US4133725A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low voltage hard anodizing process
Assignee: Sanford Process Corp
•
Filing: 1978-05-18
•
Granted: 1979-01-09
•
Expires: 1998-05-18
Abstract
Abstract A process for hard anodizing of aluminum and aluminum alloys by use of a low voltage having a DC component and a superimposed AC component. The electrolyte can have relatively low acid concentration and can be of higher temperature than usually employed for hard anodizing.
Inventors
- 👤 Moisey M. Lerner
- 👤 James H. Morse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 00:42
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/024; C25D11/06; Y; Y10; Y10S; Y10S204/00; Y10S204/08
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
123 words
A method for hard anodizing aluminum and aluminum alloy articles comprising the steps of: immersing one or more of said articles in a cooled electrolyte composed of an aqueous solution of a strong acid; applying for a predetermined time interval across said article and a cathode in said electrolyte a DC voltage with a superimposed AC voltage, the positive potential of the DC voltage component being applied to said article and the negative potential of the DC voltage component being applied to said cathode; said DC voltage component having a value during at least a portion of said time interval substantially in the range of about 14-20 volts, said value being the highest DC voltage applied during said time interval to said articles.
Claim 2
Independent Claim
123 words
A method for hard anodizing aluminum and aluminum alloy articles comprising the steps of: immersing one or more of said articles in a cooled electrolyte composed of an aqueous solution of a strong acid; applying for a predetermined time interval across said article and a cathode in said electrolyte a DC voltage with a superimposed AC voltage, the positive potential of the DC voltage component being applied to said article and the negative potential of the DC voltage component being applied to said cathode; said DC voltage component having a value during at least a portion of said time interval substantially in the range of about 14-20 volts, said value being the highest DC voltage applied during said time interval to said articles.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein said electrolyte is an aqueous solution of sulfuric acid.
Claim 4
Dependent Claim
14 words
The method of claim 2 wherein said electrolyte includes an acidic aqueous extract additive.
Claim 5
Dependent Claim
16 words
The method of claim 3 wherein said additive is an extract sold under the trademark SANFRAN.
Claim 6
Dependent Claim
26 words
The method of claim 2 wherein said electrolyte is composed of 5.7-23% by volume of 66° Baume sulfuric acid and from 2-8% by volume of SANFRAN.
Claim 7
Dependent Claim
11 words
The method of claim 1 wherein said AC voltage is sinusoidal.
Claim 8
Dependent Claim
24 words
The method of claim 6 wherein said sinusoidal voltage has an amplitude which is about 100% of the voltage level of said DC voltage.
Claim 9
Dependent Claim
20 words
The method of claim 1 wherein the superimposed AC voltage has a peak-to-peak value about 200% of the DC component.
Claim 10
Dependent Claim
29 words
The method of claim 1 including the step of: increasing the DC voltage component during said time interval to a final value in the range of about 14-20 volts.
Claim 11
Dependent Claim
41 words
The method of claim 1 including the steps of: increasing the DC voltage component during said time interval to a final value in the range of about 14-20 volts; and maintaining said final value during the remainder of said time interval.
Claim 12
Dependent Claim
42 words
The method of claim 1 including the step of: increasing the DC voltage component during said time interval to a final value in the range of about 14-20 volts while maintaining constant the ratio of the AC voltage to the DC voltage.
Claim 13
Dependent Claim
28 words
The method of claim 1 wherein said value of DC voltage component is determined for a particular aluminum alloy to provide the greatest abrasion resistance and breakdown voltage.
Claim 14
Dependent Claim
20 words
The method of claim 2 wherein said electrolyte is cooled to a temperature within the range of about 25°-60° F.
Claim 15
Independent Claim
151 words
The method for hard anodizing aluminum and aluminum alloy articles comprising the steps of: immersing one or more of said articles in a cooled electrolyte composed of an aqueous solution of sulfuric acid; applying for a predetermined time interval across said article and a cathode in said electrolyte a DC voltage with a superimposed AC voltage, the positive potential of the DC voltage component being applied to said article and the negative potential of the DC voltage component being applied to said cathode, said DC voltage component with a superimposed AC voltage being applied in the following manner: raising said DC voltage component from zero to 10 volts during a one minute interval; increasing said DC voltage component at a rate of 1/2 volt per minute to a predetermined final voltage in the range of about 14-20 volts; and maintaining said final voltage constant for the remainder of said time interval.
Claim 16
Independent Claim
151 words
The method for hard anodizing aluminum and aluminum alloy articles comprising the steps of: immersing one or more of said articles in a cooled electrolyte composed of an aqueous solution of sulfuric acid; applying for a predetermined time interval across said article and a cathode in said electrolyte a DC voltage with a superimposed AC voltage, the positive potential of the DC voltage component being applied to said article and the negative potential of the DC voltage component being applied to said cathode, said DC voltage component with a superimposed AC voltage being applied in the following manner: raising said DC voltage component from zero to 10 volts during a one minute interval; increasing said DC voltage component at a rate of 1/2 volt per minute to a predetermined final voltage in the range of about 14-20 volts; and maintaining said final voltage constant for the remainder of said time interval.
Claim 17
Dependent Claim
29 words
The method of claim 14 wherein said final voltage is between 17 and 18 volts for the 2024 aluminum alloy to achieve substantially maximum abrasion resistance and breakdown voltage.
Claim 18
Dependent Claim
31 words
The method of claim 14 wherein said final voltage is in the range of about 15-18 volts for the 6061 aluminum alloy to achieve substantially maximum abrasion resistance and breakdown voltage.
Claim 19
Dependent Claim
30 words
The method of claim 14 wherein said final voltage is about 17 and 19 volts for the 7075 aluminum alloy to achieve substantially maximum abrasion resistance and breakdown voltage, respectively.
References Cited (Backward Citations)
CA548071A
Cited
US2897125A
Cited
US2743221A
Cited
US2905600A
Cited
US2977294A
Cited
US3020219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-08 | 1982-07-10 | 1983-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-08 | 1986-07-10 | 1987-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-08 | 1990-07-10 | 1991-01-09 | $7700.00 | Window Closed / Lapsed |