US4111892A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Reinforced fire retardant resin composition improved in electrical characteristics
Assignee: Mitsubishi Chemical Corp
•
Filing: 1977-05-18
•
Granted: 1978-09-05
•
Expires: 1997-05-18
Abstract
Abstract A reinforced fire retardant resin composition of improved electrical characteristics, which comprises: A base resin of polytetramethylene terephthalate alone or in admixture with at least one other polymer, a fire retardant combination of a halogen containing compound and an antimony compound, hydrated silica and a reinforcing filler, wherein said halogen containing compound is present in an amount of 3-50 parts by wt. per 100 parts by weight of said base resin, said antimony compound is present in an amount such that the weight ratio of the halogen containing compound to the antimony compound ranges from 0.25 to 6 and the content of said hydrated silica ranges from 0.5 - 10 wt. % of the total resin composition.
Inventors
- 👤 Kazumasa Kamada
- 👤 Masafumi Hongo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:18
CPC Classifications
C; C08; C08K; C08K13/00; C08K13/02; C08K3/00; C08K5/00; C08K5/02; C08K7/00; C08K7/22; C08K7/24; C08K7/28; C08L; C08L33/00; C08L67/00; C08L67/02; C08L71/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
117 words
A reinforced fire retardant resin composition of improved electrical characteristics, which comprises: a base resin of polytetramethylene terephthalate alone or in admixture with at least one other polymer, a fire retardant combination of a halogen containing compound and an antimony compound, hydrated silica and a reinforcing filler, wherein said halogen containing compound is present in an amount of 3-50 parts by weight per 100 parts by weight of said base resin, said antimony compound is present in an amount such that the weight ratio of the halogen containing compound to the antimony compound ranges from 0.25 to 6 and the content of said hydrated silica ranges from 0.5 - 10 wt. % of the total resin composition.
Claim 2
Dependent Claim
117 words
A reinforced fire retardant resin composition of improved electrical characteristics, which comprises: a base resin of polytetramethylene terephthalate alone or in admixture with at least one other polymer, a fire retardant combination of a halogen containing compound and an antimony compound, hydrated silica and a reinforcing filler, wherein said halogen containing compound is present in an amount of 3-50 parts by weight per 100 parts by weight of said base resin, said antimony compound is present in an amount such that the weight ratio of the halogen containing compound to the antimony compound ranges from 0.25 to 6 and the content of said hydrated silica ranges from 0.5 - 10 wt. % of the total resin composition.
Claim 3
Dependent Claim
23 words
The composition of claim 1, wherein the content of said reinforcing filler is 3 - 50% by weight of the total resin composition.
Claim 4
Dependent Claim
12 words
The composition of claim 1, wherein the reinforcing filler is glass fibers.
Claim 5
Dependent Claim
43 words
The composition of claim 1, wherein the reinforcing filler comprises talc and a second reinforcing filler in a weight ratio of talc/hydrated silica of 10/1 - 1/3 and wherein the content of the talc is 0.5-20% by weight of the total resin composition.
Claim 6
Dependent Claim
13 words
The composition of claim 4, wherein said second reinforcing filler is glass fibers.
Claim 7
Dependent Claim
76 words
The composition of claim 1, wherein the fire retarding halogen containing compound is at least one compound selected from the group consisting of cycloaliphatic hexabromobenzene, tetrabromobisphenol A and derivatives thereof; tetrabromophthalic anhydride; decabromodiphenylether; trisdibromophenyl phosphate; tris 2, 3 dibromopropyl phosphate; aliphatic cyclic compounds consisting of C 14 H 4 Cl 12 O; C 17 H 8 Cl 12 ; C 18 H 12 Cl 12 and polymers consisting of brominated epoxy resins and brominated polyester resins.
Claim 8
Dependent Claim
33 words
The composition of claim 1, wherein the mixture of polytetramethylene terephthalate and said polymer comprises at least 60% by weight of said terephthalate and not more than 40% by weight of said polymer.
Claim 9
Dependent Claim
32 words
The composition of claim 7, wherein said polymer is selected from the group consisting of polystyrene, polymethyl methacrylate, polycarbonate, polyethylene terephthalate, ABS resin, AS resin, AAS resin, polyethylene, polypropylene and nylon resin.
Claim 10
Dependent Claim
29 words
The composition of claim 1, wherein said polytetramethylene terephthalate has an intrinsic viscosity of [η] of 0.4-3.0 in a mixed solvent of equal amounts of tetrachloroethane/phenol at 25° C.
Claim 11
Dependent Claim
24 words
The composition of claim 1, wherein said hydrated silica is prepared by the said decomposition of sodium silicate or an alkaline earth metal silicate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-04 | 1982-03-06 | 1982-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-04 | 1986-03-06 | 1986-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-04 | 1990-03-06 | 1990-09-05 | $7700.00 | Window Closed / Lapsed |