Process for imparting a better adhesion between reinforcing materials and plastic matrix and product thereby produced

Claim 2

A process for imparting a better adhesion between reinforcing material and plastic matrix, characterized in that said process comprises the steps of (a) treating the reinforcing material surface at a temperature ranging from 250° to 650° C.; with at least one organic compound of a tetravalent metal having the formula: M(OZ).sub.4 wherein: M is Zr or Sn; (OZ) is an organic radical non-hydrolyzable at room temperature in the presence of water, but hydrolyzable in the presence of water vapor at a temperature between 250° and 650° C.; or a polymeric derivative thereof with a linkage of the type ##STR8## (b) applying onto the thus treated reinforcing material surface at a lower temperature, at least one silane coupling agent having the formula: (OR).sub.3 Si(CH.sub.2).sub.n X wherein: n is 0, 1, 2 or 3; (OR) is an organic radical hydrolyzable at room temperature in the presence of water, bound to silicon, and in which R is an alkyl or acyl radical; X is an organo functional radical promoting the adhesion of the treated reinforcing material to the plastic material; such as chlorine, a vinyl, methacryloxy, amino, glycidoxy, mercaptyl, or an epoxy-cyclohexyl group; (c) drying the thus treated reinforcing material.

Claim 3

Process according to claim 1, characterized in that said organic compound of the tetravalent metal is selected from the group consisting of esters of zirconium acid, amino-alkyl-zirconates and amino-alkyl-stannates.

Claim 4

Process according to claim 1, characterized in that said organic compound of the tetravalent metal is an ester of zirconium acid with water-soluble polyvalent alcohols containing from 3 to 6 carbon atoms and at least 3 hydroxyl radicals.

Claim 5

Process according to claim 1, characterized in that said organic compound of the tetravalent metal is an amino-alkyl-zirconate prepared by reacting water-soluble amino-alcohols with zirconium dioxy-hydrate.

Claim 6

Process according to claim 1, characterized in that said organic compound of the tetravalent metal is an amino-alkyl-zirconate obtained by reacting water-soluble amino-alcohols with zirconium alcoholates.

Claim 7

Process according to claim 1, characterized in that said organic compound of the tetravalent metal is zirconium tetraacetate.

Claim 8

Process according to claim 1, characterized in that said organic compound of the tetravalent metal is an amino-alkyl-stannate prepared by reacting water-soluble amino-alcohols with tin alcoholates.

Claim 9

Process according to claim 1, characterized in that said organic compound of the tetravalent metal is di-isopropyl-ditriethanolamine-stannate.

Claim 10

A process of claim 1, wherein said organic compound has the formula M(OZ).sub.4.

Claim 11

A process of claim 1, wherein said organic compound is in the form of said polymeric derivative.

Claim 12

A process of claim 10, wherein M is Zr and said polymeric derivative has a linkage of the formula ##STR9##

Claim 13

Process according to claim 11, characterized in that said polymeric derivative is a polymeric zirconate complexed with water-soluble amino-alcohols and water-soluble polyvalent alcohols, the latter containing from 3 to 6 carbon atoms and at least 3 hydroxyl radicals.

Claim 14

Process according to claim 12, characterized in that said polymeric zirconate is isopropylzirconate polymer complexed with triethanolamine and glycerine.

Claim 15

Process according to claim 1, characterized in that the temperature, at which the reinforcing material surface is treated with the organic compound of the tetravalent metal, is between 350° C. and 550° C.

Claim 16

Process according to claim 1, characterized in that the heating, up to a temperature ranging from 250° C. to 650° C., at which the reinforcing material surface is treated with the organic compound of the tetravalent metal, is effected by applying said compound onto the reinforcing material that is already at a temperature between 250° C. and 650° C., or by applying said compound onto the reinforcing material, and by successively heating the reinforcing material, so treated, to a temperature ranging from 250° C. to 650° C.

Claim 17

Process according to claim 1, characterized in that said coupling agent is selected from the group consisting of vinyltriethoxysilane, vinyltriacethoxysilane, γ-aminopropyltriethoxysilane, N-β-(aminoethyl)-γ-aminopropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-mercaptopropyltrimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl-tri methoxysilane, γ-chloropropyltrimethoxysilane, and γ-methacryloxypropyltrimethoxysilane.

Claim 18

A coated reinforcing material for a plastic matrix comprising a reinforcing material coated with an organosiloxymetalloxane polymer to impart enhanced adhesion between said reinforcing material and said plastic matrix, characterized in that said reinforcing material has been subjected to the process comprising the steps of (a) treating the reinforcing material surface at a temperature ranging from 250° C. to 650° C.; with at least one organic compound of a tetravalent metal having the formula: M(OZ).sub.4 wherein: M is Zr or Sn; (OZ) is an organic radical non-hydrolyzable at room temperature in the presence of water, but hydrolyzable in the presence of water vapor at a temperature between 250° and 650°; or a polymeric derivative thereof with a linkage of the type ##STR10## (b) applying onto the thus treated reinforcing material surface at a lower temperature, at least one silane coupling agent having the formula: (OR).sub.3 Si(CH.sub.2).sub.n X wherein: n is 0, 1, 2 or 3 (OR) is an organic radical hydrolyzable at room temperature in the presence of water, bound to silicon, and in which R is an alkyl or acyl radical; X is an organo functional radical promoting the adhesion of the treated reinforcing material to the plastic material; such as chlorine, a vinyl, methacryloxy, amino, glycidoxy, mercaptyl, or an epoxy-cyclohexyl group; (c) drying the thus treated reinforcing material.

Claim 19

A coated reinforcing material for a plastic matrix comprising a reinforcing material coated with an organosiloxymetalloxane polymer to impart enhanced adhesion between said reinforcing material and said plastic matrix, characterized in that said reinforcing material has been subjected to the process comprising the steps of (a) treating the reinforcing material surface at a temperature ranging from 250° C. to 650° C.; with at least one organic compound of a tetravalent metal having the formula: M(OZ).sub.4 wherein: M is Zr or Sn; (OZ) is an organic radical non-hydrolyzable at room temperature in the presence of water, but hydrolyzable in the presence of water vapor at a temperature between 250° and 650°; or a polymeric derivative thereof with a linkage of the type ##STR10## (b) applying onto the thus treated reinforcing material surface at a lower temperature, at least one silane coupling agent having the formula: (OR).sub.3 Si(CH.sub.2).sub.n X wherein: n is 0, 1, 2 or 3 (OR) is an organic radical hydrolyzable at room temperature in the presence of water, bound to silicon, and in which R is an alkyl or acyl radical; X is an organo functional radical promoting the adhesion of the treated reinforcing material to the plastic material; such as chlorine, a vinyl, methacryloxy, amino, glycidoxy, mercaptyl, or an epoxy-cyclohexyl group; (c) drying the thus treated reinforcing material.

Claim 20

A coated reinforcing material of claim 17, wherein said organic compound has the formula M(OZ).sub.4

Claim 21

A coated reinforcing material of claim 17, wherein said organic compound is in the form of said polymeric derivative.

Claim 22

A coated reinforcing material of claim 19, wherein M is Zr and said polymeric derivative has a linkage of the formula ##STR11##

Claim 23

A coated reinforcing material of claim 17, characterized in that said organic compound of the tetravalent metal is selected from the group consisting of esters of zirconium acid, amino-alkyl-zirconates and amino-alkyl-stannates.

Claim 24

A coated reinforcing material of claim 17, characterized in that said organic compound of the tetravalent metal is an ester of zirconium acid with water-soluble polyvalent alcohols containing from 3 to 6 carbon atoms and at least 3 hydroxyl radicals.

Claim 25

A coated reinforcing material of claim 17, characterized in that said organic compound of the tetravalent metal is an amino-alkyl-zirconate prepared by reacting water-soluble amino-alcohols with zirconium dioxy-hydrate.

Claim 26

A coated reinforcing material of claim 17, characterized in that said organic compound of the tetravalent metal is an amino-alkyl-zirconate obtained by reacting water-soluble amino-alcohols with zirconium alcoholates.

Claim 27

A coated reinforcing material of claim 17, characterized in that said organic compound of the tetravalent metal is zirconium tetra-acetate.

Claim 28

A coated reinforcing material of claim 17, characterized in that said organic compound of the tetravalent metal is an amino-alkyl-stannate prepared by reacting water-soluble amino-alcohols with tin alcoholates.

Claim 29

A coated reinforcing material of claim 17, characterized in that said organic compound of the tetravalent metal is di-isopropyl-ditriethanolamine-stannate.

Claim 30

A coated reinforcing material of claim 20, characterized in that said polymeric derivative is a polymeric zirconate complexed with water-soluble amino-alcohols and water-soluble polyvalent alcohols, the latter containing from 3 to 6 carbon atoms and at least 3 hydroxyl radicals.

Claim 31

A coated reinforcing material of claim 28, characterized in that said polymeric zirconate is isopropylzirconate polymer complexed with triethanolamine and glycerine.

Claim 32

A coated reinforcing material of claim 17, characterized in that the temperature, at which the reinforcing material surface is treated with the organic compound of the tetravalent metal, is between 350° C. and 550° C.

Claim 33

A coated reinforcing material of claim 17 characterized in that the heating, up to a temperature ranging from 250° C. to 650° C., at which the reinforcing material surface is treated with the organic compound of the tetravalent metal, is effected by applying said compound onto the reinforcing material that is already at a temperature between 250° C. and 650° C., or by applying said compound onto the reinforcing material, and by successively heating the reinforcing material, so treated, to a temperature ranging from 250° C. to 650° C.

Claim 34

A coated reinforcing material of claim 17, characterized in that said coupling agent is selected from the group consisting of vinyltriethoxysilane, vinyltriacethoxysilane, γ-aminopropyltriethoxysilane, N-β-(aminoethyl-γ-aminopropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane, δ-mercaptopropyltrimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl-tri-methoxysilane, γ-chloropropyltrimethoxysilane, and γ-methacryloxypropyltrimethoxysilane.