Ceramic bonded grinding tools with graphite in the bond
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1978-02-21
•
Granted: 1979-06-12
•
Expires: 1998-02-21
Abstract
Abstract Ceramic bonded grinding and honing tools employing diamond or cubic boron nitride abrasive particles are improved by the inclusion of from 10 to 53%, by volume, of graphite in the bond, based on the total bond solids, including graphite. The bond must have a porosity volume less than 15% for honing applications and less than 10% for grinding wheels, preferably the graphite should be finely particulate. Applications in dry grinding and honing of hard materials are described. For dry grinding the optimum graphite content of the bond is from 34 to 45 volume percent. The bond may include crystalline filler such as alumina, zirconia, silicon carbide, or crystalline filler formed in situ by devitrification; and the abrasive particles may be metal coated. MoS 2 or hexagonal boron nitride may substitute for all or part of the graphite and metal powders may be employed to replace up to 50% by volume of the graphite or graphite substitute materials.
Inventors
- 👤 Paul P. Keat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:36
CPC Classifications
B; B24; B24D; B24D7/00; B24D3/00; B24D3/02; B24D3/04; B24D3/14; B24D3/16; B24D3/34; B24D3/342
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
79 words
A bonded abrasive grinding element consisting of abrasive grains distributed in a continuous ceramic bonding matrix said abrasive grains comprising diamond or cubic boron nitride and said bond consisting essentially of a ceramic matrix including from 10 to 53%, by volume, of graphite or a graphite substitute selected from hexagonal boron nitride, or molybdenum, disulfide or mixtures thereof, having a numerical average particle size of less than 200 microns, said grinding element including less than 10% porosity, by volume.
Claim 2
Dependent Claim
79 words
A bonded abrasive grinding element consisting of abrasive grains distributed in a continuous ceramic bonding matrix said abrasive grains comprising diamond or cubic boron nitride and said bond consisting essentially of a ceramic matrix including from 10 to 53%, by volume, of graphite or a graphite substitute selected from hexagonal boron nitride, or molybdenum, disulfide or mixtures thereof, having a numerical average particle size of less than 200 microns, said grinding element including less than 10% porosity, by volume.
Claim 3
Dependent Claim
40 words
A grinding element as in claim 1 in which the graphite is flake graphite having a particle size of from 1 to 10 microns and is present in an amount of from 27 to 45%, by volume of the bond.
Claim 4
Dependent Claim
30 words
A grinding element as in claim 1 in which the bond is a devitrified glass containing microcrystalline particles crystallized in situ, based on the total volume of glass and microcrystals.
Claim 5
Dependent Claim
38 words
A grinding element as in claim 1 in which the ceramic bond contains up to 60% of the total bond volume exclusive of graphite, of a microcrystalline filler selected from the group consisting of alumina and silicon carbide.
Claim 6
Dependent Claim
14 words
A grinding element as in claim 1 in which the abrasive grains are diamond.
Claim 7
Dependent Claim
16 words
A grinding element as in claim 1 in which the abrasive grains are cubic boron nitride.
Claim 8
Dependent Claim
40 words
A grinding element as in claim 1 in which from 0 to 50% by volume of the graphite or graphite substitute is replaced by a finely particulate metal filler selected from the group consisting of silver, copper, aluminum, and tin.
Claim 9
Dependent Claim
71 words
A grinding element as in claim 1 in which the abrasive is metal clad diamond, the metal cladding being selected from the group consisting of copper, silver, nickel, cobalt, molybdenum, and alloys thereof, the graphite has a particle size of from 1 to 10 microns and is flaky in form, the volume of porosity is below 10%, and the diamond volume is from 5 to 40%, of the total element volume.
Claim 10
Dependent Claim
38 words
A ceramic bonded multipoint diamond abrasive element wherein the bond contains from 34 to 45%, by volume of graphite having a particle size less than 200 microns, and wherein said element has a porosity of less than 10%.
Claim 11
Dependent Claim
38 words
A ceramic bonded multipoint diamond abrasive element wherein the bond contains from 34 to 45%, by volume of graphite having a particle size less than 200 microns, and wherein said element has a porosity of less than 10%.
References Cited (Backward Citations)
US3081161A
Cited
US3383191A
Cited
US3819387A
Cited
US3454384A
Cited
US3650714A
Cited
US3664819A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-11 | 1982-12-11 | 1983-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-11 | 1986-12-11 | 1987-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-11 | 1990-12-11 | 1991-06-12 | $7700.00 | Window Closed / Lapsed |