US4161472A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Impact modified vinyl chloride polymer composition
Assignee: Geon Co
•
Filing: 1978-01-23
•
Granted: 1979-07-17
•
Expires: 1998-01-23
Abstract
Abstract Polyvinyl chloride (PVC) resin is compounded with a conventional impact modifier referred to herein as a "co-modifier", and a block copolymer "ultra-modifier" which together provide a composition of unexpectedly enhanced impact strength. Irrespective of the characteristic particle size distribution of the co-modifier, which may be normal, bimodal or neither, the combination of ultra-modifier and co-modifier produces a broad distribution of small and large modifier particles. Better impact strength than with either small particles alone, or large particles alone is thus obtained. The ultra-modifier, which synergistically increases the impact strength of conventionally impact-modified vinyl chloride polymer compositions, consists essentially of a block copolymer of a vinyl aromatic compound and a conjugated diene, such as a styrene-diene (SD) diblock copolymer, or styrene-diene-styrene (SDS) block copolymer; the ultra-modifier is a polyblock copolymer, including linear diblock, triblock, tetrablock copolymers, and radial block copolymers including triblock and tetrablock copolymers. The co-modifier may be any elastomer additive, preferably a nucleated rubbery graft copolymer.
Inventors
- 👤 Marvin H. Lehr
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 14:24
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08L53/00; C08L53/02; Y; Y10; Y10S; Y10S525/00; Y10S525/901
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
190 words
A normally rigid thermoplastic composition comprising (a) a matrix comprising a vinyl chloride resin, (b) an impact modifier or co-modifier in said matrix for reducing the brittle temperature of said vinyl chloride resin, said impact modifier being present in an amount in the range from about 3 percent to about 25 percent by weight based on total resinous components, so as to produce at least a 20 percent improvement in Izod impact strength of non-impact-modified vinyl chloride resin, and (c) a block copolymer ultra-modifier consisting essentially of a block copolymer of a vinyl aromatic compound (S) and a conjugated diene (D), wherein said vinyl aromatic compound (S) is selected from the group consisting of styrene, α-methyl styrene, vinyl toluene, vinyl xylene, and vinyl naphthalene, said conjugated diene (D) is selected from the group consisting of butadiene, isoprene, 1,3-pentadiene, and 2,3-dimethyl-butadiene, wherein said ultra-modifier is present in an amount in the range from about 1 percent to about 15 percent by weight, based on the total resinous components of said composition, and said co-modifier and said ultra-modifier are each present as distinguishable impact modifier particles dispersed in said vinyl chloride resin.
Claim 2
Dependent Claim
190 words
A normally rigid thermoplastic composition comprising (a) a matrix comprising a vinyl chloride resin, (b) an impact modifier or co-modifier in said matrix for reducing the brittle temperature of said vinyl chloride resin, said impact modifier being present in an amount in the range from about 3 percent to about 25 percent by weight based on total resinous components, so as to produce at least a 20 percent improvement in Izod impact strength of non-impact-modified vinyl chloride resin, and (c) a block copolymer ultra-modifier consisting essentially of a block copolymer of a vinyl aromatic compound (S) and a conjugated diene (D), wherein said vinyl aromatic compound (S) is selected from the group consisting of styrene, α-methyl styrene, vinyl toluene, vinyl xylene, and vinyl naphthalene, said conjugated diene (D) is selected from the group consisting of butadiene, isoprene, 1,3-pentadiene, and 2,3-dimethyl-butadiene, wherein said ultra-modifier is present in an amount in the range from about 1 percent to about 15 percent by weight, based on the total resinous components of said composition, and said co-modifier and said ultra-modifier are each present as distinguishable impact modifier particles dispersed in said vinyl chloride resin.
Claim 3
Dependent Claim
27 words
The composition of claim 1 wherein said vinyl chloride resin is selected from the group consisting of copolymers of vinyl chloride and a homopolymer of vinyl chloride.
Claim 4
Dependent Claim
48 words
The composition of claim 2 wherein said copolymers of vinyl chloride consist essentially of copolymers of vinyl chloride and a monomer copolymerizable therewith selected from the group consisting of vinyl esters, α-olefins, alkyl acrylates, and alkyl methacrylates having up to about 18 carbon atoms in the alkyl moiety.
Claim 5
Dependent Claim
25 words
The composition of claim 3 wherein said copolymer is selected from the group consisting of vinyl chloride/vinyl acetate, vinyl chloride/vinyl propionate and vinyl chloride/vinyl ethylene.
Claim 6
Dependent Claim
34 words
The composition of claim 1 wherein said co-modifier is present in an amount in the range from about 5 percent to about 10 percent by weight of the total resinous components of said composition.
Claim 7
Dependent Claim
42 words
The composition of claim 2 wherein, in said co-modifier there are present primary resin particles in the size range from about 500 A (Angstrom) to about 7000 A, provided that less than 20 percent by weight are greater than about 5000 A.
Claim 8
Dependent Claim
31 words
The composition of claim 2 wherein said co-modifier is a grafted interpolymerization product of a hard resin and rubbery polymer, wherein said hard resin is derived from a monounsaturated vinyl monomer.
Claim 9
Dependent Claim
32 words
The composition of claim 2 wherein said co-modifier is selected from the group consisting of chlorinated polyethylene, nitrile rubber, styrene-butadiene rubber, stearic acid coated calcium carbonate, ethylene-vinyl acetate copolymers and acrylate-methacrylate copolymers.
Claim 10
Dependent Claim
29 words
The composition of claim 2 wherein said block copolymer ultra-modifier has a structure selected from a polyblock structure including a linear diblock, linear triblock, and a radial teleblock structure.
Claim 11
Dependent Claim
45 words
The composition of claim 6 wherein said vinyl chloride polymer has primary resin particles in the size range from about 2500 A to about 2μ (micron), and said block copolymer ultra-modifier has primary particles in the size range from about 200 A to about 1μ.
Claim 12
Dependent Claim
43 words
The composition of claim 9 wherein said ultra-modifier includes vinyl aromatic compound units which comprise from about 20 to about 80 percent by weight, and diene units which comprise from about 80 to about 20 percent by weight of said block copolymer ultra-modifier.
Claim 13
Dependent Claim
36 words
The composition of claim 10 wherein said block copolymer ultra-modifier is present in an amount in the range from about 2 to about 6 percent by weight, based on the total resinous components of the composition.
Claim 14
Dependent Claim
13 words
The composition of claim 12 wherein said ultra-modifier is a rubbery block copolymer.
Claim 15
Dependent Claim
15 words
A reinforced composition as defined in claim 1 including a reinforcing amount of fibrous glass.
Claim 16
Independent Claim
207 words
A method for preparing a normally rigid thermoplastic article comprising melt-blending (a) a vinyl chloride resin, (b) an impact modifier or co-modifier in said matrix for reducing the brittle temperature of said vinyl chloride resin, said impact modifier being present in an amount in the range from about 3 percent to about 25 percent by weight based on total resinous components, so as to produce at least a 20 percent improvement in Izod impact strength of non-impact-modified vinyl chloride resin, and (c) a block copolymer ultra-modifier consisting essentially of a block copolymer of a vinyl aromatic compound (S) and a conjugated diene (D), wherein said vinyl aromatic compound (S) is selected from the group consisting of styrene, α-methyl styrene, vinyl toluene, vinyl xylene, and vinyl naphthalene, said conjugated diene (D) is selected from the group consisting of butadiene, isoprene, 1,3-pentadiene, and 2,3-dimethyl-butadiene, wherein said block copolymer ultra-modifier is present in an an amount in the range from about 1 percent to about 15 percent by weight, based on the total resinous components of said composition, to obtain a uniform melt, said co-modifier and said ultra-modifier being each present as distinguishable impact modifier particles dispersed in said vinyl chloride resin; and, shaping said melt to form said article.
Claim 17
Independent Claim
207 words
A method for preparing a normally rigid thermoplastic article comprising melt-blending (a) a vinyl chloride resin, (b) an impact modifier or co-modifier in said matrix for reducing the brittle temperature of said vinyl chloride resin, said impact modifier being present in an amount in the range from about 3 percent to about 25 percent by weight based on total resinous components, so as to produce at least a 20 percent improvement in Izod impact strength of non-impact-modified vinyl chloride resin, and (c) a block copolymer ultra-modifier consisting essentially of a block copolymer of a vinyl aromatic compound (S) and a conjugated diene (D), wherein said vinyl aromatic compound (S) is selected from the group consisting of styrene, α-methyl styrene, vinyl toluene, vinyl xylene, and vinyl naphthalene, said conjugated diene (D) is selected from the group consisting of butadiene, isoprene, 1,3-pentadiene, and 2,3-dimethyl-butadiene, wherein said block copolymer ultra-modifier is present in an an amount in the range from about 1 percent to about 15 percent by weight, based on the total resinous components of said composition, to obtain a uniform melt, said co-modifier and said ultra-modifier being each present as distinguishable impact modifier particles dispersed in said vinyl chloride resin; and, shaping said melt to form said article.
References Cited (Backward Citations)
US3641206A
Cited
US3511896A
Cited
US3652483A
Cited
US3557252A
Cited
US3678133A
Cited
US3992485A
Cited
US3825622A
Cited
US3801529A
Cited
US4078018A
Cited
US4054615A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-16 | 1983-01-15 | 1983-07-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-16 | 1987-01-15 | 1987-07-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-16 | 1991-01-15 | 1991-07-17 | $7700.00 | Window Closed / Lapsed |