Method for metallizing a phosphor screen for a cathode ray tube
Assignee: Toshiba Corp
•
Filing: 1976-02-26
•
Granted: 1978-10-24
•
Expires: 1996-02-26
Abstract
Abstract A method for metallizing a phosphor screen for a cathode ray tube including the steps of forming a volatilizable substrate on the surface of the phosphor screen and depositing a metal layer on the substrate, followed by heating for volatilizing the substrate, said substrate comprising a laminate of superposed layers respectively representing different organic materials having different thermal decomposition points. This disclosed method is advantageous in that the substrate can be volatilized without causing blistering of the metal layer and the formed metal layer is enabled to reflect light more effectively.
Inventors
- 👤 Takeo Ito
- 👤 Hatsuo Tsukagoshi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 04:56
CPC Classifications
H; H01; H01J; H01J29/00; H01J29/02; H01J29/10; H01J29/18; H01J29/28; C; C23; C23C; C23C14/00; C23C14/0005
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
60 words
A method of metallizing a phosphor screen for a cathode ray tube including the steps of forming a volatilizable substrate on the surface of the phosphor screen and depositing a metal layer upon the substrate, followed by heating for volatilizing the substrate, characterized in that the substrate consists of a layer of acrylic resin and a layer of polyvinyl pyrrolidone.
Claim 2
Independent Claim
60 words
A method of metallizing a phosphor screen for a cathode ray tube including the steps of forming a volatilizable substrate on the surface of the phosphor screen and depositing a metal layer upon the substrate, followed by heating for volatilizing the substrate, characterized in that the substrate consists of a layer of acrylic resin and a layer of polyvinyl pyrrolidone.
Claim 3
Independent Claim
99 words
A method of metallizing a phosphor screen for a cathode ray tube including the steps of forming a volatizable substrate on the surface of the phosphor screen and depositing a metal layer upon the substrate, followed by heating for volatilizing the substrate, characterized in that the substrate consists of a layer of a silane compound, a layer of acrylic resin formed on the silane compound layer and a layer of a water-soluble polymer formed on the acrylic resin layer, the silane compound being selected from the group consisting of glycidoxypropyltrimethoxy silane, γ-aminopropyl triethyoxy silane andd γ-methacryloxy propyl trimethoxy silane.
Claim 4
Independent Claim
99 words
A method of metallizing a phosphor screen for a cathode ray tube including the steps of forming a volatizable substrate on the surface of the phosphor screen and depositing a metal layer upon the substrate, followed by heating for volatilizing the substrate, characterized in that the substrate consists of a layer of a silane compound, a layer of acrylic resin formed on the silane compound layer and a layer of a water-soluble polymer formed on the acrylic resin layer, the silane compound being selected from the group consisting of glycidoxypropyltrimethoxy silane, γ-aminopropyl triethyoxy silane andd γ-methacryloxy propyl trimethoxy silane.
Claim 5
Dependent Claim
24 words
The method according to claim 2, in which the water-soluble polymer is selected from the group consisting of polyvinyl alcohol, polyvinyl pyrrolidone, and polyacrylamide.
Claim 6
Dependent Claim
15 words
The method according to claim 2, in which said glycidoxypropyltrimethoxy silane is γ-glycidoxypropyl trimethoxy silane.
Claim 7
Dependent Claim
86 words
The method according to claim 2, in which the silane compound layer is formed by coating the surface of the phosphor screen with an aqueous solution consisting essentially of the silane compound, followed by drying, the acrylic resin layer is formed by coating the silane compound layer with an aqueous emulsion consisting essentially of an acrylic resin, followed by drying, and the water-soluble polymer layer is formed by coating the acrylic resin layer with an aqueous solution consisting essentially of a water-soluble polymer, followed by drying.
Claim 8
Dependent Claim
54 words
The method according to claim 2, in which the silane compound content of the aqueous solution is 0.1 to 10 percent by weight, the acrylic resin content of the aqueous emulsion is 10 to 30 percent by weight, and the water-soluble polymer content of the aqueous solution is 0.05 to 20 percent by weight.
References Cited (Backward Citations)
US3067055A
Cited
US3317337A
Cited
US3582389A
Cited
US3574663A
Cited
US3582390A
Cited
US3579367A
Cited
US3839068A
Cited
US3821009A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |