Assignee: Bayer AG
•
Filing: 1975-01-28
•
Granted: 1978-06-20
•
Expires: 1995-01-28
Abstract
Abstract A process for the low solvent or solvent free coating of heat resistant substrates by using a coating substance which has a melting point or range below about 200° C and which is heat crosslinkable. The substrate is coated at temperatures between about 20° and 250° C and the coating is subsequently heated to more elevated temperatures to effect crosslinking. The coating substance contains active hydrogen, preferably hydroxyl bearing compounds and blocked polyisocyanates which become reactive when the coating substance is heated to effect cross-linking. In a preferred embodiment, the blocked polyisocyanates consist of at least 40 equivalent percent alkanol or cycloalkanol blocked polyisocyanates. Also a coating substance containing at least 50 wt.% of a combination of active hydrogen, preferably hydroxyl bearing compounds and blocked isocyanates. The combination has a melting point of less than 200° C and a blocked isocyanate group to active hydrogen ratio of about 1:2 to 1:9. At least 40 equivalent percent of the blocked polyisocyanates are alkanol or cycloalkanol blocked and the remainder are blocked such that they are reactive at temperatures at least 30° C lower than the alkanol or cycloalkanol blocked polyisocyanates. The coating substance has a viscosity of less than about 40,000 cP at or below about 250° C.
Inventors
- 👤 Willi Dunwald
- 👤 Jurgen Lewalter
- 👤 Wilfried Zecher
- 👤 Wolf-Dieter Last
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:20
CPC Classifications
C; C09; C09D; C09D175/00; C09D175/04; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/80; C08G18/8061; C08G18/8096; C08G2150/00; C08G2150/20; Y; Y10; Y10T; Y10T428/00; Y10T428/12
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
166 words
Process of coating a heat resistant substrate comprising applying a solvent-free melt coating composition comprising blocked polyisocyanates and compounds which contain hydroxyl groups which are reactive with isocyanate groups, followed by cross-linking of the resulting coating by heating wherein a. at least 40 equivalent percent of the blocked polyisocyanates consist of alkanol or cycloalkanol blocked polyisocyanates, b. the blocked polyisocyanates and compounds which contain hydroxyl groups reactive with isocyanate groups form a composition with a melting point or range below 200° C and the proportion of reactants is so chosen that the equivalent ratio of blocked isocyanate groups to hydroxyl groups is between 1:2 and 9:1, c. coating of the substrate is carried out at a temperature within the range of 20° to 250° C at which temperature the coating composition has a substantially constant viscosity of not more than 40,000 cP, and d. the coated substrate is subsequently heated to a temperature at which the blocking agent is split off and final cross-linking takes place.
Claim 2
Dependent Claim
166 words
Process of coating a heat resistant substrate comprising applying a solvent-free melt coating composition comprising blocked polyisocyanates and compounds which contain hydroxyl groups which are reactive with isocyanate groups, followed by cross-linking of the resulting coating by heating wherein a. at least 40 equivalent percent of the blocked polyisocyanates consist of alkanol or cycloalkanol blocked polyisocyanates, b. the blocked polyisocyanates and compounds which contain hydroxyl groups reactive with isocyanate groups form a composition with a melting point or range below 200° C and the proportion of reactants is so chosen that the equivalent ratio of blocked isocyanate groups to hydroxyl groups is between 1:2 and 9:1, c. coating of the substrate is carried out at a temperature within the range of 20° to 250° C at which temperature the coating composition has a substantially constant viscosity of not more than 40,000 cP, and d. the coated substrate is subsequently heated to a temperature at which the blocking agent is split off and final cross-linking takes place.
Claim 3
Dependent Claim
30 words
Process according to claim 1, wherein a. the substrate to be coated is a metal wire and b. coating is carried out by dipping, roller application or suction felt coating.
Claim 4
Dependent Claim
25 words
Process according to claim 1 wherein the compound which contains hydroxyl groups reactive with isocyanate groups is a compound containing at least two hydroxyl groups.
Claim 5
Dependent Claim
26 words
The process according to claim 3, wherein the compound having at least two hydroxyl groups has a molecular weight of about 62 to about 10 000.
Claim 6
Dependent Claim
51 words
Process according to claim 1 wherein the blocked polyisocyanates consist of 40 to 99 equivalent percent of alkanol- or cycloalkanol- blocked polyisocyanates and 1 to 60 equivalent percent of blocked polyisocyanates which have a deblocking temperature at least 30° C below the deblocking temperature of the alkanol- or cycloalkanol- blocked polyisocyanates.
Claim 7
Dependent Claim
33 words
Process according to claim 5 wherein the blocked polyisocyanates which have a deblocking temperature at least 30° C below the deblocking temperature of the alkanol- or cycloalkanol- blocked polyisocyanates are phenol- blocked polyisocyanates.
Claim 8
Dependent Claim
70 words
Process according to claim 5 wherein before the substrate is coated, the coating composition is briefly heated to a temperature which lies above the deblocking temperature of the blocked polyisocyanates which have a deblocking temperature at least 30° C below the blocking temperature of the alkanol- or cycloalkanol- blocked polyisocyanates and below the deblocking temperature of the alkanol- or cycloalkanol- blocked polyisocyanates to produced oligomer formation in the coating composition.
Claim 9
Dependent Claim
153 words
Process of coating a heat resistant substrate comprising a. providing a melt of a solvent-free coating substance comprising i) at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, said blocked polyisocyanates characterized in that at least 40 equivalent percent of the blocked polyisocyanates consist of alkanol or cycloalkanol blocked polyisocyanates, and ii) up to 50% by weight of polymeric substances not substantially reactive with said hydroxyl groups, b. coating a heat resistant substrate with the coating substance at a temperature of about 20° to 250° C and at a substantially constant viscosity of not more than about 40,000 cP, and c. heating the coated substrate to a temperature sufficiently high to cause the polyisocyanate blocking agent to split off.
Claim 10
Dependent Claim
153 words
Process of coating a heat resistant substrate comprising a. providing a melt of a solvent-free coating substance comprising i) at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, said blocked polyisocyanates characterized in that at least 40 equivalent percent of the blocked polyisocyanates consist of alkanol or cycloalkanol blocked polyisocyanates, and ii) up to 50% by weight of polymeric substances not substantially reactive with said hydroxyl groups, b. coating a heat resistant substrate with the coating substance at a temperature of about 20° to 250° C and at a substantially constant viscosity of not more than about 40,000 cP, and c. heating the coated substrate to a temperature sufficiently high to cause the polyisocyanate blocking agent to split off.
Claim 11
Dependent Claim
181 words
A process of coating a heat resistant substrate comprising a. providing a melt of a coating substance comprising i) at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, about 40 to 99 equivalent percent of said blocked polyisocyanates being alkanol or cycloalkanol blocked and about 60 to 1 equivalent percent of said blocked polyisocyanates having a deblocking temperature at least about 30° C below the deblocking temperature of the alkanol or cycloalkanol blocked polyisocyanates, ii) up to 50% by weight of polymeric substances not substantially reactive with said hydroxyl groups, b. coating a heat resistant substrate with said coating substance which is at about 20° to 250° C and has a substantially constant viscosity of not more than about 40,000 cP, and c. heating the coated substrate to a temperature sufficiently high to cause the isocyanate blocking agent to split off, whereby a cross-linked coating is formed.
Claim 12
Dependent Claim
181 words
A process of coating a heat resistant substrate comprising a. providing a melt of a coating substance comprising i) at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, about 40 to 99 equivalent percent of said blocked polyisocyanates being alkanol or cycloalkanol blocked and about 60 to 1 equivalent percent of said blocked polyisocyanates having a deblocking temperature at least about 30° C below the deblocking temperature of the alkanol or cycloalkanol blocked polyisocyanates, ii) up to 50% by weight of polymeric substances not substantially reactive with said hydroxyl groups, b. coating a heat resistant substrate with said coating substance which is at about 20° to 250° C and has a substantially constant viscosity of not more than about 40,000 cP, and c. heating the coated substrate to a temperature sufficiently high to cause the isocyanate blocking agent to split off, whereby a cross-linked coating is formed.
Claim 13
Dependent Claim
95 words
The process of claim 9 wherein a. prior to coating the heat resistant substrate, the coating substance is briefly heated to a temperature which lies above the deblocking temperature of the blocked polyisocyanates which have a deblocking temperature at least 30° C below the deblocking temperature of the alkanol- or cycloalkanol-blocked polyisocyanates and below the deblocking temperature of the alkanol- or cycloalkanol-blocked polyisocyanates to produce oligomer formation in the coating substance, and b. the coating substance has a substantially constant viscosity of not more than 5000 cP at a temperature between 20° and 250° C.
Claim 14
Dependent Claim
121 words
A coating composition which can be cross-linked by heat and has a melting point or range below 200° C comprising blocked polyisocyanates and polyhydroxyl compounds, wherein at least 40 equivalent percent of the blocked polyisocyanates consist of alkanol- or cycloalkanol-blocked polyisocyanates, said composition having a substantially constant viscosity of not more than 40,000 cP at a temperature between about 20° C and 250° C, and the polyisocyanates being selected from the group consisting of 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, mixtures of 2,4- and 2,6-diisocyanatotoluene, 4,4'-diisocyanatodiphenylmethane, 4,4'-diisocyanatodiphenyl - dimethylmethane, 1,5-diisocyanatonaphthalene, mixtures of homologues or isomers obtained by phosgenation of aniline/formaldehyde condensates, the triisocyanate containing urethane groups obtained by reacting 3 mols of 2,4-diisocyanatotoluene with 1 mol of trimethylolpropane and the isocyanato-isocyanurate obtained by trimerizing 2,4-diisocyanatotoluene.
Claim 15
Dependent Claim
121 words
A coating composition which can be cross-linked by heat and has a melting point or range below 200° C comprising blocked polyisocyanates and polyhydroxyl compounds, wherein at least 40 equivalent percent of the blocked polyisocyanates consist of alkanol- or cycloalkanol-blocked polyisocyanates, said composition having a substantially constant viscosity of not more than 40,000 cP at a temperature between about 20° C and 250° C, and the polyisocyanates being selected from the group consisting of 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, mixtures of 2,4- and 2,6-diisocyanatotoluene, 4,4'-diisocyanatodiphenylmethane, 4,4'-diisocyanatodiphenyl - dimethylmethane, 1,5-diisocyanatonaphthalene, mixtures of homologues or isomers obtained by phosgenation of aniline/formaldehyde condensates, the triisocyanate containing urethane groups obtained by reacting 3 mols of 2,4-diisocyanatotoluene with 1 mol of trimethylolpropane and the isocyanato-isocyanurate obtained by trimerizing 2,4-diisocyanatotoluene.
Claim 16
Dependent Claim
117 words
A coating composition which can be cross-linked by heating comprising i. at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, about 40 to 99 equivalent percent of said blocked polyisocyanates being alkanol or cycloalkanol blocked and about 60 to 1 equivalent percent of said blocked polyisocyanates having a deblocking temperature at least about 30° C below the deblocking temperature of the alkanol or cycloalkanol blocked polyisocyanate, and ii. up to 50% by weight of polymeric substances not substantially reactive with said hydroxyl groups.
Claim 17
Dependent Claim
117 words
A coating composition which can be cross-linked by heating comprising i. at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, about 40 to 99 equivalent percent of said blocked polyisocyanates being alkanol or cycloalkanol blocked and about 60 to 1 equivalent percent of said blocked polyisocyanates having a deblocking temperature at least about 30° C below the deblocking temperature of the alkanol or cycloalkanol blocked polyisocyanate, and ii. up to 50% by weight of polymeric substances not substantially reactive with said hydroxyl groups.
Claim 18
Dependent Claim
148 words
A coating composition which can be cross-linked by heating to a sufficient temperature comprising i. at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, about 40 to 99 equivalent percent of said blocked polyisocyanates being alkanol or cycloalkanol blocked and about 60 to 1 equivalent percent of said blocked polyisocyanates having a deblocking temperature at least about 30° C below the deblocking temperature of the alkanol or cycloalkanol blocked polyisocyanates, and ii. up to 50% by weight of polymeric substances not substantially reactive with hydroxyl groups in which constituents (i) and (ii) together having a substantially constant viscosity of not more than 40,000 cP at a temperature between about 20° C and 250° C.
Claim 19
Dependent Claim
148 words
A coating composition which can be cross-linked by heating to a sufficient temperature comprising i. at least 50% by weight of a combination of blocked polyisocyanates and polyhydroxyl compounds having a melting point or melting range below about 200° C and having an equivalent ratio of blocked isocyanate groups to hydroxyl groups of about 1:2 to about 9:1, about 40 to 99 equivalent percent of said blocked polyisocyanates being alkanol or cycloalkanol blocked and about 60 to 1 equivalent percent of said blocked polyisocyanates having a deblocking temperature at least about 30° C below the deblocking temperature of the alkanol or cycloalkanol blocked polyisocyanates, and ii. up to 50% by weight of polymeric substances not substantially reactive with hydroxyl groups in which constituents (i) and (ii) together having a substantially constant viscosity of not more than 40,000 cP at a temperature between about 20° C and 250° C.
Claim 20
Dependent Claim
21 words
The coating composition of claim 12 wherein up to 25% by weight of solvent, based on the total mixture, is present.
Claim 21
Dependent Claim
21 words
The coating composition of claim 13 wherein up to 25% by weight of solvent, based on the total mixture, is present.
Claim 22
Dependent Claim
22 words
The coating composition of claim 12 wherein up to 100% by weight of solvent, based on the weight of solids, is present.
Claim 23
Dependent Claim
22 words
The coating composition of claim 13 wherein up to 100% by weight of solvent, based on the weight of solids, is present.
References Cited (Backward Citations)
CA679761A
Cited
DE1181844B
Cited
US3321548A
Cited
US3621000A
Cited
US3849160A
Cited
US3822240A
Cited
US3830785A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |