US4145233A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for making narrow channel FET by masking and ion-implantation
Assignee: LSI Logic FSI Corp
•
Filing: 1978-05-26
•
Granted: 1979-03-20
•
Expires: 1998-05-26
Abstract
Abstract A method for making an FET comprising as many as three parallel channels having different threshold voltages. The two outer channels can have very low W/L ratios and resulting low drain-to-source currents. In one embodiment, the FET has a central enhancement channel flanked by low W/L ratio, low current, depletion channels. This FET is fabricated by (1) forming on the field oxide a photoresist mask having a relatively narrow aperture; (2) overetching the field oxide beneath the photoresist mask aperture to form a relatively wide aperture in the field oxide, leaving a photoresist overhang; (3) implanting the substrate through the relatively narrow photoresist mask aperture to provide an enhancement section of the channel region; (4) removing the photoresist mask; and (5) depletion implanting the substrate through the relatively wide field oxide aperture. The gate structure is formed over the combined enhancement and depletion channels and a source and a drain span the ends of the channels. This effectively provides an enhancement FET which is in parallel with a depletion FET. The effective channel width of the depletion FET approximates the combined width of the two narrow depletion regions and is controlled by the photoresist overhang, i.e., by the relative width dimensions of the two mask apertures. The method is applicable to both silicon and metal gate technology, to n-channel and p-channel, and to various combinations of enhancement and/or depletion devices.
Inventors
- 👤 Stephen A. Sefick
- 👤 Robert K. Jones
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:21
CPC Classifications
H; H10; H10B; H10B10/00; H10B10/12; H10D; H10D30/00; H10D30/60; H10D30/637; H10D62/00; H10D62/10; H10D62/17; H10D62/213; H10D62/221; H10D62/235; H10D62/299; H10P; H10P30/00; H10P30/20; H10P30/22
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
188 words
In a method for forming a semiconductor device having an electrode structure formed over a channel region in a semiconductor body, the semiconductor body having a layer of oxide formed over the channel region thereof, the improvement wherein the channel region comprises at least two sections having different threshold voltages, including a section having an effective width of a predetermined dimension, comprising: forming a mask over the oxide layer on the semiconductor body, the mask having a first aperture having sides such that the width of the aperture is less than the channel region width; etching the oxide layer via the first aperture to form a second aperture therein, at least one side of the second aperture being spaced a predetermined distance outside the corresponding side of the first aperture; depositing in the semiconductor body via the first aperture impurities of a first conductivity type to form a first channel region section extending the length of the channel region and having a width smaller than the width of the channel region; removing the mask; and forming the electrode structure to encompass the aperture of the masking oxide layer.
Claim 2
Dependent Claim
188 words
In a method for forming a semiconductor device having an electrode structure formed over a channel region in a semiconductor body, the semiconductor body having a layer of oxide formed over the channel region thereof, the improvement wherein the channel region comprises at least two sections having different threshold voltages, including a section having an effective width of a predetermined dimension, comprising: forming a mask over the oxide layer on the semiconductor body, the mask having a first aperture having sides such that the width of the aperture is less than the channel region width; etching the oxide layer via the first aperture to form a second aperture therein, at least one side of the second aperture being spaced a predetermined distance outside the corresponding side of the first aperture; depositing in the semiconductor body via the first aperture impurities of a first conductivity type to form a first channel region section extending the length of the channel region and having a width smaller than the width of the channel region; removing the mask; and forming the electrode structure to encompass the aperture of the masking oxide layer.
Claim 3
Dependent Claim
31 words
The method of claim 1 wherein the oxide etching step forms each of opposite sides of the second aperture spaced the predetermined dimension from the corresponding side of the first aperture.
Claim 4
Dependent Claim
49 words
The method of claim 2, including after the channel region deposition step, the step of depositing in the substrate via the second aperture impurities of the first or second conductivity type to form a pair of channel region sections along the opposite sides of the first channel region section.
Claim 5
Dependent Claim
61 words
The method of claim 2, including after the channel region deposition step, the step of depositing in the substrate via the second aperture impurities of the first or second conductivity type, the impurities being deposited to different concentration levels at the opposite sides of the first channel region section to form a pair of channel region sections to different threshold voltages.
Claim 6
Independent Claim
188 words
A method for forming a semiconductor device having an electrode structure formed over a channel region in a semiconductor wafer of a first conductivity type having a major surface, comprising: forming an oxide layer on the major surface; forming source-and drain-locating cuts in the oxide layer; depositing impurities of the second conductivity type via the oxide cuts into the wafer to form a source and a drain therein; forming over the oxide layer a mask having a first aperture having sides such that the width of the aperture is less than the channel region width; etching the oxide layer via the first aperture to form a second aperture in the oxide layer having at least one side spaced a predetermined distance outside the corresponding side of the first aperture; depositing in the semiconductor wafer via the first aperture impurities of the first or the second conductivity type to form a first channel region section extending the length of the channel region and having a width smaller than the width of the channel region; removing the mask; and forming the electrode structure to encompass the second, oxide layer aperture.
Claim 7
Independent Claim
188 words
A method for forming a semiconductor device having an electrode structure formed over a channel region in a semiconductor wafer of a first conductivity type having a major surface, comprising: forming an oxide layer on the major surface; forming source-and drain-locating cuts in the oxide layer; depositing impurities of the second conductivity type via the oxide cuts into the wafer to form a source and a drain therein; forming over the oxide layer a mask having a first aperture having sides such that the width of the aperture is less than the channel region width; etching the oxide layer via the first aperture to form a second aperture in the oxide layer having at least one side spaced a predetermined distance outside the corresponding side of the first aperture; depositing in the semiconductor wafer via the first aperture impurities of the first or the second conductivity type to form a first channel region section extending the length of the channel region and having a width smaller than the width of the channel region; removing the mask; and forming the electrode structure to encompass the second, oxide layer aperture.
Claim 8
Dependent Claim
31 words
The method of claim 5 wherein the oxide etching step forms each of opposite sides of the second aperture spaced a predetermined dimension from the corresponding side of the first aperture.
Claim 9
Dependent Claim
50 words
The method of claim 6 including after the channel region deposition step, the step of depositing in the substrate via the second aperture impurities of the first or the second conductivity type to form a pair of channel region sections along the opposite sides of the first channel region section.
Claim 10
Dependent Claim
62 words
The method of claim 6, including after the channel region deposition step, the step of depositing in the substrate via the second aperture impurities of the first or the second conductivity type, the impurities being deposited to different concentration levels at the opposite sides of the first channel region section to form a pair of channel region sections to different threshold voltages.
Claim 11
Dependent Claim
217 words
In a method for forming a semiconductor device having a channel region for forming a channel in a semiconductor body having a layer of silicon oxide covering the channel region, the improvement wherein the channel region comprises at least two sections having different threshold voltages, including a section having an effective width of a predetermined dimension, comprising: forming a mask over the oxide layer on the semiconductor body, the mask having a first aperture, the aperture having sides defining aperture width of a predetermined dimension; etching the oxide layer via the first aperture to form a second aperture in the oxide layer, at least one side of the second aperture being spaced a predetermined distance outside the corresponding side of the first aperture; depositing in the semiconductor body via the first aperture impurities of the first conductivity type to form a first channel region section extending the length of the channel region and having a width controlled by the first aperture to a dimension smaller than the channel region width; removing the mask; and depositing in the semiconductor body via the second aperture impurities of the first conductivity type or the second conductivity type to form at least a second channel region section between the one side of the second aperture and the first channel region section.
Claim 12
Dependent Claim
217 words
In a method for forming a semiconductor device having a channel region for forming a channel in a semiconductor body having a layer of silicon oxide covering the channel region, the improvement wherein the channel region comprises at least two sections having different threshold voltages, including a section having an effective width of a predetermined dimension, comprising: forming a mask over the oxide layer on the semiconductor body, the mask having a first aperture, the aperture having sides defining aperture width of a predetermined dimension; etching the oxide layer via the first aperture to form a second aperture in the oxide layer, at least one side of the second aperture being spaced a predetermined distance outside the corresponding side of the first aperture; depositing in the semiconductor body via the first aperture impurities of the first conductivity type to form a first channel region section extending the length of the channel region and having a width controlled by the first aperture to a dimension smaller than the channel region width; removing the mask; and depositing in the semiconductor body via the second aperture impurities of the first conductivity type or the second conductivity type to form at least a second channel region section between the one side of the second aperture and the first channel region section.
Claim 13
Dependent Claim
19 words
The method of claim 9 wherein the first conductivity type is p-type and the second conductivity type is n-type.
Claim 14
Dependent Claim
32 words
The method of claim 10 wherein the substrate is p-type, the channel is n-type, and the first channel region section and the second channel region section are enhancement and depletion sections, respectively.
Claim 15
Dependent Claim
32 words
The method of claim 10 wherein the substrate is n-type, the channel is p-type, and the first channel region section and the second channel region sections are depletion and enhancement sections, respectively.
Claim 16
Dependent Claim
19 words
The method of claim 9 wherein the first conductivity type is n-type and the second conductivity type is p-type.
Claim 17
Dependent Claim
32 words
The method of claim 13 wherein the substrate is n-type, the channel is p-type, and the first channel region section and the second channel region section are enhancement and depletion sections, respectively.
Claim 18
Dependent Claim
32 words
The method of claim 13, wherein the substrate is p-type, the channel is n-type, and the first channel region section and the second channel region section are enhancement and depletion sections, respectively.
Claim 19
Dependent Claim
23 words
The method of claim 9, wherein the first channel region section and the second channel region sections are both enhancement or depletion sections.
Claim 20
Dependent Claim
23 words
The method of claim 9, wherein the etching step comprises etching the silicon oxide mask for a predetermined time using hydrofluoric acid etchant.
Claim 21
Dependent Claim
210 words
In a method for forming an insulated gate field effect transistor having a channel region for forming a channel in a semiconductor substrate, the improvement wherein the channel region comprises three sections, at least two of which have different threshold voltages, including a section having an effective width of a predetermined dimension, comprising: forming on the substrate an oxide layer of suitable thickness for use as a deposition mask; forming on the oxide layer a deposition mask having an aperture over the channel region, the aperture being of lesser width than the channel region; etching the oxide layer by applying a liquid bath etchant thereto via the mask aperture to form an aperture in the oxide layer, the oxide layer aperture being of greater width than the deposition mask aperture; as a first deposition step, implanting in the substrate via the deposition mask aperture impurities of a first conductivity type to form a first channel region section having a width smaller than the width of the channel region; and removing the deposition mask; and as a second deposition step, implanting in the substrate via the oxide layer aperture impurities of the second conductivity type to form a pair of second channel region sections along the sides of the first section.
Claim 22
Dependent Claim
210 words
In a method for forming an insulated gate field effect transistor having a channel region for forming a channel in a semiconductor substrate, the improvement wherein the channel region comprises three sections, at least two of which have different threshold voltages, including a section having an effective width of a predetermined dimension, comprising: forming on the substrate an oxide layer of suitable thickness for use as a deposition mask; forming on the oxide layer a deposition mask having an aperture over the channel region, the aperture being of lesser width than the channel region; etching the oxide layer by applying a liquid bath etchant thereto via the mask aperture to form an aperture in the oxide layer, the oxide layer aperture being of greater width than the deposition mask aperture; as a first deposition step, implanting in the substrate via the deposition mask aperture impurities of a first conductivity type to form a first channel region section having a width smaller than the width of the channel region; and removing the deposition mask; and as a second deposition step, implanting in the substrate via the oxide layer aperture impurities of the second conductivity type to form a pair of second channel region sections along the sides of the first section.
Claim 23
Dependent Claim
43 words
The method of claim 18 wherein during the second deposition step the impurities are deposited to different concentration levels at the opposite sides of the first channel region section to form each of the pair of channel region sections to different threshold voltages.
Claim 24
Dependent Claim
19 words
The method of claim 18 wherein the first conductivity type is n-type and the second conductivity type is p-type.
Claim 25
Dependent Claim
15 words
The method of claim 20 wherein the substrate is p-type and the channel is n-type.
Claim 26
Dependent Claim
15 words
The method of claim 20 wherein the substrate is n-type and the channel is p-type.
Claim 27
Dependent Claim
211 words
The method of claim 22, wherein the substrate background concentration is 10 15 cm -3 phosphorus, the channel region is about four microns wide by 16 microns long, and a source and a drain are formed at opposite ends of the channel region by about 5 × 10 18 cm -3 surface concentration of boron formed to a junction depth of about two microns, the oxide layer is formed to a depth of about two microns, and wherein: the deposition mask aperture is formed to a width of about 4 microns; etching the oxide layer comprises applying buffered hydrofluoric acid etchant via the deposition mask aperture for sufficient time to form the oxide layer aperture to a width of about 5 microns; the first deposition step comprises implanting phosphorus using a dose of 3 × 10 12 cm -2 and 50 kev; and the second deposition step comprises implanting boron using a dose of 3.5 × 10 12 cm -2 and 20 kev; the first and second deposition steps providing first and second channel region sections having peak concentrations of about 5 × 10 17 cm -3 phosphorus at a depth of about 60 nanometers; and about 4 × 10 17 cm -3 boron at a depth of 60 nanometers, respectively.
Claim 28
Dependent Claim
19 words
The method of claim 18 wherein the first conductivity type is p-type and the second conductivity type is n-type.
Claim 29
Dependent Claim
15 words
The method of claim 24 wherein the substrate is n-type and the channel is p-type.
Claim 30
Dependent Claim
15 words
The method of claim 24, wherein the substrate is p-type and the channel is n-type.
References Cited (Backward Citations)
US3873372A
Cited
US3883372A
Cited
US3933529A
Cited
US3863330A
Cited
US4001860A
Cited
US3996655A
Cited
US4037307A
Cited
US4089712A
Cited
US4084987A
Cited
US4038107A
Cited
US4038107B1
Cited
US4078947A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-19 | 1982-09-18 | 1983-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-19 | 1986-09-18 | 1987-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-19 | 1990-09-18 | 1991-03-20 | $7700.00 | Window Closed / Lapsed |