Production of stabilized wet process phosphoric acid
Assignee: WR Grace and Co
•
Filing: 1978-03-06
•
Granted: 1979-08-14
•
Expires: 1998-03-06
Abstract
Abstract Treatment of wet process phosphoric acid to inhibit post-precipitation by steps including addition of an aluminum silicate material such as perlite or the like to dilute acid from which a major portion of solids has been removed, concentration of the resulting dilute acid, and removal of resulting precipitate.
Inventors
- 👤 Richard N. Hill
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:42
CPC Classifications
C; C01; C01B; C01B25/00; C01B25/16; C01B25/18; C01B25/234; C01B25/235
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
195 words
The method of preparing a wet process phosphoric acid substantially free from post-precipitation that includes the steps: (a) to a wet process phosphoric acid having a P 2 O 5 content of 36 to 46 weight percent from which the suspended solids have been removed, adding 0.05 to 2.0 weight percent of an aluminum silicate material based on the contained weight of P 2 O 5 in the acid to provide an aluminum silicate material-acid mix; said aluminum silicate material being finely divided so as to be soluble in the phosphoric acid as the concentration of the acid is increased from 36-46 weight percent P 2 O 5 to an increased P 2 O 5 within the range of 42-52 weight percent; (b) concentrating the aluminum silicate material-acid mix to said 42-52 weight percent P 2 O 5 in an evaporation zone thereby to provide an aluminum silicate material/acid solution; (c) transferring the concentrated solution to a crystallizing zone having an overflow stream and an underflow stream; (d) recovering the overflow stream and subsequently evaporating to a concentration of up to 63% P 2 O 5 to provide wet-process phosphoric acid substantially free of post-precipitation.
Claim 2
Independent Claim
195 words
The method of preparing a wet process phosphoric acid substantially free from post-precipitation that includes the steps: (a) to a wet process phosphoric acid having a P 2 O 5 content of 36 to 46 weight percent from which the suspended solids have been removed, adding 0.05 to 2.0 weight percent of an aluminum silicate material based on the contained weight of P 2 O 5 in the acid to provide an aluminum silicate material-acid mix; said aluminum silicate material being finely divided so as to be soluble in the phosphoric acid as the concentration of the acid is increased from 36-46 weight percent P 2 O 5 to an increased P 2 O 5 within the range of 42-52 weight percent; (b) concentrating the aluminum silicate material-acid mix to said 42-52 weight percent P 2 O 5 in an evaporation zone thereby to provide an aluminum silicate material/acid solution; (c) transferring the concentrated solution to a crystallizing zone having an overflow stream and an underflow stream; (d) recovering the overflow stream and subsequently evaporating to a concentration of up to 63% P 2 O 5 to provide wet-process phosphoric acid substantially free of post-precipitation.
Claim 3
Dependent Claim
52 words
The method according to claim 1 in which the aluminum silicate material has approximately the following analysis (dry solids basis): ______________________________________
Wt. %
______________________________________
P.sub.2 O.sub.5 0.96
CaO 0.13
SiO.sub.2 68.55
Fe.sub.2 O.sub.3 0.00
Al.sub.2 O.sub.3 10.96
F 12.61
MgO 0.02
Na.sub.2 O 0.10
K.sub.2 O 0.04
Unidentified to
make 100.00
______________________________________
Claim 4
Dependent Claim
14 words
The method according to claim 1 in which the aluminum silicate material is kaolin.
Claim 5
Independent Claim
183 words
The method of preparing a wet process phosphoric acid substantially free from post-precipitation that includes the steps: (a) to a wet process phosphoric acid having a P 2 O 5 content of 36 to 46 weight percent from which the suspended solids have been removed, adding 0.05 to 2.0 weight percent perlite based on the contained weight of P 2 O 5 in the acid to provide a perlite-acid mix, said perlite being finely divided so as to be soluble in the phosphoric acid as the concentration of the acid is increased from 36-46 weight percent P 2 O 5 to an increased P 2 O 5 within the range 42-52 weight percent; (b) concentrating the perlite-acid mix to said 42-52 weight percent P 2 O 5 in an evaporation zone thereby to provide a perlite/acid solution; (c) transferring the concentrated solution to a crystallizing zone having an overflow stream and an underflow stream; (d) recovering the overflow stream and subsequently evaporating to a concentration of up to 63% P 2 O 5 to provide wet-process phosphoric acid substantially free of post precipitation.
Claim 6
Independent Claim
183 words
The method of preparing a wet process phosphoric acid substantially free from post-precipitation that includes the steps: (a) to a wet process phosphoric acid having a P 2 O 5 content of 36 to 46 weight percent from which the suspended solids have been removed, adding 0.05 to 2.0 weight percent perlite based on the contained weight of P 2 O 5 in the acid to provide a perlite-acid mix, said perlite being finely divided so as to be soluble in the phosphoric acid as the concentration of the acid is increased from 36-46 weight percent P 2 O 5 to an increased P 2 O 5 within the range 42-52 weight percent; (b) concentrating the perlite-acid mix to said 42-52 weight percent P 2 O 5 in an evaporation zone thereby to provide a perlite/acid solution; (c) transferring the concentrated solution to a crystallizing zone having an overflow stream and an underflow stream; (d) recovering the overflow stream and subsequently evaporating to a concentration of up to 63% P 2 O 5 to provide wet-process phosphoric acid substantially free of post precipitation.
Claim 7
Dependent Claim
17 words
The method according to claim 4, step (a), in which the perlite added is 0.25-0.75 wt. %.
Claim 8
Dependent Claim
15 words
The method according to claim 5 in which the perlite added is 0.3-0.4 wt. %.
Claim 9
Dependent Claim
86 words
The method according to claim 4 wherein solids removal in step (a) is accomplished by starting with an initial feed containing 0.5-8.0 weight percent of suspended solids, adding flocculant thereto in a mixing zone, transferring the mixture to a clarification zone with an overflow and an underflow, and discharging the overflow as feed for mixing with perlite in a second mixing zone; said overflow being clarified phosphoric acid substantially free of suspended solids and said underflow carrying substantially all the suspended solids of the initial feed.
Claim 10
Dependent Claim
48 words
The method according to claim 7 in which the initial feed contains approximately the following: ______________________________________
Wt. %
______________________________________
P.sub.2 O.sub.5 42.90
Solids 1.50
H.sub.2 SO.sub.4 3.50
CaO 0.60
SiO.sub.2 1.07
F 2.38
Fe.sub.2 O.sub.3 1.55
Al.sub.2 O.sub.3 1.36
Na.sub.2 O 0.19
K.sub.2 O 0.12
MgO 0.52
______________________________________
Claim 11
Dependent Claim
22 words
The method according to claim 7 in which the clarifier underflow is 2 to 20 volume percent of the clarifier inlet stream.
Claim 12
Dependent Claim
19 words
The method according to claim 9 in which the clarifier underflow is 4-10 volume percent of the inlet stream.
Claim 13
Dependent Claim
19 words
The method according to claim 10 in which the clarifier underflow is 8 volume percent of the inlet stream.
Claim 14
Dependent Claim
26 words
The method according to claim 7 in which the underflow from the crystallizing zone is 1 to 10 volume percent of the crystallizing zone inlet stream.
Claim 15
Dependent Claim
21 words
The method according to claim 12 in which the crystallizing zone underflow stream is 1-4 volume percent of the inlet stream.
Claim 16
Dependent Claim
14 words
The method according to claim 7 in which all steps are operated substantially continuously.
Claim 17
Dependent Claim
47 words
The method according to claim 7 in which soda ash in an amount which is 0.1 to 2.0 weight percent of the P 2 O 5 in the feed is added to the feed prior to transferring the mixture of feed and flocculant to the clarification zone.
References Cited (Backward Citations)
US4110422A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-13 | 1983-02-12 | 1983-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-13 | 1987-02-12 | 1987-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-13 | 1991-02-12 | 1991-08-14 | $7700.00 | Window Closed / Lapsed |