Dye impregnated plastics for laser applications
Assignee: Raytheon Co
•
Filing: 1977-07-18
•
Granted: 1979-02-13
•
Expires: 1997-07-18
Abstract
Abstract A process for doping laser dyes into plastic hosts is disclosed. This process allows the control of the doping profiles in order to achieve profiles, other than uniform, necessary for effective laser mode control, volumetric pumping, and stable resonators and oscillations during transverse pumping. In addition to the above-stated attributes, this process enables the production of dye impregnated plastics which lase at extended light wave lengths. Dye impregnated plastics, prepared in accordance with this process, exhibit electro-optical characteristics previously unattainable with plastics prepared via conventional prior art processes.
Inventors
- 👤 Stephen J. Sheldrake
- 👤 Harry H. L. Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:36
CPC Classifications
H; H01; H01S; H01S3/00; H01S3/14; H01S3/16; H01S3/168; C; C08; C08J; C08J7/00; C08J7/04; C08J7/06; C08J7/065
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
43 words
A dye impregnated plastic laser medium capable of lasing at frequencies above 0.65 μm, comprised of a solid resin selected from the group consisting of polymethylmethacrylate, polystyrene, epoxy and polyester polymers doped with a dye selected from the group whose structures are: ##STR2##
Claim 2
Dependent Claim
43 words
A dye impregnated plastic laser medium capable of lasing at frequencies above 0.65 μm, comprised of a solid resin selected from the group consisting of polymethylmethacrylate, polystyrene, epoxy and polyester polymers doped with a dye selected from the group whose structures are: ##STR2##
Claim 3
Dependent Claim
17 words
The lasing medium of claim 1 wherein said resin is polymethylmethacrylate and said dye is Carbazine 122.
Claim 4
Dependent Claim
24 words
The lasing medium of claim 2 wherein the concentration of said dye ranges from 5 × 10 -5 to 3 × 10 -3 molar.
Claim 5
Dependent Claim
15 words
The lasing medium of claim 1 wherein the doped profile of said medium is non-uniform.
Claim 6
Dependent Claim
15 words
The lasing medium of claim 3 wherein the doped profile of said medium is non-uniform.
Claim 7
Dependent Claim
174 words
A process for doping a solid plastic host material with a selected laser dye comprising the steps of: forming a dye-solvent solution by admixing from 5 × 10 -5 to 3 × 10 -3 moles of a dye solute in 1000 cc of a non-ionic solvent; adjusting the pH, if necessary, of said solution to a preselected level based on the character of said dye solute; immersing said host material in said solution at an ambient pressure; elevating the temperature of said solution while maintaining said concentration of said dye in said solvent; allowing said host material to remain immersed in said solution from about one to about two weeks whereby said material will become doped with said dye; removing said doped material from said solution; and subsequently removing excess dye-solvent solution from said material by placing said material in an oven and causing it to be exposed to an elevated temperature below 95° C for a period of from 1 to 2 weeks prior to allowing said medium to cool to ambient temperature.
Claim 8
Dependent Claim
174 words
A process for doping a solid plastic host material with a selected laser dye comprising the steps of: forming a dye-solvent solution by admixing from 5 × 10 -5 to 3 × 10 -3 moles of a dye solute in 1000 cc of a non-ionic solvent; adjusting the pH, if necessary, of said solution to a preselected level based on the character of said dye solute; immersing said host material in said solution at an ambient pressure; elevating the temperature of said solution while maintaining said concentration of said dye in said solvent; allowing said host material to remain immersed in said solution from about one to about two weeks whereby said material will become doped with said dye; removing said doped material from said solution; and subsequently removing excess dye-solvent solution from said material by placing said material in an oven and causing it to be exposed to an elevated temperature below 95° C for a period of from 1 to 2 weeks prior to allowing said medium to cool to ambient temperature.
Claim 9
Dependent Claim
31 words
The process of claim 6 wherein said dye-solvent solution concentration is maintained by controlling the pressure profile above said solution thereby precluding the loss of solvent or solute molecules by evaporation.
Claim 10
Dependent Claim
177 words
A process for forming a doped solid plastic laser medium having a non-uniform doped profile comprising the steps of: forming a dye-solvent solution by admixing a laser dye and a non-ionic solvent; adjusting the pH of said solution to a preselected level based on the character of said dye; masking the surface of said host material as desired to create a controlled absorptive cross-sectional area; immersing said masked host material in said solution at an ambient pressure; maintaining the concentration of said dye-solvent solution while causing the temperature of said solution to be elevated; allowing said host material to remain immersed in said solution for a preselected time interval; removing said material, which will have been doped with said dye, from said solution; and subsequently removing excess solvent and dye solution remaining on said material by placing said doped material in an oven and causing it to be exposed to an elevated temperature of less than 95° C for a period of from 1 to 2 weeks prior to allowing said medium to cool to ambient temperature.
Claim 11
Dependent Claim
177 words
A process for forming a doped solid plastic laser medium having a non-uniform doped profile comprising the steps of: forming a dye-solvent solution by admixing a laser dye and a non-ionic solvent; adjusting the pH of said solution to a preselected level based on the character of said dye; masking the surface of said host material as desired to create a controlled absorptive cross-sectional area; immersing said masked host material in said solution at an ambient pressure; maintaining the concentration of said dye-solvent solution while causing the temperature of said solution to be elevated; allowing said host material to remain immersed in said solution for a preselected time interval; removing said material, which will have been doped with said dye, from said solution; and subsequently removing excess solvent and dye solution remaining on said material by placing said doped material in an oven and causing it to be exposed to an elevated temperature of less than 95° C for a period of from 1 to 2 weeks prior to allowing said medium to cool to ambient temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-12 | 1982-08-14 | 1983-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-12 | 1986-08-14 | 1987-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-12 | 1990-08-14 | 1991-02-13 | $7700.00 | Window Closed / Lapsed |