Contact lens casting method
Assignee: American Optical Corp
•
Filing: 1977-09-21
•
Granted: 1979-02-27
•
Expires: 1997-09-21
Abstract
Abstract Producing from a single contact lens casting mold, lenses of a number of different sizes by including in the casting precursor for each lens, a controlled amount of an extractable diluent of low volatility which is extracted after casting to cause the resulting lens to shrink a calculable amount. Variations in amounts are used to produce corresponding variations in sizes of cast and extracted lenses.
Inventors
- 👤 Edward A. Travnicek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:30
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00009; B29D11/00038; B29D11/00057
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
111 words
The method of making a contact lens of an ophthalmic quality resin comprising: preparing a casting precursor by adding to the resin an extractable, non-reactive, miscible diluent in an amount precontrolled according to a subsequent volume reduction desired of the precursor after casting; filling a mold casting cavity of predetermined fixed shape and size with said precursor; at least partially curing the thus cast precursor in situ; removing the resulting cast lens from said cavity; and extracting said diluent from the cast lens to shrink the lens to a size smaller than that of said casting cavity, said size reduction corresponding to said amount of said diluent added to said precursor.
Claim 2
Independent Claim
111 words
The method of making a contact lens of an ophthalmic quality resin comprising: preparing a casting precursor by adding to the resin an extractable, non-reactive, miscible diluent in an amount precontrolled according to a subsequent volume reduction desired of the precursor after casting; filling a mold casting cavity of predetermined fixed shape and size with said precursor; at least partially curing the thus cast precursor in situ; removing the resulting cast lens from said cavity; and extracting said diluent from the cast lens to shrink the lens to a size smaller than that of said casting cavity, said size reduction corresponding to said amount of said diluent added to said precursor.
Claim 3
Dependent Claim
34 words
The method according to claim 1 wherein said resin is a silicone resin and said diluent is selected from the group consisting of a liquid aliphatic hydrocarbon, aromatic hydrocarbon, chlorinated hydrocarbon, and silicone oil.
Claim 4
Dependent Claim
13 words
The method according to claim 2 wherein said diluent is a silicone oil.
Claim 5
Dependent Claim
48 words
The method according to claim 1 wherein said step of extracting said diluent is accomplished with an effective solvent for said diluent, said extraction solvent being harmless and non-reactive to said lens resin and of sufficiently high volatility to be readily removed by evaporation from said cast lens.
Claim 6
Dependent Claim
38 words
The method according to claim 4 wherein said extraction solvent is selected from the group consisting of pentane, hexane, heptane, octane, benzene, toluene, xylene, carbon tetrachloride, trichloro ethylene, perchloro ethylene, trichloro trifluoroethane, methylene chloride, chloroform and hexamethyl disiloxane.
Claim 7
Dependent Claim
41 words
The method according to claim 3 wherein said diluent is extracted with a solvent selected from the group consisting of pentane, hexane, heptane, octane, benzene, toluene, xylene, carbon tetrachloride, trichloro ethylene, perchloro ethylene, trichloro trifluoroethane, methylene chloride, chloroform and hexamethyl disiloxane.
Claim 8
Dependent Claim
12 words
The method according to claim 6 wherein said extraction solvent is hexane.
Claim 9
Dependent Claim
26 words
The method according to claim 3 wherein said diluent has a phenyl-methyl ratio within 4 mole % of the phenyl-methyl ratio of said silicone casting resin.
Claim 10
Dependent Claim
20 words
The method according to claim 3 wherein said silicone oil diluent has a viscosity between 10 centistokes and 10,000 centistokes.
Claim 11
Dependent Claim
27 words
The method according to claim 1 wherein said precontrolled amount of extractable diluent is within a range of from nearly 0 volume % to 25 volume %.
Claim 12
Dependent Claim
24 words
The method according to claim 1 wherein said precontrolled amount of diluent is a liquid hydrocarbon having a normal boiling point above 100° C.
Claim 13
Dependent Claim
24 words
The method according to claim 11 wherein said liquid hydrocarbon is within a range of from nearly 0 volume % to 25 volume %.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |