US4087622A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing vinyl acetate
Assignee: Bayer AG
•
Filing: 1975-06-23
•
Granted: 1978-05-02
•
Expires: 1995-06-23
Abstract
Abstract Vinyl acetate is produced through reaction of ethylene, oxygen and acetic acid in vapor phase employing a catalyst which comprises 0.3 to 3.0 weight % of palladium metal, 0.0157 to 1.8 weight % of gold metal and 1 to 30 weight % of an alkali metal acetate, all based on the weight of the carrier or catalyst support therefor. These components are supported on said carrier or support under such conditions that (1) at least 90% by weight of each of the supported palladium and gold metals is distributed proximate the external surfaces of the carrier particles, extending to depths no greater than about 30% of the radius of each particle as measured from the external surface of each particle to the center of said particle, and (2) the proportion of gold to palladium ranges from about 5 to 60% by weight, based upon the total weight of the gold and palladium.
Inventors
- 👤 Michihiro Nakamura
- 👤 Yuzuru Fujiwara
- 👤 Teruo Yasui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 13:42
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/58; B01J23/48; B01J23/52; C; C07; C07C; C07C67/00; C07C67/04; C07C67/05; C07C67/055; B01J35/00; B01J35/30; B01J35/396; B01J35/397; B01J35/60; B01J35/61; B01J35/613; B01J35/615; B01J35/63; B01J35/635; B01J35/638; B01J35/66
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
173 words
A method of producing vinyl acetate, which comprises reacting ethylene, oxygen and acetic acid, in vapor phase, in the presence of a catalyst comprising a particulate, porous carrier, at least predominantly comprised of a member selected from the group consisting of silica, alumina, and mixtures thereof supporting 0.3 to 3.0 percent by weight of palladium metal, 0.0157 to 1.8 percent by weight of gold metal, and 1 to 30 percent by weight of an alkali metal acetate, all based on the weight of said carrier, and wherein and on said carrier at least 90 percent by weight of each of the supported palladium and gold is distributed proximate the external surfaces of the carrier particles, extending to depths no greater than about 30% of particles radius as measured from the exterior surface to the center of such particles, said porous carrier has a particle radius 1.0 to 5.0 millimeters, a pore volume of 0.1 to 2.0 cubic centimeters per gram and an internal surface area of 10 to 350 square meters per gram.
Claim 2
Independent Claim
173 words
A method of producing vinyl acetate, which comprises reacting ethylene, oxygen and acetic acid, in vapor phase, in the presence of a catalyst comprising a particulate, porous carrier, at least predominantly comprised of a member selected from the group consisting of silica, alumina, and mixtures thereof supporting 0.3 to 3.0 percent by weight of palladium metal, 0.0157 to 1.8 percent by weight of gold metal, and 1 to 30 percent by weight of an alkali metal acetate, all based on the weight of said carrier, and wherein and on said carrier at least 90 percent by weight of each of the supported palladium and gold is distributed proximate the external surfaces of the carrier particles, extending to depths no greater than about 30% of particles radius as measured from the exterior surface to the center of such particles, said porous carrier has a particle radius 1.0 to 5.0 millimeters, a pore volume of 0.1 to 2.0 cubic centimeters per gram and an internal surface area of 10 to 350 square meters per gram.
Claim 3
Dependent Claim
40 words
The method of producing vinyl acetate as defined by claim 1, wherein the reaction is carried out at a temperature of from about 50° to 250° C. and a pressure in the range of from about atmospheric to 200 atmospheres.
Claim 4
Dependent Claim
40 words
The method of producing vinyl acetate as defined by claim 2, wherein said reaction is carried out at a temperature of from about 100° to 200° C. and a pressure in the range of from about atmospheric to 10 atmospheres.
Claim 5
Dependent Claim
39 words
The method of producing vinyl acetate as defined by claim 1, wherein the amount of gold metal supported is in the range of 5 to 60 percent by weight, based upon the combined weight of palladium and gold metal.
Claim 6
Dependent Claim
70 words
The method of producing vinyl acetate as defined by claim 1, wherein said porous carrier is a carrier wherein, with the maximum peak on its pore radius distribution curve being taken as R, the sum of pore volumes within the pore radius range of 0.5 to 1.5 R is not less than 60 percent of the total pore volume within the pore radius range of 4 to 750 angstrom units.
References Cited (Backward Citations)
US3743607A
Cited
US3761513A
Cited
US3830834A
Cited
US3631079A
Cited
GB1177515A
Cited
US3670014A
Cited
US3939199A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-01 | 1981-10-31 | 1982-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-01 | 1985-10-31 | 1986-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-01 | 1989-10-31 | 1990-05-02 | $7700.00 | Window Closed / Lapsed |