Method for soldering metals with superhard man-made materials

Assignee: Individual
•
Filing: 1975-09-04
•
Granted: 1978-10-03
•
Expires: 1995-09-04
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract This invention relates to methods for soldering metals to superhard man-made materials such as diamond, boron nitride and hexanite and to soldering agents therefore. A method is proposed which comprises applying a metallizing coating to the soldering surface of the materials based on diamond and/or boron nitride, the materials to be joined by soldering being exposed to a temperature sufficient to bring about adequate adhesion of the metallizing coating to the materials to be soldered, and subsequently soldering the metal with the material bearing the metallized coating by use of soldering agents featuring ductile properties and melting points in the range up to 1,000° C, whereby, in accordance with the invention, the metallizing coating is constituted by metals showing high adhesive activity toward materials based on diamond and boron nitride and accounting for from 3.0 to 65 percent by weight of the coating and by metals showing poor oxidizability which account for the balance. The soldering procedure is effected in air under a layer of a liquid flux designed for soldering metals with metallic spelters. Also proposed is a copper-tin-titanium soldering agent which, in accordance with the invention, has the following composition, wt.%: Copper, from 15 to 60 Tin, from 5 to 15 Titanium, from 5 to 25 Lead, from 2 to 15, The balance being constituted by at least one metal from the group consisting of molybdenum, tungsten and tantalum. The proposed method and soldering agent, apart from conducting to very strong and stress-free soldered joints, also provides for a high level of reliabiity of soldered joints and an improved soldering efficiency.

Inventors

  • 👤 Jury Vladimirovich Naidich
  • 👤 Galina Alexeevna Kolesnichenko
  • 👤 Nikolai Stepanovich Zjukin
  • 👤 Boris Dmitrievich Kostjuk
  • 👤 Stanislava Stanislavovna Shaikevich
  • 👤 Yaroslav Feodosievich Motsak
  • 👤 Vitaly Pavlovich Fedulaev
  • 👤 Nikolai Alexandrovich Kolchemanov
  • 👤 Valentin Mikhailovich Ugarov
  • 👤 Viktor Vasilievich Losev
  • 👤 Mark Simonovich Drui
  • 👤 Alla Alexandrovna Lavrinovich
  • 👤 Dmitry Fedorovich Shpotakovsky
  • 👤 Stanislav Viktorovich Chizhov

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-01 18:16
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/14; C09K3/1436; C09K3/1445; B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; B23K; B23K1/00; B23K1/19; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/302; Y; Y10; Y10S; Y10S76/00; Y10S76/12

Claims Analysis

Total Claims: 12
Claim 1
Independent Claim 58 words
A method for coating synthetic diamonds comprising coating said material with a metal melt comprising lead in an amount varying from 2 to 15% by weight, and a metal selected from the group consisting of chromium, molybdenum, tungsten, tantalum, and mixtures thereof; mixed with a metal selected from the group consisting of silver, or tin, and mixtures thereof.
Claim 2
Independent Claim 58 words
A method for coating synthetic diamonds comprising coating said material with a metal melt comprising lead in an amount varying from 2 to 15% by weight, and a metal selected from the group consisting of chromium, molybdenum, tungsten, tantalum, and mixtures thereof; mixed with a metal selected from the group consisting of silver, or tin, and mixtures thereof.
Claim 3
Independent Claim 85 words
A method for coating a material selected from the group consisting of boron nitride and synthetic diamonds, comprising: applying to the surface of said material a metallizing coating consisting essentially of a first layer of an adherent metal selected from the group consisting of chromium, molybdenum, tungsten, and tantalum; and a second layer of a metal of reduced oxidizability selected from the group consisting of silver, lead, and tin; wherein the adherent metal varies from 3 to 65 percent by weight of the metallizing coating.
Claim 4
Independent Claim 85 words
A method for coating a material selected from the group consisting of boron nitride and synthetic diamonds, comprising: applying to the surface of said material a metallizing coating consisting essentially of a first layer of an adherent metal selected from the group consisting of chromium, molybdenum, tungsten, and tantalum; and a second layer of a metal of reduced oxidizability selected from the group consisting of silver, lead, and tin; wherein the adherent metal varies from 3 to 65 percent by weight of the metallizing coating.
Claim 5
Dependent Claim 11 words
The method of claim 2, wherein said material is boron nitride.
Claim 6
Dependent Claim 42 words
The method of claim 3, wherein the first layer of adherent metal is applied to a thickness of about 0.0005 to 0.001 mm, and the second metal layer of reduced oxidizability is applied to a thickness of about 0.001 to 0.01 mm.
Claim 7
Dependent Claim 11 words
The method of claim 2, wherein said material is synthetic diamonds.
Claim 8
Dependent Claim 42 words
The method of claim 5, wherein the first layer of adherent metal is applied to a thickness of about 0.0005 to 0.001 mm, and the second metal layer of reduced oxidizability is applied to a thickness of about 0.001 to 0.01 mm.
Claim 9
Dependent Claim 21 words
The method of claim 2, wherein said coated material is soldered with an alloy having a melting point under 1,000° C.
Claim 10
Dependent Claim 62 words
The method of claim 7, wherein said soldering is conducted at a temperature equal to the solder melting point for about 0.5 to 2 minutes at a rate of heating and cooling of the surfaces being joined of about 10 to 30 degrees per second by the use of a liquid flux having a melting point of about 500° to 700° C.
Claim 11
Dependent Claim 16 words
The method of claim 7, wherein said soldering procedure is effected under layer of liquid flux.
Claim 12
Dependent Claim 34 words
The method of claim 2, wherein said metallizing coating is applied by means selected from the group consisting of metal sputtering, electrolytic deposition, dipping in an adhesive melt, and a powder-like adhesive alloy paste.

References Cited (Backward Citations)

US2570248A Cited
US3006069A Cited
US3417460A Cited
US3178273A Cited
US3293012A Cited
US3356473A Cited
US3548345A Cited
US3650714A Cited
US3795041A Cited
US3868234A Cited
US3894673A Cited
US3793705A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1981-10-02 1982-04-03 1982-10-03 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1985-10-02 1986-04-03 1986-10-03 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1989-10-02 1990-04-03 1990-10-03 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag