyamides, diacrylphthalate, ethylene-vinyl acetate copolymer resins, cellulose acetate butylate, polyurethanes, polystyrol, polycarbonates, chlorovinyl resins, polyfluorovinyl resins, epoxy resins or acrylic resins, which resins have an average particle diameter of under 200μ.
Claim 10
Dependent Claim
39 words
The method of claim 6, wherein the metal powder is selected from aluminum, zinc, chromium, cobalt, iron, nickel, tin, lead, copper, manganese, titanium, molybdenum, zirconium, bismuth, antimony or tungsten, said metal having an average particle diameter of under 200μ.
Claim 11
Dependent Claim
44 words
The method of claim 6, wherein the alloy powder is an alloy of the metal selected from aluminum, zinc, chromium, cobalt, nickel, iron, tin, lead, copper, manganese, titanium, molybdenum, zirconium, bismuth, antimony or tungsten, said metal having an average particle diameter of under 200μ.
Claim 12
Dependent Claim
266 words
The method of claim 6, wherein the water-soluble and water-dispersible resins are selected from the group consisting of epoxy resins, phenol resins, alkyl resins, acryl resins and butadiene resins present in the suspension solution in an amount of 2 to 50 g/l; the sol is an inorganic compound selected from the group consisting of an oxide or hydroxide of nickel, titanium, chromium, zinc, aluminum and tin having an average particle size of about 1 to 500 mμ, said sol being present in the suspension solution in an amount of from 1 to 100 g/l; the infusible organic polymer resin powder is selected from nylon, polyethylene, polypropylene, polyamides, diacrylphthalate, ethylene-vinyl acetate copolymer resins, cellulose acetate butylate, polyurethanes, polystyrol, polycarbonates, chlorovinyl resins, polyfluorovinyl resins, epoxy resins or acrylic resins, which resins have an average particle diameter of under 200μ in a concentration ranging from 3 g/l to 100 g/l; the metal powder is selected from aluminum, zinc, chromium, cobalt, nickel, iron, tin, lead, copper, manganese, titanium, molybdenum, zirconium, bismuth, antimony or tungsten; the alloy powder is selected from alloys of the metals of aluminum, zinc, chromium, cobalt, nickel, iron, tin, lead, copper, manganese, titanium, molybdenum, zirconium, bismuth, antimony or tungsten, and the difficultly water-soluble or water-insoluble compound powder is a compound of a metal selected from aluminum, zinc, chromium, cobalt, nickel, iron, tin, lead, copper, manganese, titanium, molybdenum, zirconium, bismuth, antimony or tungsten; said metal powders, alloy powder and difficultly water-soluble or water-insoluble components having an average particle diameter of under 200μ and being present in the suspension solution in amounts ranging from 3 g/l to 700 g/l.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-24 | 1981-10-24 | 1982-04-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-24 | 1985-10-24 | 1986-04-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-24 | 1989-10-24 | 1990-04-25 | $7700.00 | Window Closed / Lapsed |