US4199342A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of imparting a permanent curvature to a sheet of glass
Assignee: BFG Glassgroup GIE
•
Filing: 1978-12-07
•
Granted: 1980-04-22
•
Expires: 1998-12-07
Abstract
Abstract An untempered sheet of glass is given a predetermined curvature by means of pre-heated forming dies (3,4 in FIG. 1). The glass sheet (1) is not pre-heated or is heated only to a relatively low temperature prior to being inserted between the dies. Heat transfer from the dies to the glass prior to closure of the dies produces or assists in producing in the thickness of the glass sheet a transitory thermal stress gradient which gives resistance to breakage under bending forces. The absence of high temperature pre-heating of the sheet is conducive to a more predictable stress distribution pattern over the area of the sheet prior to bending. The process enables predetermined sheet curvatures to be achieved with higher degrees of accuracy.
Inventors
- 👤 Pierre Mestre
- 👤 Henri Prevost
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:00
CPC Classifications
C; C03; C03B; C03B23/00; C03B23/02; C03B23/023; C03B23/03; C03B23/0307
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
110 words
A process of imparting a permanent curvature to a sheet of glass by subjecting the sheet to bending forces between pre-heated forming dies having complementary curved surfaces, characterised in inserting the sheet in untempered condition between the pre-heated dies while its temperature prior to its insertion does not exceed 250° C. and is less than the temperature of the dies whereby heat is transferred from the dies to the sheet, closing the dies while a transitory thermal stress gradient exists in the thickness of the sheet due at least in part to heat transfer from such dies and opening the dies after at least partial relief of the bending stresses.
Claim 2
Dependent Claim
110 words
A process of imparting a permanent curvature to a sheet of glass by subjecting the sheet to bending forces between pre-heated forming dies having complementary curved surfaces, characterised in inserting the sheet in untempered condition between the pre-heated dies while its temperature prior to its insertion does not exceed 250° C. and is less than the temperature of the dies whereby heat is transferred from the dies to the sheet, closing the dies while a transitory thermal stress gradient exists in the thickness of the sheet due at least in part to heat transfer from such dies and opening the dies after at least partial relief of the bending stresses.
Claim 3
Dependent Claim
25 words
A process according to claim 1, wherein the sheet of glass is not subjected to any heating prior to its insertion between the forming dies.
Claim 4
Dependent Claim
20 words
A process according to claim 1, wherein the glass is pre-heated to a temperature of not more than 200° C.
Claim 5
Dependent Claim
35 words
A process according to claim 1, claim 2 or claim 3, wherein following insertion of the sheet between the dies it remains out of contact with one or both dies for less than 30 seconds.
Claim 6
Dependent Claim
30 words
A process according to claim 4, wherein following insertion of the sheet between the dies it remains out of contact with one or both dies for less than 10 seconds.
Claim 7
Dependent Claim
37 words
A process according to claim 1, claim 2 or claim 3, wherein the period of time for which both dies are in contact with the glass during closing of the dies is not more than 5 seconds.
Claim 8
Dependent Claim
32 words
A process according to claim 6, wherein the said period of time for which both dies are in contact with the glass during closing of the dies is less than 3 seconds.
Claim 9
Dependent Claim
34 words
A process according to claim 1, claim 2 or claim 3, wherein the period of time between insertion of the glass sheet between the dies and their complete closure is less than 20 seconds.
Claim 10
Dependent Claim
30 words
A process according to claim 8, wherein the said period of time between insertion of the glass sheet between the dies and their complete closure is less than 15 seconds.
Claim 11
Dependent Claim
51 words
A process according to claim 1, claim 2 or claim 3, wherein the temperature of the dies and the residence time of the glass sheet between the dies are such that the temperature of the glass does not rise above a value corresponding to a glass viscosity of 10 10 poises.
Claim 12
Dependent Claim
46 words
A process according to claim 10, wherein the temperature of the dies and the residence time of the glass sheet between the dies are such that the temperature of the glass does not rise above a value corresponding to a glass viscosity of 10 13 poises.
Claim 13
Dependent Claim
28 words
A process according to claim 1, claim 2 or claim 3, wherein after opening of the dies cooling of the glass is promoted by blowing air over it.
Claim 14
Dependent Claim
26 words
A process according to claim 1, claim 2, or claim 3, applied for imparting curvature to a sheet of glass less than 3 mm in thickness.
Claim 15
Dependent Claim
26 words
A process according to claim 1, claim 2 or claim 3, applied for bending a sheet of glass to a radius of more than 3 meters.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |