Assignee: Czech Academy of Sciences
•
Filing: 1975-08-18
•
Granted: 1978-06-20
•
Expires: 1995-08-18
Abstract
Abstract The invention relates to a new type of soft contact lens from a hydrophilic, swelled copolymer, with high swelling capacity, high permeability for oxygen, comparatively high strength and low modulus of elasticity, said characteristics making the lens suitable for permanent wearing. The lens contains, at swelling equilibrium with water at 20° C, from about 50 to about 95% by weight of water, preferably from about 70 to about 90%, and consists of a multiblock copolymer of acrylonitrile with acrylamide, containing, if desired, a minor amount of other monomer units, not exceeding 20 molar percent. The swelled hydrogel contains two distinct but inseparable phases, one of them being polyacrylonitrile detectable by X-ray analysis, the other being amorphous highly solvated hydrophilic polymer containing predominantly acrylamide units.
Inventors
- 👤 Vladimir Stoy
- 👤 Otto Wichterle
- 👤 Artur Stoy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:14
CPC Classifications
G; G02; G02C; G02C7/00; G02C7/02; G02C7/04; G02B; G02B1/00; G02B1/04; G02B1/041; G02B1/043
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
158 words
A soft contact lens suitable for substantially permanent wear and having a concavo-convex cross-sectional shape with its concave surface adapted to fit the human eye, which lens is formed from a water-swelled hydrogel (a) containing about 50 to about 90% by weight of water at swelling equilibrium with water at 20° C. and (b) consisting of a macromolecular block copolymer comprising (i) multiple segments of acrylonitrile units and (ii) multiple segments of acrylamide units and (iii) 0 to 20 molar % of other monomeric units, said macromolecular block copolymer being obtained from the partial acid hydrolysis of polyacrylonitrile and comprising in its water-swelled condition two distinct but inseparable phases, one of said phases being composed essentially of non-swelled crystalline or quasi-crystalline polyacrylonitrile segments non-covalently cross-linked by strong dipoles between nitrile groups and detectable by X-ray analysis showing the usual polyacrylonitrile pattern, the other of said phases being amorphous and being predominantly composed of highly swelled hydrophilic polyacrylamide segments.
Claim 2
Dependent Claim
158 words
A soft contact lens suitable for substantially permanent wear and having a concavo-convex cross-sectional shape with its concave surface adapted to fit the human eye, which lens is formed from a water-swelled hydrogel (a) containing about 50 to about 90% by weight of water at swelling equilibrium with water at 20° C. and (b) consisting of a macromolecular block copolymer comprising (i) multiple segments of acrylonitrile units and (ii) multiple segments of acrylamide units and (iii) 0 to 20 molar % of other monomeric units, said macromolecular block copolymer being obtained from the partial acid hydrolysis of polyacrylonitrile and comprising in its water-swelled condition two distinct but inseparable phases, one of said phases being composed essentially of non-swelled crystalline or quasi-crystalline polyacrylonitrile segments non-covalently cross-linked by strong dipoles between nitrile groups and detectable by X-ray analysis showing the usual polyacrylonitrile pattern, the other of said phases being amorphous and being predominantly composed of highly swelled hydrophilic polyacrylamide segments.
Claim 3
Dependent Claim
33 words
A soft contact lens as set forth in claim 1, in which the water-swelled hydrogel contains about 70 to about 90% by weight of water at swelling equilibrium with water at 20° C.
Claim 4
Dependent Claim
26 words
A soft contact lens as set forth in claim 1, in which the surface has been made slippery by neutralizing anionic groups with alkali metal cations.
Claim 5
Dependent Claim
27 words
A soft contact lens as set forth in claim 1, in which the modulus of elasticity is lower than that of the cornea of the human eye.
Claim 6
Dependent Claim
179 words
The process of forming a soft contact lens suitable for substantially permanent wear and having a concavo-convex cross-sectional shape with its concave surface adapted to fit the human eye, which comprises molding a water-swelled hydrogel at 90° - 170° C into said lens shape and thereafter cooling in the mold under pressure, said hydrogel (a) containing about 50 to about 90% by weight of water at swelling equilibrium with water at 20° C. and (b) consisting of a macromolecular block copolymer comprising (i) multiple segments of acrylonitrile units and (ii) multiple segments of acrylamide units and (iii) 0 to 20 molar % of other monomeric units, said macromolecular block copolymer being obtained from the partial acid hydrolysis of polyacrylonitrile and comprising, in its water-swelled condition, two distinct but inseparable phases, one of said phases being composed essentially of non-swelled crystalline or quasi-crystalline polyacrylonitrile segments non-convalently crosslinked by strong dipoles between nitrile groups and detectable by X-ray analysis showing the usual polyacrylonitrile pattern, the other of said phases being amorphous and being predominantly composed of highly swelled hydrophilic polyacrylamid segments.
Claim 7
Dependent Claim
179 words
The process of forming a soft contact lens suitable for substantially permanent wear and having a concavo-convex cross-sectional shape with its concave surface adapted to fit the human eye, which comprises molding a water-swelled hydrogel at 90° - 170° C into said lens shape and thereafter cooling in the mold under pressure, said hydrogel (a) containing about 50 to about 90% by weight of water at swelling equilibrium with water at 20° C. and (b) consisting of a macromolecular block copolymer comprising (i) multiple segments of acrylonitrile units and (ii) multiple segments of acrylamide units and (iii) 0 to 20 molar % of other monomeric units, said macromolecular block copolymer being obtained from the partial acid hydrolysis of polyacrylonitrile and comprising, in its water-swelled condition, two distinct but inseparable phases, one of said phases being composed essentially of non-swelled crystalline or quasi-crystalline polyacrylonitrile segments non-convalently crosslinked by strong dipoles between nitrile groups and detectable by X-ray analysis showing the usual polyacrylonitrile pattern, the other of said phases being amorphous and being predominantly composed of highly swelled hydrophilic polyacrylamid segments.
References Cited (Backward Citations)
DE2114669A1
Cited
US3767759A
Cited
US3812071A
Cited
US3931123A
Cited
US3948870A
Cited
US3929741A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |