Polyurethane latexes from sulfonate prepolymer, aqueous chain extension process, and coated support
Assignee: Rhone Progil SA
•
Filing: 1974-10-11
•
Granted: 1978-08-29
•
Expires: 1994-10-11
Abstract
Abstract Process of preparing anionic polyurethane latexes without the addition of a foreign emulsifying surface active agent comprising rendering the basic polyester or polyether constituent of the latex intrinsically emulsifiable or dispersible in water by incorporating an anionic functional group in the chain thereof and reacting this basic constituent with a diisocyanate in order to obtain a prepolymer which is then emulsified in water.
Inventors
- 👤 Robert Violland
- 👤 Jean Neel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:48
CPC Classifications
C; C14; C14C; C14C9/00; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0804; C08G18/0819; C08G18/0828; C14C11/00; C14C11/003; C14C11/006; Y; Y10; Y10T; Y10T442/00; Y10T442/20; Y10T442/2861
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
219 words
A process for preparing an auto-emulsified, highly disperse, film-forming and storage stable anionic polyurethane latex comprising charging an auto-emulsified and water propagable isocyanato chain terminated, anionic polyurethane prepolymer into an aqueous medium, and thence agitating the resulting dispersion to auto-emulsify and chain propagate said prepolymer, said prepolymer having a molecular weight between about 2000 and 10,000 and being formed from the reaction of at least: (a) a member selected from the group consisting of an anionic sulfonated polyester, an anionic sulfonated polyether and admixtures thereof, having a molecular weight between about 1000 and 4000 and a sulfur content between about 0.5 and 3% by weight, wherein said polyester is prepared by condensing at least: (i) a dicarboxylic acid or its lower alkyl diester (ii) a polyol (iii) and a sulfonated diacid, its sulfonated diester or the alkali metal salt thereof, said diacid being selected from the group consisting of isosulfophthalic and sulfosuccinic acid, and wherein said polyether is prepared from a bifunctional molecule selected from the group consisting of a sulfonated diacid, its sulfonated diester or the alkali metal salt thereof, said diacid being selected from the group consisting of isosulfophthalic and sulfosuccinic acid; (b) with an amount of at least one diisocyanate sufficient to produce a prepolymer having only terminal isocyanate groups; (c) and, a chain extending agent.
Claim 2
Dependent Claim
219 words
A process for preparing an auto-emulsified, highly disperse, film-forming and storage stable anionic polyurethane latex comprising charging an auto-emulsified and water propagable isocyanato chain terminated, anionic polyurethane prepolymer into an aqueous medium, and thence agitating the resulting dispersion to auto-emulsify and chain propagate said prepolymer, said prepolymer having a molecular weight between about 2000 and 10,000 and being formed from the reaction of at least: (a) a member selected from the group consisting of an anionic sulfonated polyester, an anionic sulfonated polyether and admixtures thereof, having a molecular weight between about 1000 and 4000 and a sulfur content between about 0.5 and 3% by weight, wherein said polyester is prepared by condensing at least: (i) a dicarboxylic acid or its lower alkyl diester (ii) a polyol (iii) and a sulfonated diacid, its sulfonated diester or the alkali metal salt thereof, said diacid being selected from the group consisting of isosulfophthalic and sulfosuccinic acid, and wherein said polyether is prepared from a bifunctional molecule selected from the group consisting of a sulfonated diacid, its sulfonated diester or the alkali metal salt thereof, said diacid being selected from the group consisting of isosulfophthalic and sulfosuccinic acid; (b) with an amount of at least one diisocyanate sufficient to produce a prepolymer having only terminal isocyanate groups; (c) and, a chain extending agent.
Claim 3
Dependent Claim
54 words
The process as defined in claim 1, wherein said dicarboxylic acid is selected from the group consisting of adipic, maleic, fumaric, phthalic, isophthalic, terephthalic, succinic, sebacic and suberic and said polyol is selected from the group consisting of ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butanediol, hexanediol, neopentyl glycol, cyclohexanediol, and dicyclohexanediol propane.
Claim 4
Dependent Claim
25 words
The process as defined in claim 1, wherein said sulfonated, anionic polyether is obtained from the reaction of an alkylene oxide and said bifunctional molecule.
Claim 5
Dependent Claim
29 words
The process as defined in claim 1, wherein said sulfonated, anionic polyether is obtained from the reaction of an alkylene oxide with a polyhydric alcohol and said bifunctional molecule.
Claim 6
Dependent Claim
47 words
The process as defined in claim 4 wherein said alkylene oxide is selected from the group consisting of ethylene oxide, propylene oxide and butylene oxide and said polyhydric alcohol is selected from the group consisting of ethylene glycol, diethylene glycol, glycerine, pentaerythritol, sorbitol, hexanetriol and trimethylol propane.
Claim 7
Dependent Claim
47 words
The process as defined in claim 1, wherein the chain extending agent is a diol selected from the group consisting of ethylene glycol, diethylene glycol, neopentyl glycol, hexanediol, and butanediol, which is employed prior to contacting with water to regulate the urethane group content of said prepolymer.
Claim 8
Dependent Claim
45 words
The process as defined in claim 1, wherein the chain extending agent is an amine selected from the group consisting of ethanolamine, aminoethyl-ethanolamine, ethylenediamine, propylenediamine and hexamethylene diamine, which is employed prior to contacting with water to regulate the urea group content of said prepolymer.
Claim 9
Dependent Claim
26 words
The process as defined in claim 1 wherein a polyfunctional compound having a hydroxy or isocyanate functonality greater than two is employed to reticulate said prepolymer.
Claim 10
Dependent Claim
14 words
The anionic polyurethane aqueous latex prepared according to the process defined by claim 1.
Claim 11
Dependent Claim
27 words
The anionic polyurethane aqueous latex as defined by claim 9, wherein said anionic polyester has an acid number between about 0.14 mg KOH/g and 9 mg KOH/g.
Claim 12
Dependent Claim
23 words
The anionic polyurethane aqueous latex as defined by claim 9, wherein said prepolymer has an isocyanate content ranging between about 2.1% and 3.5%.
Claim 13
Dependent Claim
32 words
The anionic polyurethane aqueous latex as defined by claim 9, wherein said prepolymer has a urethane or urea nitrogen content ranging between about 1% and 5% based on the prepolymer molecular weight.
Claim 14
Dependent Claim
16 words
A flexible support having the anionic polyurethane aqueous latex as defined by claim 9 applied thereto.
Claim 15
Dependent Claim
50 words
The flexible support as defined by claim 13, wherein said polyurethane latex is applied in film form and said film has a rupture strength of at least 290 kg/cm 2 , an elongation at rupture of at least 1280%, a modulus at 100% of at least 14.3 kg/cm 2 .
References Cited (Backward Citations)
US3479310A
Cited
GB1128568A
Cited
US3617352A
Cited
US3736216A
Cited
US3734874A
Cited
US3759873A
Cited
US3879450A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |