Abstract A high temperature thermistor and its method of fabrication are disclosed. The thermistor is fabricated from titanium dioxide ceramic forming material and is fabricated to achieve a high degree of densification approaching 100% of theoretical density. At elevated temperatures in the range of from about 700° F. to about 1500° F. densified titania ceramic material behaves as a semiconductor having a resistance which is responsive principally to the temperature of the thermistor element. The thermistor is fabricated by processing titania powder which includes a substantial majority of rutile phase material. The titania powder is processed to achieve a thermistor chip or member which demonstrates a high degree of density.
The method of manufacture of a thermistor operable at temperatures in excess of about 700° F. comprising the steps of forming a powder of high temperature stable phase ceramic forming metal oxide; preparing sinterable wafers from said powder; affixing electrodes to said wafers; and sintering said wafers to achieve a ceramic body having a density greater than about ninety-seven percent (97%) of theoretical density.
Claim 2
Independent Claim
64 words
The method of manufacture of a thermistor operable at temperatures in excess of about 700° F. comprising the steps of forming a powder of high temperature stable phase ceramic forming metal oxide; preparing sinterable wafers from said powder; affixing electrodes to said wafers; and sintering said wafers to achieve a ceramic body having a density greater than about ninety-seven percent (97%) of theoretical density.
Claim 3
Dependent Claim
27 words
The method of manufacture according to claim 1 wherein the step of sintering is carried out at a pyrometric cone equivalent number of at least eighteen (18).
Claim 4
Dependent Claim
27 words
The method of manufacture according to claim 1 including the step of forming the powder having a particle size range and distribution adjusted to achieve maximum densification.
Claim 5
Dependent Claim
25 words
The method of manufacture according to claim 3 wherein the step of sintering is carried out at a temperature in excess of about 2700° F.