Abstract
Abstract This invention relates to the use of indium compounds as thermal stabilizers for vinyl halide resins. Very small additions of indium compounds to vinyl halide resins, with or without the inclusion of other stabilizers, have been found to contribute marked improvements in resistance to high temperature discoloration. For example, additions sufficient to provide less than 100 ppm of indium based upon the weight of said resin are particularly effective in helping to maintain original color over a longer period of time at elevated temperatures such as are encountered during hot processing and fabricating operations.
Inventors
- 👤 Dale J. Dieckmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:56
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/09; C08K5/098; C08K3/00; C08K3/10; C08K3/105; C08K5/13; C08K5/138; C08K5/36; C08K5/37
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
59 words
A heat stabilized thermoplastic resin composition comprising vinyl halide resin having uniformly incorporated therewith a minor proportion of indium in chemically combined form said proportion being sufficient to effect a significant retardation of discoloration of said composition at elevated temperatures and amount to less than about 500 parts by weight of indium per million parts of vinyl halide resin.
Claim 2
Dependent Claim
59 words
A heat stabilized thermoplastic resin composition comprising vinyl halide resin having uniformly incorporated therewith a minor proportion of indium in chemically combined form said proportion being sufficient to effect a significant retardation of discoloration of said composition at elevated temperatures and amount to less than about 500 parts by weight of indium per million parts of vinyl halide resin.
Claim 3
Dependent Claim
14 words
The composition of claim 1 wherein said indium is present in an inorganic compound.
Claim 4
Dependent Claim
29 words
The composition of claim 1 wherein the indium is present in amounts providing about 10 to about 200 ppm of indium by weight based upon said vinyl halide resin.
Claim 5
Dependent Claim
13 words
The composition of claim 1 wherein said indium is in the trivalent state.
Claim 6
Dependent Claim
20 words
The composition of claim 4 wherein said trivalent indium is fully in a salt, mercaptide, phenate or other salt-like linkage.
Claim 7
Dependent Claim
15 words
The composition of claim 5 wherein said indium is present in a water soluble salt.
Claim 8
Dependent Claim
18 words
The composition of claim 5 wherein said indium is present in a salt of an organic carboxylic acid.
Claim 9
Dependent Claim
12 words
The composition of claim 7 wherein said acid is aliphatic and monocarboxylic.
Claim 10
Dependent Claim
17 words
The composition of claim 5 wherein said indium is present in a mercaptide of a carboxylic thiol.
Claim 11
Dependent Claim
19 words
The composition of claim 1 wherein the vinyl halide resin is a polymer or copolymer of a chlorinated monomer.
Claim 12
Dependent Claim
17 words
The composition of claim 10 wherein said resin is primarily derived from vinyl chloride and/or vinylidene chloride.
Claim 13
Dependent Claim
48 words
A composition as defined in claim 1 which also contains a minor amount relative to said vinyl halide resin but a major amount relative to said indium of at least one stabilizer from the established classes of stabilizers already recognized to be effective stabilizers for vinyl halide resins.
Claim 14
Dependent Claim
59 words
A composition as defined in claim 12 wherein said stabilizer material belongs to one of the following recognized classes (A) salt type compounds including carboxylate soaps of metals such as alkali metals, alkaline earth metals, cadmium, tin and lead. (B) organotin compounds (C) antimony compunds (D) epoxy compounds (E) phosphite esters (F) phenolic compounds, and (G) non-metallic sulfur-containing compounds.
Claim 15
Dependent Claim
15 words
A composition as defined in claim 12 wherein said stabilizer material is a metal soap.
Claim 16
Dependent Claim
19 words
A composition as defined in claim 12 wherein said stabilizer material is a sulfur-containing organotin compound or antimony compound.
Claim 17
Dependent Claim
18 words
A composition as defined in claim 12 wherein said stabilizer material is a non-metallic organic compound containing sulfur.
Claim 18
Independent Claim
62 words
A method of protecting vinyl halide resins from thermally induced discoloration which comprises distributing throughout said resins a minor proportion of indium in chemically combined form said proportion being sufficient to effect a significant retardation of discoloration of said resins at elevated temperatures and amounting to less than 500 parts by weight of indium per million parts of said vinyl halide resin.
Claim 19
Independent Claim
62 words
A method of protecting vinyl halide resins from thermally induced discoloration which comprises distributing throughout said resins a minor proportion of indium in chemically combined form said proportion being sufficient to effect a significant retardation of discoloration of said resins at elevated temperatures and amounting to less than 500 parts by weight of indium per million parts of said vinyl halide resin.
Claim 20
Dependent Claim
27 words
The method of claim 17 wherein said distributing involves mixing an easily dispersible material containing said indium with said resins while the latter are in particulate form.
Claim 21
Dependent Claim
27 words
The method of claim 17 wherein a relatively concentrated form of said indium is predispersed in a carrier before being mixed with the bulk of said resins.
Claim 22
Dependent Claim
16 words
The method of claim 19 wherein said carrier is an inert liquid compatible with said resins.
Claim 23
Dependent Claim
19 words
The method of claim 20 wherein said liquid is a solvent for the relatively concentrated form of said indium.
Claim 24
Dependent Claim
18 words
The method of claim 18 wherein said carrier is a recognized additive commonly used in vinyl halide resins.
Claim 25
Dependent Claim
34 words
The method of claim 18 wherein said carrier belongs to one of the following recognized additive classes: (A) Primary stabilizers (B) Secondary stabilizers (C) Lubricants (D) Plasticizers (E) Processing Aids (F) Fillers and pigments.
Claim 26
Dependent Claim
18 words
A stabilizer composition comprising 5 to 20% by weight of indium S,S',S" tris(isooctyl-thioglycolate) and 95 to 80% isooctyl-thioglycolate.
Claim 27
Dependent Claim
18 words
A stabilizer composition comprising 5 to 20% by weight of indium S,S',S" tris(isooctyl-thioglycolate) and 95 to 80% isooctyl-thioglycolate.
Claim 28
Dependent Claim
41 words
A thermal discoloration inhibiting stabilizer composition for vinyl halide resins comprising a minor proportion of indium in chemically combined form in uniform admixture with a major proportion of an established thermal stabilizer generally recognized to be effective in vinyl halide resins.
Claim 29
Dependent Claim
41 words
A thermal discoloration inhibiting stabilizer composition for vinyl halide resins comprising a minor proportion of indium in chemically combined form in uniform admixture with a major proportion of an established thermal stabilizer generally recognized to be effective in vinyl halide resins.
Claim 30
Dependent Claim
27 words
The stabilizer composition of claim 25 wherein said indium is present as a salt of a monocarboxylic acid and said major proportion comprises alkaline earth metal soaps.
Claim 31
Dependent Claim
34 words
The stabilizer composition of claim 25 wherein said minor proportion of indium is in the form of a trimercaptide and said major proportion is composed of the free mercaptan compound corresponding to said trimercaptide.
Claim 32
Dependent Claim
23 words
The stabilizer composition of claim 25 wherein said major proportion comprises a compound of the group consisting of organotin mercaptides and antimony mercaptides.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-25 | 1982-12-25 | 1983-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-25 | 1986-12-25 | 1987-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-25 | 1990-12-25 | 1991-06-26 | $7700.00 | Window Closed / Lapsed |