Abstract A positive active material for electric primary cells, such as are used in electronic watches, is formed from a powder composed at least partially of grains having cores of silver peroxide completely surrounded by a layer of monovalent silver oxide and covered with a thin surface layer of metallic silver. The remainder of the powder, if any, comprises monovalent silver oxide grains, also covered with a thin surface layer of metallic silver. A process for making the material includes adding a reducing agent such as hydrazine to a powder having grains of less than 50 microns in diameter of essentially pure silver peroxide and reducing the silver peroxide to the point at which a thin layer of metallic silver forms on the surface of each powder grain. This point can be detected by a substantial reduction in electrical resistivity of the powder and occurs when approximately one-half of the original powder remains as silver peroxide.
A method of preparing a positive active material for primary electric cells, the method comprising: adding a predetermined quantity of a reducing agent to a selected amount of silver peroxide powder sufficient to reduce an outer layer of each grain of said powder until a layer of metallic silver is formed on the surface of each of the powder grains; reducing said powder with said reducing agent; measuring the resistance of said powder; and terminating said reducing step as soon as the resistivity of said powder significantly decreases, thereby indicating the formation of a thin surface layer of metallic silver on the grains of said powder.
Claim 2
Independent Claim
106 words
A method of preparing a positive active material for primary electric cells, the method comprising: adding a predetermined quantity of a reducing agent to a selected amount of silver peroxide powder sufficient to reduce an outer layer of each grain of said powder until a layer of metallic silver is formed on the surface of each of the powder grains; reducing said powder with said reducing agent; measuring the resistance of said powder; and terminating said reducing step as soon as the resistivity of said powder significantly decreases, thereby indicating the formation of a thin surface layer of metallic silver on the grains of said powder.
Claim 3
Dependent Claim
11 words
The method of claim 1 wherein the reducing agent comprises hydrazine.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein said predetermined quantity of a reducing agent is just sufficient to reduce approximately one-half of the silver peroxide powder.