Assignee: Corning Glass Works
•
Filing: 1977-03-16
•
Granted: 1978-05-30
•
Expires: 1997-03-16
Abstract
Abstract An improvement upon the making of colored photosensitive glasses via the exposure thereof to high energy or actinic radiation followed by heat treatment thereof, the improvement comprising conducting the exposure of the glasses while such are at a temperature between about 200° - 410° C. to thereby considerably shorten the time required for developing color and to produce colors of very high intensity.
Inventors
- 👤 Joseph Ference
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:47
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/076; C03C3/11; C03C23/00; C03C23/0005; C03C23/002; C03C23/003; C03C23/004; C03C4/00; C03C4/04
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
276 words
A method for making a glass article wherein at least a portion thereof is integrally colored by silver which consists of the steps: (a) melting a batch for a glass containing the constituents of alkali fluoride and the constituents of at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (b) forming said melt into a glass article; (c) exposing at least a portion of said article at ambient temperature to high energy or actinic radiation; (d) heating at least said exposed portion of said article to a temperature between about the transformation range of the glass and the softening point thereof for a sufficient length of time to cause nucleation and growth of microcrystals of alkali fluoride containing at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (e) re-exposing at least said portion of said glass article to high energy or actinic radiation while at least said portion is at a temperature below the transformation range of the glass that is at a temperature between about 200° -410° C. for a sufficient length of time to cause metallic silver to be deposited as discrete colloidal particles less than 200A in the smallest dimension, and/or deposited within said microcrystals, the silver-containing part of the microcrystal being less than about 200A in the smallest dimension, and/or deposited on the surface of said microcrystals, the portion of the microcrystal coated with silver being less than about 200A in the smallest dimension, said microcrystals having a concentration of at least 0.005% by volume; and then (f) cooling said article to ambient temperature.
Claim 2
Independent Claim
276 words
A method for making a glass article wherein at least a portion thereof is integrally colored by silver which consists of the steps: (a) melting a batch for a glass containing the constituents of alkali fluoride and the constituents of at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (b) forming said melt into a glass article; (c) exposing at least a portion of said article at ambient temperature to high energy or actinic radiation; (d) heating at least said exposed portion of said article to a temperature between about the transformation range of the glass and the softening point thereof for a sufficient length of time to cause nucleation and growth of microcrystals of alkali fluoride containing at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (e) re-exposing at least said portion of said glass article to high energy or actinic radiation while at least said portion is at a temperature below the transformation range of the glass that is at a temperature between about 200° -410° C. for a sufficient length of time to cause metallic silver to be deposited as discrete colloidal particles less than 200A in the smallest dimension, and/or deposited within said microcrystals, the silver-containing part of the microcrystal being less than about 200A in the smallest dimension, and/or deposited on the surface of said microcrystals, the portion of the microcrystal coated with silver being less than about 200A in the smallest dimension, said microcrystals having a concentration of at least 0.005% by volume; and then (f) cooling said article to ambient temperature.
Claim 3
Dependent Claim
15 words
A method according to claim 1 wherein said re-exposing is conducted at about 275°-325° C.
Claim 4
Dependent Claim
75 words
A method of according to claim 1 wherein said glass consists essentially, in weight percent on the oxide basis as calculated from the batch, of about 10-20% Na 2 O, 0.0005-0.3% Ag, 1-4% F, an amount of at least one halide selected from the group consisting of Cl, Br, and I at least sufficient to react stoichiometrically with the Ag, but not more than a total of about 3%, and the remainder SiO 2 .
Claim 5
Dependent Claim
16 words
A method according to claim 3 wherein said glass also contains about 0.01-0.2% CeO 2 .
Claim 6
Dependent Claim
24 words
A method according to claim 3 wherein said glass also contains up to 18% ZnO and/or up to 10% Al 2 O 3 .
Claim 7
Dependent Claim
42 words
A method according to claim 1 wherein said integrally colored portion of said glass article exhibits transparency and the concentration of said microcrystals does not exceed about 0.1% by volume and the size thereof does not exceed about 0.1 micron in diameter.
Claim 8
Dependent Claim
17 words
A method according to claim 1 wherein said integrally colored portion of said glass article is polychromatic.
Claim 9
Independent Claim
313 words
A method for making a glass article wherein at least a portion thereof is integrally colored by silver which consists of the steps: (a) melting a batch for a glass containing the constituents of alkali fluoride and the constituents of at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (b) forming said melt into a glass article; (c) exposing at least a portion of said article to high energy or actinic radiation while at least said portion is at a temperature below the transformation range of the glass that is at a temperature between about 200°-410° C. for a sufficient length of time to develop a latent image therein. (d) removing the high energy or actinic radiation and subjecting at least said portion of said article to a temperature between the transformation range and the softening point of the glass for a period of time sufficient to cause nucleation and growth of microcrystals of alkali fluoride containing at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (e) re-exposing at least said portion of said article to high energy or actinic radiation while at least said portion is at a temperature below the transformation range of the glass that is at a temperature between about 200°-410° C. for a sufficient length of time to cause metallic silver to be deposited as discrete colloidal particles less than 200A in the smallest dimension, and/or deposited within said microcrystals, the silver-containing part of the microcrystal being less than about 200A in the smallest dimension, and/or depositied on the surface of said microcrystal, the portion of the microcrystal coated with silver being less than about 200A in the smallest dimension, said microcrystals having a concentration of at least 0.005% by volume; and then (f) cooling said article to ambient temperature.
Claim 10
Independent Claim
313 words
A method for making a glass article wherein at least a portion thereof is integrally colored by silver which consists of the steps: (a) melting a batch for a glass containing the constituents of alkali fluoride and the constituents of at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (b) forming said melt into a glass article; (c) exposing at least a portion of said article to high energy or actinic radiation while at least said portion is at a temperature below the transformation range of the glass that is at a temperature between about 200°-410° C. for a sufficient length of time to develop a latent image therein. (d) removing the high energy or actinic radiation and subjecting at least said portion of said article to a temperature between the transformation range and the softening point of the glass for a period of time sufficient to cause nucleation and growth of microcrystals of alkali fluoride containing at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide; (e) re-exposing at least said portion of said article to high energy or actinic radiation while at least said portion is at a temperature below the transformation range of the glass that is at a temperature between about 200°-410° C. for a sufficient length of time to cause metallic silver to be deposited as discrete colloidal particles less than 200A in the smallest dimension, and/or deposited within said microcrystals, the silver-containing part of the microcrystal being less than about 200A in the smallest dimension, and/or depositied on the surface of said microcrystal, the portion of the microcrystal coated with silver being less than about 200A in the smallest dimension, said microcrystals having a concentration of at least 0.005% by volume; and then (f) cooling said article to ambient temperature.
Claim 11
Dependent Claim
17 words
A method according to claim 8 wherein said exposing and re-exposing are conducted at about 275°-325° C.
Claim 12
Dependent Claim
74 words
A method according to claim 8 wherein said glass consists essentially, in weight percent on the oxide basis as calculated from the batch, of about 10-20% Na 2 O, 0.0005-0.3% Ag, 1-4% F, an amount of at least one halide selected from the group consisting of Cl, Br, and I at least sufficient to react stoichiometrically with the Ag, but not more than a total of about 3%, and the remainder SiO 2 .
Claim 13
Dependent Claim
16 words
A method according to claim 10 wherein said glass also contains about 0.01-0.2% CeO 2 .
Claim 14
Dependent Claim
24 words
A method according to claim 10 wherein said glass also contains up to 18% ZnO and/or up to 10% Al 2 O 3 .
Claim 15
Dependent Claim
42 words
A method according to claim 8 wherein said integrally colored portion of said glass article exhibits transparency and the concentration of said microcrystals does not exceed about 0.1% by volume and the size thereof does not exceed about 0.1 micron in diameter.
Claim 16
Dependent Claim
17 words
A method according to claim 8 wherein said integrally colored portion of said glass article is polychromatic.
References Cited (Backward Citations)
US3876436A
Cited
US3833511A
Cited
US3892582A
Cited
US3920463A
Cited
US4017318A
Cited
US4057408A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |