US4100330A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for coating glass with silicon and a metal oxide and resulting product
Assignee: PPG Industries Inc
•
Filing: 1977-03-28
•
Granted: 1978-07-11
•
Expires: 1997-03-28
Abstract
Abstract Glass is heated to a temperature of at least about 400° C. and contacted sequentially with a silane-containing gas and an organometallic composition which thermally decompose to form, respectively, a coating layer of silicon and a coating layer of metal oxide on the glass surface. The resultant coated glass article is more durable than a silicon coated glass article and has better solar energy control properties than a metal oxide coated glass article.
Inventors
- 👤 Harold E. Donley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:48
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3429; C03C17/3482; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31609; Y10T428/31612
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
113 words
A method for producing a coated glass article comprising the steps of: a. maintaining a glass substrate at a temperature of at least about 400° C. in a non-oxidizing atmosphere; b. contacting a surface of the glass substrate with a silane-containing gas for a sufficient time to form a silicon coating on the glass surface; c. maintaining the silicon coated glass at a temperature of at least about 250° C. in an oxidizing atmosphere; and d. contacting the silicon coated surface with a coating composition comprising a metal compound which, upon contact with the hot glass surface, thermally decomposes to form a metal oxide coating over the silicon coating on the glass surface.
Claim 2
Independent Claim
113 words
A method for producing a coated glass article comprising the steps of: a. maintaining a glass substrate at a temperature of at least about 400° C. in a non-oxidizing atmosphere; b. contacting a surface of the glass substrate with a silane-containing gas for a sufficient time to form a silicon coating on the glass surface; c. maintaining the silicon coated glass at a temperature of at least about 250° C. in an oxidizing atmosphere; and d. contacting the silicon coated surface with a coating composition comprising a metal compound which, upon contact with the hot glass surface, thermally decomposes to form a metal oxide coating over the silicon coating on the glass surface.
Claim 3
Dependent Claim
20 words
The method according to claim 1, wherein the silane-containing gas is a mixture comprising monosilane and an inert carrier gas.
Claim 4
Dependent Claim
41 words
The method according to claim 2, wherein the silane-containing gas is a mixture comprising from about 0.1 to 20 percent by volume silane, up to about 10 percent by volume hydrogen and from about 70 to 99.9 percent by volume nitrogen.
Claim 5
Dependent Claim
42 words
The method according to claim 1, wherein the silicon coated surface is contacted with a coating composition comprising an organometallic compound of a metal selected from the group consisting of cobalt, iron, chromium, copper, manganese, nickel, tin, vanadium, titanium and mixtures thereof.
Claim 6
Dependent Claim
31 words
The method according to claim 4, wherein the organometallic compound is the acetylacetonate of a metal selected from the group consisting of cobalt, iron, chromium, copper, manganese, nickel and mixtures thereof.
Claim 7
Dependent Claim
28 words
The method according to claim 5, wherein the organometallic compound is dissolved in a solvent selected from the group consisting of aliphatic and olefinic halocarbons and halogenated hydrocarbons.
Claim 8
Dependent Claim
210 words
The method for producing a coated glass article according to claim 1, wherein a. a glass substrate is maintained at a temperature from about 500° to about 700° C. in an atmosphere comprising about 90 to 95 percent nitrogen and about 5 to 10 percent by volume hydrogen; b. a surface of the glass substrate is contacted with a gaseous mixture of about 0.1 to 20 percent by volume monosilane, up to about 10 percent by volume hydrogen and about 70 to 99.9 percent by volume nitrogen for a sufficient time to form a silicon coating about 250 Angstroms to about 600 Angstroms in thickness on the glass surface; c. the silicon coated glass is maintained at a temperature from about 400° to about 600° C. in air; and d. the silicon coated surface is contacted with a coating composition comprising a solvent and about 0.1 to 10 percent by weight of metal of an organometallic compound of a metal selected from the group consisting of cobalt, iron, chromium, copper, manganese, nickel, tin, vanadium, titanium and mixtures thereof which compound thermally decomposes, upon contact with the hot glass surface, to form a metal oxide coating from about 300 Angstroms to about 600 Angstroms in thickness upon the silicon coated surface.
Claim 9
Dependent Claim
11 words
A coated article prepared according to the method of claim 1.
Claim 10
Dependent Claim
11 words
A coated article prepared according to the method of claim 7.
References Cited (Backward Citations)
GB830179A
Cited
US3410710A
Cited
US3185586A
Cited
US3660061A
Cited
US3658568A
Cited
US3652246A
Cited
DE2115516A1
Cited
US3978272A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-10 | 1982-01-09 | 1982-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-10 | 1986-01-09 | 1986-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-10 | 1990-01-09 | 1990-07-11 | $7700.00 | Window Closed / Lapsed |